Preparation method of ether ester copolymerization type polycarboxylic acid water reducing agent capable of improving rheological behavior

A rheological characteristic and copolymerization technology, which is applied in the field of ether ester copolymerization polycarboxylate water reducer, can solve the problems of lower concrete anticorrosion ability and lower concrete strength, so as to prevent bleeding and segregation, improve dispersion and keep slump The effect of fall

Active Publication Date: 2019-04-16
KZJ NEW MATERIALS GROUP CO LTD +1
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, although the addition of traditional polycarboxylate-based water reducers to high-strength or high-performance concrete can reduce the friction between particles in the concrete, it will also have many negative effects, such as reduced concrete strength, reduced concrete anti-corrosion ability, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of ether ester copolymerization type polycarboxylic acid water reducing agent capable of improving rheological behavior
  • Preparation method of ether ester copolymerization type polycarboxylic acid water reducing agent capable of improving rheological behavior
  • Preparation method of ether ester copolymerization type polycarboxylic acid water reducing agent capable of improving rheological behavior

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Esterification reaction: 200.0g molecular weight is the methoxypolyethylene glycol of 4000, 52.2g methyl acrylate, 80.0gCH 3 (CH 2 ) 11 C 6 h 4 (OC 2 h 4 ) 20 Mix OH and 1.25g of polymerization inhibitor phenothiazine hydroquinone, under the protection of nitrogen, heat up to 40-60°C, then add 3.15g of catalyst 4-dimethylaminopyridine, heat up to 80-90°C, and react at constant temperature for 8h , down to room temperature after the reaction, to obtain the first mixture containing the esterification product and unreacted unsaturated acid and unsaturated carboxylic acid ester.

[0030] (2) Copolymerization reaction: get the first mixture that 100.0g step (1) makes, 200.0g molecular weight is the isopentenol polyoxyethylene ether of 5000, 16.0g methacrylic acid, 30.0g compound A (R 1 for -CH 2 , R 2 for CH 3 , n is 100) and 200.0g of deionized water are added to the reaction vessel and mixed, hydrogen peroxide aqueous solution (wherein hydrogen peroxide is 3....

Embodiment 2

[0033] (1) Transesterification reaction: 160.0g of methoxypolyethylene glycol with molecular weight of 3000, 65.9g of methyl methacrylate, 80.0g of CH 3 (CH 2 ) 7 C 6 h 4 (OC 2 h 4 ) 11 Mix OH and 1.02g of polymerization inhibitor hydroquinone, under the protection of nitrogen, heat up to 40-60°C, then add 3.25g of catalyst dibutyltin oxide, heat up to 90-100°C, keep warm for 6 hours, after the reaction Cool down to room temperature to obtain a first mixture of esterified product and unreacted methyl acrylate.

[0034](2) Copolymerization reaction: 200.0g of the first mixture prepared in step (1), 100.0g of isobutyl alcohol polyoxyethylene ether with a molecular weight of 4000, 14.4g of acrylic acid, 10.0g of compound A (R 1 for -CH 2 , R 2 is H, n is 20) and 300.0g deionized water are added to the reaction vessel and mixed, ammonium persulfate aqueous solution (wherein ammonium persulfate 3.15g, water 30.00g), dodecanethiol aqueous solution (wherein isopropanol 1.80g...

Embodiment 3

[0037] (1) Transesterification reaction: 100.0g of methoxypolyethylene glycol with a molecular weight of 1000, 57.0g of methyl methacrylate, 60.0g of CH 3 (CH 2 ) 8 C 6 h 4 (OC 2 h 4 ) 15 OH and 0.80g polymerization inhibitor diphenylamine were mixed, and under the protection of nitrogen, the temperature was raised to 40-60°C, and then 3.54g of catalyst sodium carbonate was added, the temperature was raised to 90-100°C, and the reaction was kept for 6 hours. After the reaction was completed, it was lowered to room temperature to obtain A first mixture of esterified product and unreacted methyl methacrylate.

[0038] (2) Copolymerization reaction: the first mixture prepared by 150.0g step (1), 150.0g molecular weight is 6000 isobutenol polyoxyethylene ether, 14.7g maleic anhydride, 20.0g compound A (R 1 for -CH 2 CH 2 , R 2 for CH 3 , n is 50) and 200.0g deionized water are added to the reaction vessel and mixed, hydrogen peroxide aqueous solution (wherein hydrogen p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an ether ester copolymerization type polycarboxylic acid water reducing agent for improving a rheological behavior. The water reducing agent is preparedthrough a copolymerization reaction of a first mixture, unsaturated polyether with the molecular weight of 4000-6000, unsaturated acid, a compound A, an initiator, a molecular weight regulator and deionized water, wherein the first mixture is prepared through an ester exchange reaction of methoxypolyethylene glycol with the molecular weight of 1000-4000, alkylphenol polyoxyethylene ether, unsaturated carboxylic ester and a polymerization inhibitor. According to the invention, a benzene ring and an imide structure are introduced, and the introduction of the benzene ring structure can effectively improve the adsorption efficiency and the thickness of an adsorption layer of polymer molecules on the surface of cement particles, so that the space stability effect of the water reducing agent ismore obvious; by means of introducing the imide structure, the adsorbability on the surface of the cement particles, the electrostatic repulsion effect among the cement particles, and the stability and the fluidity of the cement paste can be improved.

Description

technical field [0001] The invention relates to the field of concrete materials in building materials, in particular to an ether-ester copolymerized polycarboxylate water reducer for improving the rheological properties of cement paste. Background technique [0002] In the field of concrete materials, water reducing agent is an admixture of concrete mixture, which is used to improve its rheological properties, and has been widely used at present. The application of water reducing agent can effectively reduce the water-cement ratio of concrete, improve the pore structure and compactness of concrete, and improve the strength and durability of concrete. This has important positive significance in improving project quality, service life, reducing costs, and reducing environmental pollution. . [0003] With the vigorous development of my country's construction industry, important buildings with high-strength, high-performance concrete structures and special functional requiremen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/06C08F220/06C08F4/40C08F2/38C08G65/332C04B24/26C04B103/30
CPCC04B24/2694C04B2103/006C04B2103/302C08F283/06C08F283/065C08G65/3322C08F220/06
Inventor 赖华珍方云辉邵幼哲吴传灯郭元强林添兴麻秀星温庆如
Owner KZJ NEW MATERIALS GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com