Polycarbonate film for bags and suitcases

A polycarbonate and film technology, applied in the field of polymer films, can solve the problems of difficult disentanglement, large interaction force of PC molecular chains, serious entanglement, etc., achieve good mechanical properties, widen the scope of use, and use effects improved effect

Active Publication Date: 2022-05-13
株洲地博光电材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although PC is a linear macromolecule, due to the large number of carbonyl groups and benzene rings in the molecular chain, the interaction force between PC molecular chains is strong, the entanglement is serious, and it is not easy to disentangle, which makes it difficult to produce molecular slippage under the action of external force. without deformation, the product size is stable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of polycarbonate material that is used on luggage, its preparation method comprises the following steps:

[0018] 1) configure the aqueous solution of sodium dodecylsulfonate, in the aqueous solution of described sodium dodecylsulfonate, the concentration of sodium dodecylsulfonate is 2g / L, and solvent is water; Add sepiolite in the aqueous solution of sodium base sulfonate, and sepiolite adds the solid-liquid mass ratio solid / liquid=1:50 of the aqueous solution of described sodium dodecylsulfonate, stirs and disperses to form suspension; The aqueous solution of ferric chloride, in the aqueous solution of ferric chloride, the concentration of ferric chloride is 4g / 100mL, and the solvent is water; The aqueous solution of ferric chloride is added in the suspension, the ferric chloride The aqueous solution is added to the suspension in a volume ratio of ferric chloride aqueous solution:suspension=1:2, then the suspension is kept in an ice-water bath to 0°C, and pyrr...

Embodiment 2

[0023] A kind of polycarbonate material that is used on luggage, its preparation method comprises the following steps:

[0024] 1) configure the aqueous solution of sodium dodecylsulfonate, in the aqueous solution of described sodium dodecylsulfonate, the concentration of sodium dodecylsulfonate is 2g / L, and solvent is water; Add sepiolite in the aqueous solution of sodium base sulfonate, and sepiolite adds the solid-liquid mass ratio solid / liquid=1:50 of the aqueous solution of described sodium dodecylsulfonate, stirs and disperses to form suspension; The aqueous solution of ferric chloride, in the aqueous solution of ferric chloride, the concentration of ferric chloride is 4g / 100mL, and the solvent is water; The aqueous solution of ferric chloride is added in the suspension, the ferric chloride The aqueous solution is added to the suspension in a volume ratio of ferric chloride aqueous solution:suspension=1:2, then the suspension is kept in an ice-water bath to 0°C, and pyrr...

Embodiment 3

[0029] A kind of polycarbonate material that is used on luggage, its preparation method comprises the following steps:

[0030] 1) configure the aqueous solution of sodium dodecylsulfonate, in the aqueous solution of described sodium dodecylsulfonate, the concentration of sodium dodecylsulfonate is 3g / L, and solvent is water; Add sepiolite in the aqueous solution of sodium base sulfonate, and sepiolite adds the solid-liquid mass ratio solid / liquid=1:50 of the aqueous solution of described sodium dodecylsulfonate, stirs and disperses to form suspension; The aqueous solution of ferric chloride, in the aqueous solution of ferric chloride, the concentration of ferric chloride is 5g / 100mL, and solvent is water; The aqueous solution of described ferric chloride is added in the described suspension, the ferric chloride The aqueous solution is added to the suspension in a volume ratio of ferric chloride aqueous solution:suspension=1:2, then the suspension is kept in an ice-water bath ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

A preparation method of the polycarbonate film comprises the following steps: 1) adding sepiolite into an aqueous solution of sodium dodecyl sulfate, then adding an aqueous solution of ferric chloride, pyrrole and ferric citrate, washing, drying, carrying out ball milling, and sieving with a 1000-mesh sieve to obtain sieved powder; 2) soaking the sieved powder in an aqueous solution of cerium trichloride and nickel dichloride, adding octadecyl trimethyl ammonium bromide, and calcining to obtain calcined powder; 3) soaking the calcined powder in an N, N-dimethylformamide solution of lipoic acid to form a mixture, and performing sealed heating, solid-liquid separation, washing and drying to obtain modified powder; and 4) carrying out melt blending on polycarbonate and the modified powder, carrying out extrusion granulation, and then carrying out injection molding and film drawing to form the polycarbonate film. The polycarbonate material prepared by the invention has good mechanical properties and certain heat resistance, the use effect of the polycarbonate body is obviously improved, the durability of the material is improved, and the use range of the film is widened.

Description

technical field [0001] The invention belongs to the technical field of polymer films, in particular to a polycarbonate film used for bags. Background technique [0002] Polycarbonate (PC) has excellent comprehensive performance, outstanding impact resistance, stable optical performance and good weather resistance. Various types of PCs with different properties including aliphatic, aromatic, and aliphatic-aromatic can be prepared according to the selection of polymerization process and raw materials. Although PC is a linear macromolecule, due to the large number of carbonyl groups and benzene rings in the molecular chain, the interaction force between PC molecular chains is strong, the entanglement is serious, and it is not easy to disentangle, which makes it difficult to produce molecular sliding under the action of external force. And deformation, the product size is stable. The performance of PC film has been further improved on the basis of raw materials, and its enviro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08K3/16C08K5/098C08K5/19C08K5/3415C08K5/42C08K7/26C08K9/04C08K13/06C08J5/18
CPCC08J5/18C08J2369/00C08K5/42C08K3/16C08K5/3415C08K7/26C08K5/098C08K5/19C08K9/04C08K13/06
Inventor 邵铭吴桂华夏杰
Owner 株洲地博光电材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com