Process for copper coating on surface of magnesium and magnesium alloy
A surface chemical and electroless copper plating technology, which is applied in the field of metal surface treatment, can solve problems such as difficult implementation, and achieve the effects of prolonging service life, low cost, and good sterilization and disinfection
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0035] 2. Pickling and alkaline cleaning: Soak magnesium or magnesium alloy in pickling solution for 3 minutes to remove oxides and impurities on the surface until the surface of the magnesium alloy reveals a metallic luster. Take it out, quickly and thoroughly wash the surface of magnesium or magnesium alloy with clean water. Then put the magnesium or magnesium alloy into the alkali washing solution and soak at room temperature, take it out after 3 minutes, clean it with clean water, and put it in a drying oven for drying.
[0036] The pickling solution is dilute nitric acid solution, and its concentration can be:
[0037] 50ml / l, 150ml / l, 100ml / l, 60ml / l or 120ml / l dilute nitric acid solution,
[0038] The alkali washing solution is sodium hydroxide solution, or potassium hydroxide solution, or sodium carbonate solution, or potassium carbonate solution, or sodium phosphate solution, or ammonia solution, or more than one combination thereof, but it must be ensured tha...
Embodiment 2
[0052] 2. Pickling and alkaline cleaning: Soak magnesium or magnesium alloy in pickling solution for 1 minute to remove oxides and impurities on the surface until the surface of the magnesium alloy reveals a metallic luster. Take it out, quickly and thoroughly wash the surface of magnesium or magnesium alloy with clean water. Then put the magnesium or magnesium alloy into the alkali washing solution and soak at room temperature, take it out after 0.5min, clean it with clean water, and put it in a drying oven for drying.
[0053] The pickling solution is a mixed solution of acetic acid and sodium nitrate, and its ratio can be:
[0054] Acetic acid 40ml / l, sodium nitrate 5g / l, the balance is water;
[0055] Acetic acid 60ml / l, sodium nitrate 1g / l, the balance is water;
[0056] Acetic acid 10ml / l, sodium nitrate 10g / l, the balance is water;
[0057] Acetic acid 20ml / l, sodium nitrate 3g / l, the balance is water;
[0058] Acetic acid 50ml / l, sodium nitrate 7g / l, the bal...
Embodiment 3
[0073] 2. Pickling and alkaline cleaning: Soak magnesium or magnesium alloy in pickling solution for 4 minutes to remove oxides and impurities on the surface until the surface of the magnesium alloy reveals a metallic luster. Take it out, quickly and thoroughly wash the surface of magnesium or magnesium alloy with clean water. Then put the magnesium or magnesium alloy into the alkali washing solution and soak at room temperature, take it out after 5 minutes, clean it with clean water, and put it in a drying oven for drying.
[0074] The pickling solution is a mixed solution of chromic anhydride and sodium nitrate, and its ratio can be:
[0075] Chromic anhydride 70g / l, sodium nitrate 8g / l, the balance is water.
[0076] Chromic anhydride 40g / l, sodium nitrate 15g / l, the balance is water.
[0077] Chromic anhydride 120g / l, sodium nitrate 1g / l, the balance is water.
[0078] Chromic anhydride 40g / l, sodium nitrate 6g / l, the balance is water.
[0079] Chromic anhydride...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap