A high-weldable environment-friendly ultra-fine solder wire for intelligent manipulator welding and its preparation method

A technology of intelligent manipulator and solder wire, applied in welding equipment, welding medium, welding/cutting medium/material, etc., can solve the problem of easy broken core of solder wire, increase service life, refine grains, improve corrosion resistance sexual effect

Active Publication Date: 2021-12-31
中山翰华锡业有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the technical problem that the existing solder wire is easy to break the core, the present invention provides a highly solderable and environmentally friendly ultra-fine solder wire for intelligent manipulator welding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-weldable environment-friendly ultra-fine solder wire for intelligent manipulator welding and its preparation method
  • A high-weldable environment-friendly ultra-fine solder wire for intelligent manipulator welding and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A high-weldable environment-friendly ultra-fine solder wire for intelligent manipulator welding, including the following components by weight, 97.2% solder alloy, 2.80% flux, wherein the composition of the solder alloy is as shown in Table 2, the flux The composition ratio is described in Table 3, and its preparation method comprises the following steps:

[0031] Weigh each component according to the weight percentages in Table 2 and Table 3, and set aside; add rosin into the reaction kettle and heat to 130°C, add solvent and thermosetting resin and stir for 20 minutes after dissolving, then add thixotropic agent and stir until completely dissolved, Lower the temperature to 90°C, add active agent, surfactant and corrosion inhibitor and stir for 60 minutes, cool to obtain flux; melt the tin into the melting furnace and melt to 360°C, heat and stir for 20 minutes, remove the tin slag, add Stir silver, copper, and molybdenum for 20 minutes, then heat up to 430°C, add ceriu...

Embodiment 2

[0033] A high-weldable environment-friendly ultra-fine solder wire for intelligent manipulator welding, comprising the following components by weight, 97.40% solder alloy, 2.60wt% flux, wherein the composition ratio of the solder alloy is shown in Table 2. The component distribution of flux is as described in table 3, and its preparation method comprises the following steps:

[0034] Weigh each component according to the weight percentages in Table 2 and Table 3, and set aside; add the rosin into the reactor and heat it to 135°C, after it dissolves, add the solvent and the thermosetting resin and stir for 30 minutes, then add the thixotropic agent and stir until it is completely dissolved. Lower the temperature to 80°C, add active agent, surfactant and corrosion inhibitor and stir for 50 minutes, cool to obtain flux; melt the tin into the melting furnace and melt to 350-360°C, keep stirring for 250min, then remove the tin slag , add silver, copper, molybdenum and stir for 10 m...

Embodiment 3

[0036] A high-weldability environment-friendly ultra-fine solder wire for intelligent manipulator welding, comprising the following components by weight, 96.9wt% solder alloy, 3.1wt% flux, wherein the composition ratio of the solder alloy is shown in Table 2, The component distribution of flux is as described in table 3, and its preparation method comprises the following steps:

[0037] Weigh each component according to the weight percentages in Table 2 and Table 3, and set aside; add rosin into the reaction kettle and heat to 150°C, after dissolving, add solvent and thermosetting resin and stir for 2 minutes, then add thixotropic agent and stir until completely dissolved, Lower the temperature to 80°C, add active agent, surfactant and corrosion inhibitor and stir for 40 minutes, cool to obtain flux; melt the tin into the melting furnace and melt to 355°C, keep stirring for 25 minutes, remove the tin slag, add Stir silver, copper and molybdenum for 10 minutes, then raise the t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-weldable environment-friendly ultra-fine solder wire for intelligent manipulator welding and a preparation method thereof. Silver, copper, molybdenum, cerium, tellurium and lutetium, the addition of cerium can change the structure of the solder, thereby refining the grains, reducing solder joint bridging, changing the surface wettability of the solder alloy, improving creep properties, tensile Characteristics, the addition of tellurium can improve the corrosion resistance, wear resistance and strength of the material, can improve the tensile strength of the solder and prevent the generation of tin whiskers, lutetium has good conductivity and ductility, and has a strong activation in solder alloys The powder has an excellent effect on improving the electrothermal performance and anti-oxidation performance, improves the tensile strength and toughness of the solder, has good solder wire wettability, excellent tensile strength and is lead-free and environmentally friendly. This application has the advantages of high solderability and not easy to break the core , High solderability and lead-free environmental protection development of products when applied to high-end application fields such as intelligent manipulator welding.

Description

【Technical field】 [0001] The invention belongs to the technical field of welding materials, and in particular relates to a high-weldable environment-friendly ultra-fine solder wire used for welding with an intelligent robot and a preparation method thereof. 【Background technique】 [0002] With the development of electronic products and their technology, products are gradually developing towards functionalization and miniaturization, and the requirements for solder wire are getting higher and higher. The microelectronic interconnection material industry is also growing with the development of the domestic electronic industry Gradually growing up, ordinary solder wire products are not inferior to foreign products, but there is still a considerable gap with foreign products in more refined products and high-end applications such as robot welding, and some even completely rely on imports. For example, for micro-electronic assemblies (SMT), circuit boards, components, micro-conne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/26B23K35/36B23K35/40
CPCB23K35/262B23K35/3613B23K35/3612B23K35/40
Inventor 李爱良周建龙斌李义成汪亮
Owner 中山翰华锡业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap