Nanometer inorganic powder modified water emulsion wall paint and its prepn

A nano-inorganic, water-emulsion technology, applied in the direction of coating, latex paint, etc., can solve difficulties, reduce VOC content and other problems, and achieve the effect of good air quality

Inactive Publication Date: 2005-07-13
SUN YAT SEN UNIV
View PDF1 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

All countries in the world are currently committed to the research and development of low-VOC latex paint, but in the latex paint system, it is inevitable to add various a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nanometer inorganic powder modified water emulsion wall paint and its prepn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] The formula is: 26.2kg of tap water, 40kg of styrene-acrylic emulsion, 0.5kg of sodium polyacrylate dispersant, 0.1kg of wetting agent, 18kg of rutile titanium dioxide, 8kg of heavy calcium carbonate, 3kg of talcum powder, 1.8kg of nano-inorganic powder, polyether Modified silicone emulsion defoamer 0.5kg, hydroxyethyl cellulose 0.3kg, alkali-swellable thickener 0.3kg, hydrophobic modified polyurethane thickener 0.6kg, pH regulator (2-amino-2-methyl -1-propanol) 0.15kg, antifungal agent (2-n-octyl-4-isothiazoline-3-ketoimidazole) 0.15kg, bactericide 0.1kg, antifreeze agent (propylene glycol) 0.2kg, film-forming aid Agent (2,2,4-trimethyl-1,3-pentanediol methyl ethyl butyrate) 0.1kg;

[0050] Preparation process: (1) First, add tap water to the stainless steel dispersion steel, start the disperser, weigh various materials according to the formula standard, add cellulose thickener in sequence at a stirring speed of 250-350 rpm, disperse agent, wetting agent, 1 / 2 defoamer...

Embodiment 2

[0055] The formula is: 28.5kg of tap water, 24kg of pure acrylic emulsion, 8kg of silicon acrylic emulsion, 0.7kg of sodium polyacrylate dispersant, 0.15kg of wetting agent, 23kg of anatase titanium dioxide, 7kg of heavy calcium carbonate, 5kg of talcum powder, nano inorganic Powder 1.2kg, polyether modified silicone emulsion defoamer 0.6kg, hydroxyethyl cellulose 0.25kg, alkali swelling thickener 0.4kg, hydrophobic modified polyurethane thickener 0.5kg, pH regulator (soda ash ) 0.2kg, antifungal agent (isothiazole derivative) 0.1kg, fungicide 0.15kg, antifreeze agent (ethylene glycol) 0.1kg, film-forming aid (propylene glycol phenyl ether) 0.15kg;

[0056] Preparation process: (1) First, add tap water to the stainless steel dispersion steel, start the disperser, weigh various materials according to the formula standard, add cellulose thickener in sequence at a stirring speed of 250-350 rpm, disperse agent, wetting agent, 1 / 2 defoamer, pH regulator; after stirring evenly, add ...

Embodiment 3

[0061] The formula is: tap water 31.5kg, styrene-acrylic emulsion 20kg, pure acrylic emulsion 16kg, sodium polyacrylate dispersant 0.4kg, wetting agent 0.2kg, rutile titanium dioxide 14.4kg, heavy calcium carbonate 10kg, talcum powder 4kg, nano inorganic powder Body 1.5kg, polyether modified silicone emulsion defoamer 0.4kg, hydroxyethyl cellulose 0.15kg, alkali swelling thickener 0.5kg, hydrophobic modified polyurethane thickener 0.4kg, pH regulator (2- Amino-2-methyl-1-propanol) 0.2kg, antifungal agent (2-n-octyl-4-isothiazoline-3-ketoimidazole) 0.1kg, bactericide 0.2kg, antifreeze agent (glycerine Alcohol) 0.15kg, film-forming aid (benzyl alcohol) 0.1kg.

[0062] Preparation process: (1) First, add tap water to the stainless steel dispersion steel, start the disperser, weigh various materials according to the formula standard, add cellulose thickener in sequence at a stirring speed of 250-350 rpm, disperse agent, wetting agent, 1 / 2 defoamer, pH regulator; after stirring ev...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to one kind of nanometer inorganic powder modified water emulsion as multifunctional wall paint and its preparation process. The water emulsion as wall paint features containing nanometer inorganic composite powder in 0.5-5 wt%, and the nanometer inorganic composite powder consists of nanometer zinc oxide 1-5 wt%, other nanometer oxide 1-5 wt% and tourmaline powder 90-98 wt% and is produced through surface treatment. The water emulsion as wall paint is prepared through conventional latex preparing process including mixing, high speed dispersing, regulating and other steps. The water emulsion as wall paint has excellent physical performance, can release negative ion to purify air and kill bacteria to provide people with excellent living environment.

Description

technical field [0001] The invention relates to a multifunctional water emulsion wall paint modified by nano-inorganic composite powder and a preparation method thereof. Background technique [0002] The function of traditional interior wall coatings is to make the wall surfaces of rooms and corridors clean and beautiful, and have a large light reflectivity to make the spaces of rooms and corridors bright. With the development of modern technology and the needs of meeting various purposes, the types and functions of interior wall coatings are constantly increasing. However, due to the widespread use of latex paint for interior walls, adverse reactions such as irritation, fatigue, headaches, and memory loss have occurred in many countries. The test results show that this is related to the pollution of volatile organic compounds in architectural coatings. All countries in the world are currently committed to the research and development of low-VOC latex paint, but in the lat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/02C09D7/12C09D125/14C09D133/00C09D183/00
Inventor 曾汉民王俊卿
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap