A kind of reinforced short fiber masterbatch for rubber transmission belt and preparation method thereof

A short fiber and transmission belt technology, which is applied in the field of functional fiber masterbatch and its preparation, can solve the problems of insufficient heat resistance, complex pretreatment process, poor interface bonding, etc., and achieve the goals of not easy to agglomerate, improve bonding, and prolong service life Effect

Active Publication Date: 2021-12-21
陇川县百信胶带有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to overcome the deficiencies in the prior art, provide a kind of reinforced staple fiber masterbatch and preparation method for rubber transmission belt, solve the poor interface bonding with the rubber matrix when aramid short fiber reinforced rubber in the prior art, Insufficient heat resistance and complex pretreatment process, the provided reinforced short fibers for rubber transmission belts have the advantages of uniform dispersion, improved bonding with the rubber matrix, improved tensile strength, elongation, and bonding strength of rubber, and use Advantages of longevity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033]A reinforced short fiber masterbatch for rubber transmission belts, said reinforced short fiber masterbatch for rubber transmission belts consists of the following components by weight: 40 parts of modified aramid short fibers, 15 parts of polyolefin elastomer POE , 20 parts of neoprene rubber, 3 parts of silane coupling agent, 5 parts of aromatic oil, 10 parts of 2500 mesh talcum powder, 3 parts of stearic acid, 1 part of anti-aging agent DNP;

[0034] The modified aramid short fiber is an aramid short fiber whose surface is coated with a calcium silicate hard shell.

[0035] The preparation method of the above-mentioned reinforced staple fiber masterbatch for rubber transmission belts comprises the following steps:

[0036] Step 1. Immerse short aramid fibers with a length of 2 mm in a saturated solution of calcium hydroxide, keep it at a temperature of 80° C. for 60 minutes, and then immerse it in a sodium silicate solution. The mass concentration of the solute is 40%...

Embodiment 2

[0042] A reinforced short fiber masterbatch for rubber transmission belts, said reinforced short fiber masterbatch for rubber transmission belts consists of the following components by weight: 60 parts of modified aramid short fibers, 30 parts of polyolefin elastomer POE , 30 parts of neoprene, 8 parts of silane coupling agent, 10 parts of aromatic oil, 20 parts of 2500 mesh silicon dioxide, 8 parts of stearic acid, 5 parts of anti-aging agent NBC;

[0043] The modified aramid short fiber is an aramid short fiber whose surface is coated with a hard aluminum silicate shell.

[0044] The preparation method of the above-mentioned reinforced staple fiber masterbatch for rubber transmission belts comprises the following steps:

[0045] Step 1. Immerse short aramid fibers with a length of 2mm in a saturated solution of aluminum hydroxide, keep it at a temperature of 50°C for 30 minutes, and then immerse it in a sodium silicate solution with a mass concentration of solute of 40%. Ke...

Embodiment 3

[0051] A reinforced short fiber masterbatch for rubber transmission belts, said reinforced short fiber masterbatch for rubber transmission belts consists of the following components by weight: 50 parts of modified aramid short fibers, 20 parts of polyolefin elastomer POE , 25 parts of neoprene rubber, 3-8 parts of silane coupling agent, 5-10 parts of aromatic oil, 15 parts of 2500 mesh talcum powder, 5 parts of stearic acid, 3 parts of anti-aging agent DNP;

[0052] The modified aramid short fiber is an aramid short fiber whose surface is coated with a calcium silicate hard shell.

[0053] The preparation method of the above-mentioned reinforced staple fiber masterbatch for rubber transmission belts comprises the following steps:

[0054] Step 1. Immerse the short aramid fiber with a length of 2 mm in a saturated solution of calcium hydroxide, keep it at a temperature of 60°C for 50 minutes, and then immerse it in a sodium silicate solution with a mass concentration of solute ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of functional fiber masterbatch and its preparation method, in particular to a reinforced staple fiber masterbatch for rubber transmission belts and its preparation method, which consists of the following components: modified aramid staple fiber, polyolefin elastomer, rubber, coupling Agents, aromatic oils, reinforced modified fillers, plasticizers, anti-aging agents. The preparation method includes: immersing the short aramid fiber in the metal hydroxide solution, then in the soluble silicate solution, repeating soaking to form the short aramid fiber with a hard silicate shell layer on the surface, and then mixing with the coupling agent After dispersing and standing still, the remaining raw materials are added for banburying, and the rubber material is granulated by a twin-screw extruder to obtain a reinforced short fiber masterbatch for rubber transmission belts. The invention solves the problems of poor interface bonding and insufficient heat resistance of aramid short fiber reinforced rubber in the prior art, and has the advantages of uniform dispersion, strong binding force, high tensile strength, high bonding strength and long service life. long advantage.

Description

technical field [0001] The invention relates to the technical field of functional fiber masterbatch and its preparation method, in particular to a reinforced short fiber masterbatch for rubber transmission belts and its preparation method. Background technique [0002] High temperature resistant transmission belt is made of multi-layer rubber cotton sail (polyester cotton cloth) or polyester canvas covered with high temperature resistant or heat resistant rubber, bonded together by high temperature vulcanization, widely used in metallurgy, casting, sintering, coking, building materials and other industries The relatively harsh high-temperature working environment mainly uses high-temperature solid materials produced in the production process of sintered ore, coke and cement to drive. With the rapid development of the domestic economy, the scale of ore, steel, coal mines and other enterprises has gradually expanded, and the output has increased. The performance of ordinary tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/28C08L23/16C08L77/10C08L23/08C08L11/00C08L91/00C08K13/02C08K3/34C08K5/09C08K5/18C08K3/22C08K3/04C08K3/36C08J3/22C08J5/06C08J5/10D06M11/79B29C35/02D06M101/36
CPCC08J3/226C08J5/06C08J5/10D06M11/79B29C35/02C08J2323/28C08J2423/16C08J2477/10C08J2423/08C08J2411/00C08J2491/00C08K13/02C08K3/34C08K5/09C08K5/18C08K2003/2296C08K3/04C08K3/36D06M2101/36
Inventor 汤天文
Owner 陇川县百信胶带有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com