Polymer material wrappage of pigment yellow 138 or derivative of pigment yellow 138, preparation method of polymer material wrappage, and downstream product of polymer material wrappage

A technology of polymer materials and derivatives, applied in the field of pigments, can solve the inevitable generation of a large amount of waste acid, can not be used and other problems

Active Publication Date: 2020-02-14
DONGGUAN UNIV OF TECH
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Equally, this method also can inevitably produce a large amount of waste acid, waste caustic, highly saline waste water and waste alcohol
[0005] In addition, Pigment Yellow 138 obtained by traditional organic synthesis methods is mostly not suitable for high-temperature thermoplastic resins. Although its heat resistance is as high as 300 ° C, it cannot be used for PMMA (polymethyl methacrylate), PC (poly Carbonate), PET (polyethylene terephthalate) and other high-temperature materials, such as BASF's PALIOTOLYELLOW K 0961HD (pigment yellow 138 powder product), clearly stated in its product description that the pigment is not suitable for PMMA , PC, PA (polyamide) and PET, its main application is hydrocarbon polymers, such as polyvinyl chloride, polyethylene, polystyrene, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer material wrappage of pigment yellow 138 or derivative of pigment yellow 138, preparation method of polymer material wrappage, and downstream product of polymer material wrappage
  • Polymer material wrappage of pigment yellow 138 or derivative of pigment yellow 138, preparation method of polymer material wrappage, and downstream product of polymer material wrappage
  • Polymer material wrappage of pigment yellow 138 or derivative of pigment yellow 138, preparation method of polymer material wrappage, and downstream product of polymer material wrappage

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] A method for preparing a polymer material wrapping of Pigment Yellow 138 or its derivatives in one embodiment, comprising the following steps:

[0036] The monoacid anhydride aromatic compound, 8-aminoquinaldine compound, solid organic acid and thermoplastic polymer material are mixed, extruded or kneaded to obtain the polymer material wrapping of Pigment Yellow 138 or its derivatives.

[0037] Wherein, 8-aminoquinaldine compound, structure is as shown in formula (I):

[0038] R1, R2, R3, R4 and R5 are each independently H, methyl, ethyl, alkoxy, alkylthio or halogen.

[0039] Monoacid anhydride aromatic compound, the structure is as shown in formula (II):

[0040] X is an aromatic group (such as benzene ring, naphthalene, pyrene, anthracene, phenanthrene, etc.) or a halogenated derivative of an aromatic group.

[0041] Further, the 8-aminoquinaldine compound is one of the following compounds:

[0042] R1', R2', R3', R4', R5', R6' are each independently methy...

Embodiment 1

[0075]

[0076] Mix (40g, 140mmol) tetrachlorophthalic anhydride, (11g, 70mmol) 8-aminoquinaldine, (3g, 16mmol) citric acid and 0.5kg PMMA, extrude the reaction in a single-screw extruder, cool and dry and cut into pellets , to obtain PMMA masterbatch of yellow pigment yellow 138.

[0077] After grinding the PMMA masterbatch of Pigment Yellow 138 prepared in Example 1, toner particles are obtained, and its size distribution spectrum is as follows: Figure 4 shown. Tested by Malvern particle size analyzer, D50=4.09 μm, D99=10.6 μm.

[0078] figure 1 The reflectance spectrogram of the PMMA color masterbatch crude product of the pigment yellow 138 prepared by embodiment 1 is mixed with ABS and injected into a sheet, by figure 1 It can be seen that the plastic sheet exhibits similar absorption spectrum properties to traditional pigment yellow.

Embodiment 2

[0080] Mix (40g, 140mmol) tetrachlorophthalic anhydride, (11g, 70mmol) 8-aminoquinaldine, (3g, 16mmol) citric acid and 0.5kg PC, extrude the reaction in a twin-screw extruder, cool and dry and cut into pellets , to obtain yellow pigment yellow 138 PC masterbatch.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a polymer material wrappage of pigment yellow 138 or a derivative of pigment yellow 138, a preparation method of the polymer material wrappage, and a downstream product of thepolymer material wrappage. The method comprises the following steps: mixing a monoanhydride aromatic compound, an 8-aminoquinaldine compound, a solid organic acid and a thermoplastic polymer material; adjusting the reaction molar ratio of the raw materials and the mass content of pigment yellow 138 or the derivative of pigment yellow 138 in a final product so as to realize extruding or kneading of an obtained mixture and obtain the polymer material wrappage of pigment yellow 138 or the derivative of pigment yellow 138 in one step. The raw material reactants of pigment yellow 138 or the derivative of pigment yellow 138 have better dispersity in the high polymer material; therefore, pigment yellow 138 or the derivative of pigment yellow 138 can be directly generated and uniformly dispersedin the high polymer material in the extrusion or kneading process, no solvent is required to be added in the process, separation and purification are not required after the reaction is finished, the generation of three wastes in the traditional synthesis process of pigment yellow 138 or the derivative is avoided, the process flow is greatly simplified, and the energy consumption is reduced.

Description

technical field [0001] The invention relates to the technical field of pigments, in particular to a polymer material wrapper of Pigment Yellow 138 or its derivatives, its preparation method and its downstream products. Background technique [0002] Pigment Yellow 138 is a high-performance organic pigment. Because of its strong coloring ability and excellent heat resistance, weather resistance and solvent resistance, it occupies a large proportion in the yellow pigment market. In addition, in addition to being used in conventional industrial fields such as coatings, inks, paints, etc., Pigment Yellow 138 is also widely used in high-tech aspects of LEDs and photosensitive films. Usually, Pigment Yellow 138 is prepared through traditional organic synthesis steps, which requires the use of a large amount of organic solvents, such as alcohols, ammonia, organic acids, and organic high-boiling solvents (including DMF, NMP, DMSO, etc.), and organic synthesis reactions to obtain crud...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08K9/10C08K5/3437C08J3/22C08L33/12C08L69/00C08L23/12C08L27/06C08L67/02C09D7/41C09D11/037D06P1/00C09B69/00
CPCC08J3/226C08J2367/02C08J2369/00C08J2423/12C08J2427/06C08J2433/12C08J2469/00C08K5/3437C08K9/10C09B69/00C09D11/037C09D7/41D06P1/0052
Inventor 李辰魏文山段若蒙赵雁飞刘志宏田禾
Owner DONGGUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products