Porcelain formula and production process

A production process and technology for porcelain, applied in metal material coating process, anodizing, electrolytic coatings, etc., can solve the problems of poor antifouling performance, antibacterial performance, poor mechanical strength, etc., and achieve improved mechanical performance and antibacterial performance. , Improve mechanical properties, improve the effect of force

Inactive Publication Date: 2020-12-25
长沙而道新能源科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a porcelain formula and production process to solve technical problems such as poor mechanical strength, poor antifouling performance and poor antibacterial performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A porcelain formula, which is made of the following raw materials: 10kg of zinc powder, 0.8kg of cerium oxide, 4kg of alumina, 35kg of sodium silicate, 10kg of sodium fluoroaluminate, 13kg of aniline, 35kg of nano-graphite, and silicon dioxide coated hydrogenation Titanium 45kg; Wherein, described silicon dioxide coated titanium hydride is prepared by the following method:

[0038] (A) firstly add titanium hydride into an aqueous ethanol solution with a mass concentration of 80%, and disperse evenly with ultrasonic waves to obtain a prefabricated solution;

[0039] (B) Then add alkylphenol polyoxyethylene ether and silicon tetrachloride to p-bromotoluene, then slowly add the preformed solution dropwise while stirring, hydrolysis occurs, and post-treatment, the silicon dioxide-coated titanium hydride is obtained .

[0040] The particle size of nano-graphite is 30nm.

[0041] When preparing silicon dioxide-coated titanium hydride, the mass ratio of titanium hydride, eth...

Embodiment 2

[0057] A porcelain formula made from the following raw materials: 10kg of zinc powder, 1kg of cerium oxide, 3kg of alumina, 45kg of sodium silicate, 8kg of sodium fluoroaluminate, 15kg of aniline, 25kg of nano-graphite, and titanium hydride coated with silica 55kg; Wherein, the silicon dioxide coated titanium hydride is prepared by the following method:

[0058] (A) firstly add titanium hydride into an aqueous ethanol solution with a mass concentration of 60%, and disperse evenly with ultrasonic waves to obtain a prefabricated liquid;

[0059] (B) Then add alkylphenol polyoxyethylene ether and silicon tetrachloride to p-bromotoluene, then slowly add the preformed solution dropwise while stirring, hydrolysis occurs, and post-treatment, the silicon dioxide-coated titanium hydride is obtained .

[0060] The particle size of nano-graphite is 50nm.

[0061] When preparing silicon dioxide-coated titanium hydride, the mass ratio of titanium hydride, ethanol aqueous solution, p-brom...

Embodiment 3

[0077] A porcelain formula made from the following raw materials: 10kg of zinc powder, 0.9kg of cerium oxide, 3.5kg of alumina, 40kg of sodium silicate, 9kg of sodium fluoroaluminate, 14kg of aniline, 30kg of nano-graphite, coated with silica Titanium hydride 50kg; Wherein, described silicon dioxide coated titanium hydride is prepared by the following method:

[0078] (A) firstly add titanium hydride into an aqueous ethanol solution with a mass concentration of 70%, and disperse evenly with ultrasonic waves to obtain a prefabricated liquid;

[0079] (B) Then add alkylphenol polyoxyethylene ether and silicon tetrachloride to p-bromotoluene, then slowly add the preformed solution dropwise while stirring, hydrolysis occurs, and post-treatment, the silicon dioxide-coated titanium hydride is obtained .

[0080] The particle size of nano-graphite is 40nm.

[0081] When preparing silicon dioxide-coated titanium hydride, the mass ratio of titanium hydride, ethanol aqueous solution, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a porcelain formula and a production process. According to the porcelain formula and the production process, zinc powder, cerium oxide, aluminum oxide, sodium silicate, sodium fluoroaluminate, aniline, nano-graphite, silicon dioxide coated titanium hydride and the like are used as raw materials to prepare a porcelain product which has excellent mechanical strength, an antifouling property and an antibacterial property, wherein the silicon dioxide coated titanium hydride is prepared by a method which comprises the following steps of: firstly, adding titanium hydride intoan ethanol aqueous solution, and ultrasonically dispersing uniformly to obtain prefabricated liquid; and then adding alkylphenol ethoxylates and silicon tetrachloride into p-bromotoluene, slowly dropwise adding the prefabricated liquid while stirring, and carrying out hydrolysis and post-treatment to obtain the silicon dioxide coated titanium hydride.

Description

technical field [0001] The invention relates to the technical field of porcelain, in particular to a porcelain formula and production process. Background technique [0002] Porcelain is shaped by firing at a high temperature in a kiln, and the glaze color on the surface of the porcelain will change chemically due to the temperature difference. The whiteness of most porcelain is 65-75, and the glossiness is less than 80%, which can only meet the requirements of ordinary daily use, and it is difficult to meet the higher aesthetic requirements. [0003] Porcelain is a kind of utensil composed of porcelain stone, kaolin, quartz stone, mullite, etc., with glass glaze or painted surface applied on the surface. Traditional porcelain is mostly produced with people's needs for daily life, such as tableware, tea set, coffee set, wine set, and vase containers used in daily life. However, with the improvement of living standards and the expansion of the application field of porcelain,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/05C22C18/00C22C32/00C23C8/00C25D11/34
CPCC22C1/05C22C18/00C22C32/001C23C8/00C25D11/026C25D11/34
Inventor 卯志华
Owner 长沙而道新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com