A kind of magnetic superhydrophobic polystyrene-based porous material and preparation method thereof

A polystyrene, superhydrophobic technology used in the field of composite materials

Active Publication Date: 2021-09-14
SOUTHWEST PETROLEUM UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the research on this kind of functional materials with special wettability needs to be further deepened.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of magnetic superhydrophobic polystyrene-based porous material and preparation method thereof
  • A kind of magnetic superhydrophobic polystyrene-based porous material and preparation method thereof
  • A kind of magnetic superhydrophobic polystyrene-based porous material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A method for preparing a magnetic superhydrophobic polystyrene-based porous material, the steps are as follows:

[0037] S1. Disperse 8 parts by weight of ferric chloride hexahydrate in 82 parts by weight of ethylene glycol to form a transparent solution A; then disperse 7 parts by weight of anhydrous sodium acetate and 3 parts by weight of polyethyleneimine in solution A. 400rpm mechanical stirring for 30min to form a uniform mixed solution B. Add the mixed solution B into a polytetrafluoroethylene reactor, react at 200°C for 8 hours to form a black product, and then wash it several times with absolute ethanol and deionized water under the action of a magnetic field to prepare amino-modified ferric oxide.

[0038] S2, adding 2000 parts by weight of deionized water to 15 parts by weight of styrene, 10 parts by weight of glycidyl methacrylate, 25 parts by weight of divinylbenzene, 5 parts by weight of amino-modified ferric oxide, 15 parts by weight of Span80 , 5 parts b...

Embodiment 2

[0041] A method for preparing a magnetic superhydrophobic polystyrene-based porous material, the steps are as follows:

[0042] S1. Disperse 5 parts by weight of ferric chloride hexahydrate in 50 parts by weight of glycerol to form a transparent solution A; then disperse 4 parts by weight of anhydrous sodium acetate and 10 parts by weight of polyether amine in solution A, at 200rpm Stir mechanically for 60 min to form a homogeneously mixed solution B. Add the mixed solution B into a polytetrafluoroethylene reactor, react at 100°C for 24 hours to form a black product, and then wash it several times with absolute ethanol and deionized water under the action of a magnetic field to prepare amino-modified ferric oxide.

[0043] S2, adding 100 parts by weight of deionized water to 10 parts by weight of styrene, 50 parts by weight of glycidyl methacrylate, 10 parts by weight of ethylene glycol dimethacrylate, 20 parts by weight of amino-modified ferric oxide, In a mixed system of 50...

Embodiment 3

[0046] S1. Disperse 20 parts by weight of ferric chloride hexahydrate in 90 parts by weight of ethanol to form a transparent solution A; then disperse 20 parts by weight of anhydrous sodium acetate and 1 part by weight of polyacrylamide in solution A, and mechanically stir at 200rpm 5min to form a homogeneous mixed solution B. Add the mixed solution B into a polytetrafluoroethylene reactor, react at 300°C for 4 hours to form a black product, and then wash it several times with absolute ethanol and deionized water under the action of a magnetic field to prepare amino-modified ferric oxide.

[0047]S2, adding 3000 parts by weight of deionized water to 50 parts by weight of styrene, 50 parts by weight of glycidyl stearate, 50 parts by weight of pentaerythritol triacrylate, 50 parts by weight of amino-modified ferric oxide, 50 parts by weight of Tween80 and 10 parts by weight of benzoyl peroxide in a mixed system, and mechanically emulsified for 60 minutes under the action of an e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a magnetic superhydrophobic polystyrene-based porous material, which comprises raw materials such as styrene monomer, epoxy group-containing vinyl monomer, amino-modified iron tetraoxide and crosslinking agent, in the initiator Under the action of , water and emulsifier, polymerize at 40-80°C for 4-24h to obtain a magnetic superhydrophobic polystyrene-based porous material. The crosslinking agent is one of ethylene glycol dimethacrylate, divinylbenzene, triallyl isocyanurate, pentaerythritol triacrylate, and trimethylolpropane triacrylate. The epoxy-containing ethylenic monomer is one of glycidyl methacrylate, glycidyl acrylate, and glycidyl stearate. The magnetic superhydrophobic polystyrene-based porous material prepared by the invention has both superhydrophobicity and magnetic response, can be used for oil-water separation in the food industry, chemical industry and petroleum industry, and can perform automatic oil-water separation under magnetic drive.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a magnetic superhydrophobic polystyrene-based porous material and a preparation method thereof. Background technique [0002] In today's world, mining, textile, food, petrochemical, metal / steel and other industries produce a large amount of oily wastewater, which has become the main pollutant in the world and has a serious impact on people's daily life and the ecological environment. However, oil removal from oily wastewater remains a challenge. Methods such as gravity separation, centrifugation, ultrasonic separation, air flotation, electric field, adsorption and biological treatment are widely used in the treatment of oily wastewater. Among these methods, the application of adsorption is considered to be one of the most promising technologies due to its convenience, low cost, high efficiency, and no secondary pollution. [0003] Therefore, researchers have develop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/36C08F212/08C08F220/32C08F222/14C08F222/20C08F226/06C08F2/44C08J9/28C08K9/04C08K3/22C08L25/06C08L25/00C08L33/14C08L39/04H01F1/42
CPCC08F2/44C08F212/08C08F212/36C08F220/32C08F222/10C08F226/06C08J9/28C08J2325/00C08J2325/06C08J2333/14C08J2339/04C08K3/22C08K9/04C08K9/08C08K2003/2275H01F1/42
Inventor 赵春霞黄浩然郭长远李云涛邓诗琴向东郭翠翠
Owner SOUTHWEST PETROLEUM UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com