High-pressure-resistant water permeable brick and making method thereof

A production method and technology of permeable bricks, which are applied in the field of high-pressure-resistant permeable bricks and their production, can solve the problems of low compressive strength of permeable bricks, limit the wide application of permeable bricks, etc., so as to improve the service life, enhance the resistance to deformation, improve The effect of adhesion

Inactive Publication Date: 2019-08-30
柳州柳晶环保科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the compressive strength of the permeable bricks currently used is low, which limits the wide applicatio

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Example 1:

[0025] Permeable brick components include 80 parts by weight of construction waste slag, 40 parts of waste steel bar, 20 parts of waste slag, 4 parts of reinforcing fiber, 3 parts of black iron oxide, 4 parts of oyster shell powder, and 8 parts of water purification material. The reinforcing fibers include 8% carbon fiber, 10% cupro ammonia fiber, 20% polypropylene fiber, 21% quartz glass fiber, 15% polytetrafluoroethylene fiber, and 26% graphene-based reinforcing fiber. Water purification materials include 7% activated carbon, 10% sodium carbonate, 20% nano-titanium dioxide, 32% graphene oxide, and 31% mesoporous composite molecular sieve.

[0026] The manufacturing method of this embodiment includes the following steps:

[0027] (1) After mixing construction waste slag, waste steel bars, and waste slag, add them to a pulverizer for pulverization, and then sieve to obtain mixture A;

[0028] (2) Add the reinforcing fiber, iron oxide black, and oyster she...

Example Embodiment

[0034] Example 2:

[0035] Permeable brick components include 90 parts by weight of construction waste slag, 48 parts of waste steel bars, 40 parts of waste slag, 8 parts of reinforcing fiber, 4 parts of black iron oxide, 11 parts of oyster shell powder, and 12 parts of water purification materials. The reinforcing fibers include 11% carbon fiber, 9% cupro fiber, 22% polypropylene fiber, 22% quartz glass fiber, 12% polytetrafluoroethylene fiber, and 24% graphene-based reinforcing fiber. Water purification materials include 10% activated carbon, 9% sodium carbonate, 21% nano-titanium dioxide, 29% graphene oxide, and 31% mesoporous composite molecular sieve.

[0036] The manufacturing method of this embodiment includes the following steps:

[0037] (1) After mixing construction waste slag, waste steel bars, and waste slag, add them to a pulverizer for pulverization, and then sieve to obtain mixture A;

[0038] (2) Add the reinforcing fiber, iron oxide black, and oyster shell p...

Example Embodiment

[0044] Example 3:

[0045] Permeable brick components include 120 parts by weight of construction waste slag, 42 parts of waste steel bar, 25 parts of waste slag, 6 parts of reinforcing fiber, 9 parts of black iron oxide, 6 parts of oyster shell powder, and 9 parts of water purification material. The reinforcing fibers include 12% carbon fiber, 11% cupro fiber, 17% polypropylene fiber, 18% quartz glass fiber, 16% polytetrafluoroethylene fiber, and 26% graphene-based reinforcing fiber. Water purification materials include 8% activated carbon, 11% sodium carbonate, 21% nano-titanium dioxide, 32% graphene oxide, and 28% mesoporous composite molecular sieve.

[0046] The manufacturing method of this embodiment includes the following steps:

[0047] (1) After mixing construction waste slag, waste steel bars, and waste slag, add them to a pulverizer for pulverization, and then sieve to obtain mixture A;

[0048] (2) Add the reinforcing fiber, iron oxide black, and oyster shell powde...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-pressure-resistant water permeable brick and a making method thereof. The water permeable brick comprises the following components in parts by weight: 80-120 parts of construction wastes, 40-50 parts of scrap steel bars, 20-40 parts of waste mineral slag, 4-10 parts of reinforced fibers, 3-9 parts of iron oxide black, 4-12 parts of oyster shell powder and 8-12 partsof a water purification material. The reinforced fibers are added into the water permeable brick, and the reinforced fibers are prepared by mixing multiple fibers, so that growth of micro-cracks and formation of macro-cracks of a water permeable plate substrate under a pressure effect can be effectively hindered, the anti-deforming capability of the water permeable brick is enhanced, and the service life of the water permeable brick is prolonged. In addition, the water purification material added into the water permeable brick is environment-friendly and pollution-free and is capable of filtering, adsorbing and degerming water. The water permeable brick prepared in the invention is high in permeable rate and long in service life and has a water purification effect.

Description

technical field [0001] The invention relates to the technical field of making permeable bricks, in particular to a high-pressure-resistant permeable brick and a manufacturing method thereof. Background technique [0002] At present, the ground in urban construction such as city squares, commercial streets, sidewalks, community activity venues, and parking lots are mostly paved with impermeable materials such as cement pavement bricks, ceramic glazed bricks, granite, marble, and asphalt concrete. These materials prevent the infiltration of rainwater, affect municipal drainage, and increase the city's heat island effect in hot season. In addition, because the road surface water cannot be removed in time, the water body will be polluted and a large number of bacteria will grow, which directly restricts the comfort of the urban environment and people's health. Therefore, permeable bricks with water permeability have begun to replace traditional paving materials and become a new...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/08
CPCC04B26/08C04B2111/00284C04B2111/2061C04B2201/50C04B18/141C04B18/167C04B14/48C04B14/42C04B14/308C04B14/28C04B14/386C04B16/0633C04B14/022C04B14/024C04B22/10C04B14/305C04B14/041
Inventor 任文强
Owner 柳州柳晶环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap