Method for preparing surface layer of earth memorial site in humid environment

A hybrid material, epoxy resin technology, applied in soil conditioning materials, chemical instruments and methods, organic fertilizers, etc., can solve problems such as undiscovered

Inactive Publication Date: 2006-10-04
CHENGDU UNIVERSITY OF TECHNOLOGY
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] After searching, at present, acrylic resin system and organosilicon-modified acrylic resin emulsion are mostly researched at home and abroad, but no patent has been found on the method of using acrylic resin, organosilicon and epoxy resin to prepare the protection material for earthen sites in humid environment Application or Literature Report

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] One of the present invention is based on butyl acrylate, β-hydroxyethyl methacrylate, maleic anhydride, silane coupling agents KH570 and KH550, tetraethyl orthosilicate, epoxy resin E44, and ethyl acetate A method for preparing an acrylate-organic silicon-epoxy resin organic / inorganic hybrid material by radical solution copolymerization and sol-gel method as solvent and azobisisobutyronitrile as initiator. Its technological process is:

[0015] (1) butyl acrylate, β-hydroxyethyl methacrylate, maleic anhydride and silane coupling agent KH570 are used as quaternary comonomers, mixed in a mass ratio of 6.0: 2.5: 1.0: 0.5, and the added mass is Ethyl acetate, which is 3 times the total amount of monomers, is used as a solvent, and under the action of the initiator azobisisobutyronitrile, solution polymerization is carried out at 70° C. to prepare a transparent acrylic resin prepolymer.

[0016] (2) Hydrolyzing tetraethyl orthosilicate and water at room temperature at a mol...

Embodiment 2

[0021] One of the present invention is based on butyl acrylate, β-hydroxyethyl methacrylate, maleic anhydride, silane coupling agents KH570 and KH550, tetraethyl orthosilicate, epoxy resin E44, and ethyl acetate A method for preparing a new type of acrylate-organic silicon-epoxy resin organic / inorganic hybrid material by free radical solution copolymerization and sol-gel method as solvent and azobisisobutyronitrile as initiator. Its technological process is:

[0022] (1) butyl acrylate, β-hydroxyethyl methacrylate, maleic anhydride and silane coupling agent KH570 are used as quaternary comonomers, mixed in a mass ratio of 6.0: 2.5: 1.0: 0.5, and the added mass is Ethyl acetate, which is 3 times the total amount of monomers, is used as a solvent, and under the action of the initiator azobisisobutyronitrile, solution polymerization is carried out at 70° C. to prepare a transparent acrylic resin prepolymer.

[0023] (2) Hydrolyzing tetraethyl orthosilicate and water at room temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The disclosed acrylate-organosilicon -epoxy resin is prepared by butyl acrylate, hydroxyethyl beta-methacrylate, maleic acid, KH570 and KH550, ethyl silicate, and epoxy resin E44; wherein, is applies ethyl acetate as solvent, azo-bis-iso-butyronitrile as initiator, and selects free radical copolymerization and sol-gel method. This organic / inorganic hybridized material has well transparency and thermal stability and fit to site protection.

Description

1. Technical field [0001] The invention relates to butyl acrylate, β-hydroxyethyl methacrylate, maleic anhydride, silane coupling agents KH570 and KH550, tetraethyl orthosilicate, epoxy resin E44 as basic raw materials, and ethyl acetate as solvent 1. Azobisisobutyronitrile is used as an initiator, and an acrylate-organosilicon-epoxy resin organic / inorganic hybrid material is synthesized by free radical solution copolymerization and sol-gel method, which belongs to the field of composite materials. The acrylate-organic silicon-epoxy resin organic / inorganic hybrid material prepared by the invention is suitable for reinforcement and protection of the surface layer of earthen ruins in a humid environment. 2. Technical background [0002] The use of chemical materials to reinforce and protect the surface of earthen sites is an important means to prevent the weathering of earthen sites [Zhou Shuanglin, Yuan Sixun. Preparation of non-aqueous dispersion of organosilicon-modified ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F20/12C08F2/44C08F4/04C08F283/10C08K5/54C08L33/06C09K17/40
Inventor 林金辉万淘刘菁叶巧明汪灵李小洁肖维兵
Owner CHENGDU UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com