Raw materiel cement additive and application thereof
A technology of cement additives and additives, applied in the field of cement additives, can solve problems such as poor effect and reduce energy consumption, and achieve the effects of saving grinding power consumption, improving grinding efficiency, and reducing activation energy
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0022] A raw cement additive comprises the following materials in parts by weight: 8-15 parts of diethanol monoisopropanolamine, 25 parts of sodium tripolyphosphate, 7 parts of molasses, 15 parts of propylene glycol, 6 parts of nitrophenol, calcium chloride 15 parts, 3 parts of potassium nitrate, 5 parts of sodium nitrate, 8 parts of sodium silicate, 6 parts of sodium carbonate, 5 parts of sodium bicarbonate, 15 parts of modified sodium humate, and 80 parts of water.
[0023] The preparation method of described modified sodium humate comprises the following steps:
[0024] (1) Take humic acid ore powder, sodium hydroxide, sodium thiosulfate, add distilled water to mix, stir at 100-120 rpm, react at 100°C for 80 minutes, then centrifuge for 10 minutes at a speed of 3500 rpm, take supernatant;
[0025] (2) The supernatant is placed in a stainless steel tray, and dried in an oven at 80-180° C. to constant weight to obtain modified sodium humate.
[0026] The preparation method ...
Embodiment 2
[0028] A raw cement additive comprises the following materials in parts by weight: 8-15 parts of diethanol monoisopropanolamine, 15 parts of sodium tripolyphosphate, 3 parts of molasses, 8 parts of propylene glycol, 1 part of nitrophenol, calcium chloride 10 parts, 1 part potassium nitrate, 1 part sodium nitrate, 2 parts sodium silicate, 1 part sodium carbonate, 2 parts sodium bicarbonate, 8 parts modified sodium humate, 50 parts water.
[0029] The preparation method of described modified sodium humate comprises the following steps:
[0030] (1) Take humic acid ore powder, sodium hydroxide, sodium thiosulfate, add distilled water to mix, stir at 100-120 rpm, react at 100°C for 80 minutes, then centrifuge for 10 minutes at a speed of 3500 rpm, take supernatant;
[0031] (2) The supernatant is placed in a stainless steel tray, and dried in an oven at 80-180° C. to constant weight to obtain modified sodium humate.
[0032] The preparation method of the sodium tripolyphosphate ...
Embodiment 3
[0034] A raw cement additive comprising the following materials in parts by weight: 10 parts of diethanol monoisopropanolamine, 18 parts of sodium tripolyphosphate, 4 parts of molasses, 10 parts of propylene glycol, 3 parts of nitrophenol, and 12 parts of calcium chloride , 1 part of potassium nitrate, 1 part of sodium nitrate, 2 parts of sodium silicate, 1 part of sodium carbonate, 2 parts of sodium bicarbonate, 8 parts of modified sodium humate, and 50 parts of water.
[0035] The preparation method of described modified sodium humate comprises the following steps:
[0036] (1) Take humic acid ore powder, sodium hydroxide, sodium thiosulfate, add distilled water to mix, stir at 100-120 rpm, react at 100°C for 80 minutes, then centrifuge for 10 minutes at a speed of 3500 rpm, take supernatant;
[0037] (2) The supernatant is placed in a stainless steel tray, and dried in an oven at 80-180° C. to constant weight to obtain modified sodium humate.
[0038] The preparation meth...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com