High-transmittance eggshell white ceramic product and making method thereof

A technology for white ceramics and products, applied in the field of ceramics, can solve the problems of low strength, easy cracking and deformation, thin body, etc., and achieve the effect of reducing the sintering temperature, improving whiteness and density, and high viscosity

Inactive Publication Date: 2019-03-22
福建省德化业美陶瓷有限公司
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Thin-bodied porcelain has a thin body and low strength, and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-transmittance eggshell white ceramic product and making method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] This embodiment provides a white ceramic product with high light transmittance and thin body, including a blank and a glaze. The blank includes the following raw materials in parts by weight: 45 parts of kaolin, 18 parts of potassium feldspar, 15 parts of montmorillonite, 10 parts of quartz, 10 parts of clay and 1 part of talc; the glaze includes the following raw materials in parts by weight: 25 parts of nepheline orthoclase, 18 parts of dolomite, 8 parts of burnt talc, 4 parts of kaolin, 3 parts of calcium carbonate, and 3 parts of sepiolite , plant ash 2 parts, iron oxide 0.1 part.

[0027] Wherein said kaolin contains 46% to 50% of silicon dioxide content, 34% to 37% of aluminum oxide content, 0.3% to 0.6% of calcium oxide content, 0.3% to 0.4% of magnesium oxide content, and 0.3% to 0.4% of potassium oxide content. 4.5%-5.5%, sodium oxide content 0.45%-0.6%, ferric oxide content < 1%, titanium dioxide content < 0.35%.

[0028] The present invention also provides a...

Embodiment 2

[0036] This embodiment provides a white ceramic product with high light transmittance and thin body, including a blank and a glaze. The blank includes the following raw materials in parts by weight: 46 parts of kaolin, 19 parts of potassium feldspar, 16 parts of montmorillonite, 12 parts of quartz, 11 parts of clay and 2 parts of talc; the glaze includes the following raw materials in parts by weight: 27 parts of nepheline orthoclase, 19 parts of dolomite, 9 parts of burnt talc, 5 parts of kaolin, 4 parts of calcium carbonate, and 3 parts of sepiolite , plant ash 3 parts, potassium oxide 1 part, sodium oxide 1 part, iron oxide 0.2 part.

[0037] Wherein said kaolin contains 46% to 50% of silicon dioxide content, 34% to 37% of aluminum oxide content, 0.3% to 0.6% of calcium oxide content, 0.3% to 0.4% of magnesium oxide content, and 0.3% to 0.4% of potassium oxide content. 4.5%-5.5%, sodium oxide content 0.45%-0.6%, ferric oxide content < 1%, titanium dioxide content < 0.35%. ...

Embodiment 3

[0046] This embodiment provides a white ceramic product with high light transmission and thin body, including a blank and a glaze, and the blank includes the following raw materials in parts by weight: 48 parts of kaolin, 21 parts of potassium feldspar, 16 parts of montmorillonite, 13 parts of quartz, 12 parts of clay and 3 parts of talc; the glaze includes the following raw materials in parts by weight: 28 parts of nepheline orthoclase, 20 parts of dolomite, 10 parts of burnt talc, 6 parts of kaolin, 4 parts of calcium carbonate, and 4 parts of sepiolite , plant ash 3 parts, potassium oxide 2 parts, sodium oxide 1 part, iron oxide 0.3 part.

[0047] Wherein said kaolin contains 46% to 50% of silicon dioxide content, 34% to 37% of aluminum oxide content, 0.3% to 0.6% of calcium oxide content, 0.3% to 0.4% of magnesium oxide content, and 0.3% to 0.4% of potassium oxide content. 4.5%-5.5%, sodium oxide content 0.45%-0.6%, ferric oxide content < 1%, titanium dioxide content < 0.3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-transmittance eggshell white ceramic product. The high-transmittance eggshell white ceramic product comprises a preform body and glaze, wherein the preform body is prepared from the following raw materials in parts by weight: 45 to 50 parts of kaolin, 18 to 25 parts of potassium feldspar, 15 to 18 parts of montmorillonite, 10 to 15 parts of quartz, 10 to 14 parts of clay and 1 to 5 parts of talc; the glaze is prepared from the following raw materials in parts by weight: 25 to 30 parts of nepheline syenite, 18 to 22 parts of dolomite, 8 to 12 parts of burned talc,4 to 8 parts of kaolin, 3 to 6 parts of calcium carbonate, 3 to 5 parts of sepiolite, 2 to 5 parts of plant ash, 0 to 3 parts of potassium oxide, 0 to 2 parts of sodium oxide and 0.1 to 0.5 part of ferric oxide. The making method provided by the invention comprises the steps of burdening, throwing, fettling, biscuit firing, glazing and firing. The ceramic product prepared from the raw materials bythe process has the characteristics of white glazing color, high transmittance, clear and clean glaze surface, firm and white matrix, warm jade color, no cracks on the whole, and certain water resistance and thermal stability.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a white ceramic product with high light transmission and thin body and a manufacturing method thereof. Background technique [0002] Thin-bodied porcelain began in the Northern Song Dynasty and has a history of thousands of years. It is famous all over the world for its thin body. There are many poems describing thin-bodied porcelain, "thin as cicada's wings", "I'm afraid the wind will blow it away, and it will be sold in the sun", "pure glaze, almost no fetal bone", "moisturizing and transparent, thin and light", these are all It describes the characteristics of thin bodied porcelain as thin as paper, white as jade, bright as mirror, and sound like fragrance. More than 4,000 years ago, the black pottery of the Longshan culture was produced at a very high level, with an extremely thin wall of 0.5-1mm, known as the thin and bright eggshell black pottery. Historicall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/24C04B33/13C03C8/00
CPCC03C8/00C04B33/13C04B33/24C04B2235/3418C04B2235/3472C04B2235/6567
Inventor 苏珠巽苏杰东
Owner 福建省德化业美陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap