A processing technology and trash can technology, applied in the direction of plastic recycling, recycling technology, etc., can solve the problems of difficult particle size control, large floor space, large limitations, etc., to avoid frequent equipment replacement, cost saving, uniform size Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0031]A kind of trash can processing technology, comprises the following steps:
[0032] (1) After heating and softening polyvinyl chloride, add polyvinylidene fluoride, acrylonitrile-butadiene-styrene copolymer and liquid paraffin to mix with an ultrasonic oscillator for ultrasonic vibration homogenization, and the homogenized solution is ready for use;
[0033] (2) Mix the silicone resin, alkyd resin, and basalt to adjust the pH to 7.8, then mechanically modify the blender at high speed to obtain a mixed resin for later use;
[0034] (3) Mix hexamethylphosphoric triamide, zinc oxide, silicon dioxide, and flame retardant, then heat up and stir, then add the above homogeneous liquid and homogenize again by ultrasonic vibration to obtain a mixed liquid for later use;
[0035] (4) Add phenoxyethanol, 1,2,3-benzotriazole and plasticizer to the above mixed solution and stir evenly at a high temperature of 120°C to obtain the mixed material for later use;
[0036] (5) Add the abov...
Embodiment 2
[0045] A kind of trash can processing technology, comprises the following steps:
[0046] (1) After heating and softening polyvinyl chloride, add polyvinylidene fluoride, acrylonitrile-butadiene-styrene copolymer and liquid paraffin to mix with an ultrasonic oscillator for ultrasonic vibration homogenization, and the homogenized solution is ready for use;
[0047] (2) Mix the silicone resin, alkyd resin, and basalt to adjust the pH to 7.9, and then mechanically modify the mixer at high speed to obtain a mixed resin for later use;
[0048] (3) Mix hexamethylphosphoric triamide, zinc oxide, silicon dioxide, and flame retardant, then heat up and stir, then add the above homogeneous liquid and homogenize again by ultrasonic vibration to obtain a mixed liquid for later use;
[0049] (4) Add phenoxyethanol, 1,2,3-benzotriazole and plasticizer to the above mixed solution and stir evenly at a high temperature of 125°C to obtain the mixed material for later use;
[0050] (5) Add the a...
Embodiment 3
[0054] A kind of trash can processing technology, comprises the following steps:
[0055] (1) After heating and softening polyvinyl chloride, add polyvinylidene fluoride, acrylonitrile-butadiene-styrene copolymer and liquid paraffin to mix with an ultrasonic oscillator for ultrasonic vibration homogenization, and the homogenized solution is ready for use;
[0056] (2) Mix the silicone resin, alkyd resin and basalt to adjust the pH to 8.0, then mechanically modify the mixer at high speed to obtain a mixed resin for later use;
[0057] (3) Mix hexamethylphosphoric triamide, zinc oxide, silicon dioxide, and flame retardant, then heat up and stir, then add the above homogeneous liquid and homogenize again by ultrasonic vibration to obtain a mixed liquid for later use;
[0058] (4) Add phenoxyethanol, 1,2,3-benzotriazole and plasticizer to the above mixed solution and stir evenly at a high temperature of 130°C to obtain the mixed material for later use;
[0059] (5) Add the above-...