Submicron graphene silver powder suitable for 5G field and preparation method and application thereof
A sub-micron, silver powder technology, applied in the field of electronics and micro-nano, can solve the problem of uneven doping of graphene-doped silver powder, and achieve excellent physical and chemical properties and electrical conductivity, good dispersion, and uniform doping.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0031] A method for preparing submicron RGO-doped silver powder applicable to the 5G field, comprising the steps of:
[0032] Step 1) Solution A: Add 1 g of RGO prepared into 1 L of ultrapure water, use a probe-type ultrasonic oscillator to sonicate for 30 minutes, and cool to room temperature for later use;
[0033] Solution B: Add 300g of silver nitrate into 1L of ultrapure water, stir continuously to dissolve it, and heat it to 30°C in a constant temperature water bath for later use;
[0034] Solution C: 166g of 80% hydrazine hydrate was added to solution A;
[0035] Solution D: add 100g polyvinyl alcohol and 5g oleylamine to solution C respectively, stir evenly, and heat to 30°C in a constant temperature water bath for later use;
[0036] In the case of uniform stirring, use a peristaltic pump to add solution B to solution D at a uniform speed, and the addition time is 5 minutes;
[0037] After the dropwise addition of the solution, continue to stir for 1 h, then filter,...
Embodiment 2
[0039] A method for preparing submicron RGO-doped silver powder applicable to the 5G field, comprising the steps of:
[0040] Step 1) Solution A: Add 1 g of RGO prepared into 1 L of ultrapure water, use a probe-type ultrasonic oscillator to sonicate for 30 minutes, and cool to room temperature for later use;
[0041] Solution B: Add 300g of silver nitrate into 1L of ultrapure water, stir continuously to dissolve it, and heat it to 30°C in a constant temperature water bath for later use;
[0042] C solution: the ascorbic acid of 233g is added in the A solution;
[0043] Solution D: Add 100g of Span 60 and 5g of Tween 80 into solution C, stir well, and heat to 30°C in a constant temperature water bath for later use;
[0044] In the case of uniform stirring, use a peristaltic pump to add solution B to solution D at a uniform speed, and the addition time is 3 minutes;
[0045] After the dropwise addition of the solution, continue stirring for 1.5 h, then filter, and freeze-dry f...
Embodiment 3
[0047] A method for preparing submicron RGO-doped silver powder applicable to the 5G field, comprising the steps of:
[0048] Step 1) Solution A: Add 1 g of RGO prepared into 1 L of ultrapure water, use a probe-type ultrasonic oscillator to sonicate for 30 minutes, and cool to room temperature for later use;
[0049] Solution B: Add 300g of silver nitrate into 1L of ultrapure water, stir continuously to dissolve it, and heat it to 30°C in a constant temperature water bath for later use;
[0050] Solution C: add 50g of formaldehyde to solution A;
[0051] Solution D: Add 100g of triethanolamine and 5g of sodium stearate into solution C, stir well, and heat to 30°C in a constant temperature water bath for later use;
[0052] In the case of uniform stirring, use a peristaltic pump to add solution B to solution D at a uniform speed, and the addition time is 1min;
[0053] After the dropwise addition of the solution, continue to stir for 2 hours, then filter, and freeze-dry for 1...
PUM
Property | Measurement | Unit |
---|---|---|
Concentration | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com