a kind of in 2 o 3 /li 0.5 la 0.5 tio 3 Hydrogen sulfide gas sensitive composite material and its preparation method and application

A composite material and hydrogen sulfide gas technology, applied in the field of H2S gas sensitive materials, can solve the problems of poor selectivity, high working temperature, long response and recovery time, etc., and achieve the improvement of catalytic activity, lower working temperature, and shortened response and recovery time Effect

Active Publication Date: 2022-04-01
ZHENGZHOU UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, a single metal oxide semiconductor generally has the disadvantages of relatively high operating temperature, long response and recovery time, and poor selectivity; and the perovskite material YMnO reported in the literature in recent years 3 Although the response and recovery time is shortened, only 5-6 seconds, but its sensitivity is only 0.49

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • a kind of in <sub>2</sub> o <sub>3</sub> /li <sub>0.5</sub> la <sub>0.5</sub> tio <sub>3</sub> Hydrogen sulfide gas sensitive composite material and its preparation method and application
  • a kind of in <sub>2</sub> o <sub>3</sub> /li <sub>0.5</sub> la <sub>0.5</sub> tio <sub>3</sub> Hydrogen sulfide gas sensitive composite material and its preparation method and application
  • a kind of in <sub>2</sub> o <sub>3</sub> /li <sub>0.5</sub> la <sub>0.5</sub> tio <sub>3</sub> Hydrogen sulfide gas sensitive composite material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of In 2 o 3 / Li 0.5 La 0.5 TiO 3 (LLTO) the preparation method of hydrogen sulfide gas sensitive composite material, comprises the steps:

[0037] (1) In 50ml of ethanol, add 0.005mol lanthanum nitrate (La(NO 3 ) 3 ·6H 2 O), 0.03mol citric acid monohydrate, 0.0055mol lithium nitrate (LiNO 3 ), after stirring and dissolving, slowly add 0.01mol tetrabutyl titanate, 0.06mol ethylene glycol, stir and mix for 30min, set aside;

[0038] (2) 0.6mmol of indium nitrate (In(NO 3 ) 3 .4.5H 2 O) join in the mixed solution of step (1), stir 40min to dissolve completely, obtain uniform solvothermal precursor solution;

[0039] (3) Transfer the mixed solution of step (2) into a 100 milliliter polytetrafluoroethylene-lined non-magnetic steel reaction kettle, put it into a blast drying oven at 150° C. for solvothermal reaction for 6 hours;

[0040] (4) After the reaction in step (3), the reaction kettle was cooled naturally, and then centrifuged and washed three times...

Embodiment 2

[0042] A kind of In 2 o 3 / Li 0.5 La 0.5 TiO 3 (LLTO) the preparation method of hydrogen sulfide gas sensitive composite material, comprises the steps:

[0043] (1) In 60ml of ethanol, add 0.006mol lanthanum nitrate (La(NO 3 ) 3 ·6H 2 O), 0.036mol citric acid monohydrate, 0.0065mol lithium nitrate (LiNO 3 ), after stirring and dissolving, slowly add 0.012mol tetrabutyl titanate, 0.72mol ethylene glycol, stir and mix for 40min, set aside;

[0044] (2) 0.73mmol of indium nitrate (In(NO 3 ) 3 .4.5H 2 O) join in the mixed solution of step (1), stir 40min to dissolve completely, obtain uniform solvothermal precursor solution;

[0045] (3) Transfer the mixed solution of step (2) into a non-magnetic steel reaction kettle lined with 100 milliliters of polytetrafluoroethylene, and put it into a blast drying oven at 160° C. for solvothermal reaction for 6 hours;

[0046] (4) After the reaction in step (3), the reaction kettle was cooled naturally, and then centrifuged and wa...

Embodiment 3

[0048] A kind of In 2 o 3 / Li 0.5 La 0.5 TiO 3 (LLTO) the preparation method of hydrogen sulfide gas sensitive composite material, comprises the steps:

[0049] (1) In 60ml of ethanol, add 0.008mol lanthanum nitrate (La(NO 3 ) 3 ·6H 2 O), 0.035mol citric acid monohydrate, 0.0085mol lithium nitrate (LiNO 3 ), after stirring and dissolving, slowly add 0.016mol tetrabutyl titanate, 0.07mol ethylene glycol, stir and mix for 30min, set aside;

[0050] (2) 0.8mmol of indium nitrate (In(NO 3 ) 3 .4.5H 2 O) join in the mixed solution of step (1), stir 40min to dissolve completely, obtain uniform solvothermal precursor solution;

[0051] (3) Transfer the mixed solution of step (2) into a non-magnetic steel reaction kettle lined with 100 milliliters of polytetrafluoroethylene, and put it into a blast drying oven at 170° C. for solvothermal reaction for 7 hours;

[0052] (4) After the reaction in step (3), the reaction kettle was cooled naturally, and then centrifuged and was...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Sensitivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an In 2 o 3 / Li 0.5 La 0.5 TiO 3 The preparation method of the hydrogen sulfide gas-sensitive composite material comprises the following steps: (1) sequentially adding lanthanum nitrate, citric acid, lithium nitrate, tetrabutyl titanate, and ethylene glycol into a certain amount of ethanol, stirring and mixing evenly, and setting aside; 2) adding a certain amount of indium nitrate to the mixed solution of step (1), stirring until completely dissolved to obtain a mixed solution; (3) transferring the mixed solution of step (2) into a reaction kettle for solvothermal reaction; (4) After the reaction in step (3), cool naturally, then centrifuge, and dry and anneal the resulting product to obtain the In 2 o 3 / Li 0.5 La 0.5 TiO 3 Hydrogen sulfide gas sensing composite material. In prepared by the present invention 2 o 3 / Li 0.5 La 0.5 TiO 3 The hydrogen sulfide gas-sensing composite material has shorter response and recovery time than most hydrogen sulfide gas sensors reported in the literature, can detect hydrogen sulfide gas quickly, and detects hydrogen sulfide in a wide range.

Description

technical field [0001] The invention belongs to H 2 The technical field of S gas sensitive materials, in particular, relates to a kind of In 2 o 3 / Li 0.5 La 0.5 TiO 3 (LLTO) hydrogen sulfide gas sensing composite material and its preparation method and application. Background technique [0002] Hydrogen sulfide gas is a poisonous gas with a pungent smell. Very low concentrations of hydrogen sulfide gas can damage the human respiratory system and nervous system. On the one hand, hydrogen sulfide gas can exist in swamps, sewers, toilets, and human bodies through bacterial decomposition of organic matter; on the other hand, hydrogen sulfide gas is also widely present in oil, natural gas, and coal mines. It will cause damage to equipment and bring life threats of explosion and poisoning to mining personnel. Therefore, the detection of hydrogen sulfide gas is urgent. [0003] Gas sensor technology plays an important role in the future development, and there is an increas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G15/00C01G23/00G01N27/12
CPCC01G15/00C01G23/003G01N27/127G01N27/12C01P2002/72C01P2004/03C01P2004/80
Inventor 范佳杰刘自豪马梦君张先乐孙龙范向伟张忠新高彩琴
Owner ZHENGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com