A kind of preparation method of low-viscosity high-hydroxyl value polymer surface strengthening agent for paper

A technology of surface enhancer and high hydroxyl value, which is applied in the direction of enhancer addition, papermaking, paper coating, etc., and can solve the problems of poor stability and low crosslinking density of acrylic resin

Active Publication Date: 2022-03-29
浙江恒川新材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the poor stability and low crosslinking density of water-based high-hydroxyl value acrylic resins, the purpose of the present invention is to provide a method for preparing a low-viscosity, high-stability, ultra-high-hydroxyl polymer surface enhancer for paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of low-viscosity high-hydroxyl value polymer surface strengthening agent for paper

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The invention provides a method for preparing a low-viscosity high-hydroxyl value polymer surface enhancer for paper, comprising the following steps:

[0033] 1) In parts by weight, add 25 parts of diethylene glycol dimethyl ether dispersion medium into the reactor, and heat to 120-140°C.

[0034] 2) Mix the soft vinyl monomer, hard vinyl monomer, hydroxyl-containing vinyl monomer, glycidyl methacrylate and isobornyl methacrylate in a weight ratio of 20:54:14:1:3 Mixing was performed to prepare a monomer mixed liquid A.

[0035]3) Weigh 69 parts of monomer mixture A, add 1.1-1.4 parts of dibenzoyl peroxide and 0.08-0.15 parts of tert-butyl peroxybenzoate double-initiator system, mix well and slowly add double-initiator system , the dropping time is 2 to 4 hours, and then the heat preservation reaction is continued for 60 to 90 minutes to form a polymer core.

[0036] 4) Weigh 17-69 parts of monomer mixture A, add 3 parts of acrylic acid monomer, 0.5-1.5 parts of diben...

Embodiment 1

[0048] 1) In parts by weight, add 25 parts of diethylene glycol dimethyl ether dispersion medium into the reactor, and heat to 120°C.

[0049] 2) Soft vinyl monomer butyl acrylate, hard vinyl monomer methyl methacrylate, hydroxyl-containing vinyl monomer hydroxypropyl acrylate, glycidyl methacrylate and isobornyl methacrylate 20:54:14:1:3 weight ratio was mixed to prepare monomer mixture A.

[0050] 3) Weigh 69 parts of monomer mixture A, add 1.1 parts of dibenzoyl peroxide and 0.8 parts of tert-butyl peroxybenzoic acid double initiator system, mix well and slowly add the double initiator system dropwise, the dropping time for 2 hours, and then continue to keep warm for 60 minutes to form a polymer core.

[0051] 4) Weigh 17 parts of monomer mixture A, add 3 parts of acrylic acid monomer, 0.5 part of dibenzoyl peroxide, and 0.05 part of tert-butyl peroxybenzoate, and mix well to prepare monomer mixture B.

[0052] 5) Gradually drop the monomer mixture solution B into the pol...

Embodiment 2

[0058] 1) In parts by weight, add 25 parts of diethylene glycol dimethyl ether dispersion medium into the reactor, and heat to 125°C.

[0059] 2) Soft vinyl monomer butyl methacrylate, hard vinyl monomer methyl methacrylate, hydroxyl-containing vinyl monomer hydroxypropyl acrylate, glycidyl methacrylate and methacrylate isoborneol The esters were mixed in a weight ratio of 20:54:14:1:3 to obtain a monomer mixture A.

[0060] 3) Weigh 69 parts of monomer mixture A, add 1.2 parts of dibenzoyl peroxide and 0.09 part of tert-butyl peroxybenzoic acid double initiator system, mix well and slowly add double initiator system, the time for adding for 3 hours, and then continue the incubation reaction for 70 minutes to form a polymer core.

[0061] 4) Weigh 21 parts of monomer mixture A, add 3 parts of acrylic acid monomer, 0.8 part of dibenzoyl peroxide, and 0.1 part of tert-butyl peroxybenzoate, and mix well to prepare monomer mixture B.

[0062] 5) Gradually drop the monomer mixtur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
viscosityaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a low-viscosity high-hydroxyl value polymer surface enhancer for paper. First, diethylene glycol dimethyl ether is used as the dispersion medium, butyl acrylate, methyl methacrylate, hydroxypropyl acrylate, glycidyl methacrylate and isobornyl methacrylate are used as raw materials, and diphenyl peroxide is used. Acrylic acid and tert-butyl peroxybenzoate dual initiation system, so that the monomer undergoes radical polymerization to prepare the acrylate core; add acrylic acid dropwise, and the carboxyl group on its molecular chain can react with the epoxy group on the glycidyl methacrylate to produce Hydroxyl; then add triethanolamine and dioctyl phthalate to neutralize to form quaternary ammonium salt, and prepare ultra-high hydroxyl acrylic resin through high-speed water dispersion; finally, construct the polymer surface for paper by compounding water-based blocked polyisocyanate crosslinking agent enhancer. The product of the present invention has multiple cross-linked network structures, and can also form a cross-linked network with paper base materials, thereby efficiently increasing the performance of the paper base.

Description

technical field [0001] The invention belongs to and relates to a preparation method of a low-viscosity high-hydroxyl value polymer surface enhancer for paper. Background technique [0002] The water-based hydroxyacrylic resin is usually composed of acrylic acid, hydroxyl group-containing acrylate monomers and functional acrylate monomers, and then adding a suitable free radical polymerization initiator to form a polymer. After the reaction is completed, add organic alcohol amine to neutralize the carboxyl group on the surface of the polymer, and then add water to disperse under the condition of high-speed rotation. This is also the most effective method for obtaining high-hydroxyl value water-based acrylic resin emulsion. When the water-based high-hydroxyl value acrylic resin is cross-linked with the curing agent, there are many cross-linking sites, and the resin emulsion is easier to form a good compatible system with the curing agent, which makes the composite system more ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F265/06C08F220/18C08F220/14C08F220/20C08F220/32C08F220/06C08F212/08C08G18/80C08G18/63D21H19/24D21H21/16D21H21/18
CPCC08F265/06C08G18/8077C08G18/8064C08G18/633D21H19/24D21H21/16D21H21/18C08F220/1804C08F220/14C08F220/20C08F220/325C08F220/1811C08F220/06C08F220/1802C08F212/08
Inventor 赵新民邱旭峰杨柳青林俊辉陈宪王建军
Owner 浙江恒川新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More