Composite silicon brick and preparation method thereof

A technology of silica brick and silica, which is applied in the field of composite silica brick and its preparation, can solve the problems of easy flocculation of lime milk solution, poor effect of mineralizer, and uneven dispersion, and achieve high-efficiency mineralization, high utilization rate, and uniformity The effect of organizational structure

Inactive Publication Date: 2010-06-09
ZHENGZHOU UNIV +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, iron oxide and calcium oxide used in production are added in the form of fine powder and milk of lime respectively. Compared with nano-scale powder, the particle size of the former is not fine enough, and the dispersion in the silica brick is not uniform enough; the latter actually adds It is calcium hydroxide, and its lime milk solution is easy to flocculate and not easy to disperse, so it is less effective as a mineralizer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Example 1: The proportioning of each component is (mass percentage) aggregate (wherein silica particles 52%, waste silica brick particles 8%) 60%, silica powder 35%, nano-calcium carbonate powder 2.0%, nano-iron oxide 0.5%, nano silicon dioxide 1.5%, lime 0.5%, fluorite powder 0.5%, sulfurous acid pulp waste liquid 2% (additional).

Embodiment 2

[0039] Embodiment 2: The proportioning of each component is (mass percentage) aggregate (wherein silica particle 55%, waste silica brick particle 10%) 65%, silica powder 28.5%, nano-calcium carbonate powder 1.0%, nano-iron oxide 1.0 %, nano silicon dioxide 2.0%, lime 1.5%, fluorite powder 1.0%, sulfurous acid pulp waste liquid 1.5% (additional).

Embodiment 3

[0041] Embodiment 3: the proportioning of each component is (mass percentage) aggregate (wherein silica particle 55%, waste silica brick particle 15%) 70%, silica powder 24.5%, nano-calcium carbonate powder 0.8%, nano-iron oxide 1.5% %, nano silicon dioxide 1.2%, lime 1.0%, fluorite powder 0.5%, sulfurous acid pulp waste liquid 1.0% (additional).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a nano-sized composite silica brick and a production method thereof. The invention is characterized in that: raw materials and binder of the silica brick are as follows: silica granules and fine powders, waste silica brick granules, calcium carbonate nanoparticles, iron oxide nanoparticles, silicon dioxide nanoparticles, fluorite powders, lime and sulfite pulp wastes. Theproduction method is based on the existing production process of the silica brick, and introduces compound nanopowders in optimal proportions in the production process of the silica brick after high-efficiency dispersion, to produce nano-sized composite silica bricks. With the addition of nanopowders, the performance of silica brick is significantly improved, and manifested as follows: 1) the particle size fraction is more reasonable, the accumulation is compact and the texture is uniform; 2) the slurry has good plasticity and moldability and the production efficiency is improved; 3) the burning temperature is decreased to 20 DEG C, thus realizing energy conservation and discharge reduction; 4) the tridymite is superior in crystallization conversion and has low content of quartz residues;5) the number of closed pores is increased, the number of opened pores are reduced, the porosity is reduced, and the strength and refractoriness under load are increased; and 6) the final product hasgood appearance, smooth end surface and good bonding property, and the rate of qualified products is increased.

Description

technical field [0001] The invention belongs to the technical field of inorganic non-metallic materials (refractory materials), and specifically relates to a composite silica brick and a preparation method thereof. The various nano powders used refer to nano calcium carbonate, nano iron oxide and nano silicon dioxide. Background technique [0002] Silica brick is a kind of SiO 2 The traditional refractory products as the main component are acidic refractory materials with high temperature volume stability, good thermal conductivity, excellent resistance to acid slag erosion, especially high softening temperature under load (only 30-50°C difference from refractoriness), etc. features. The main raw material for making silica bricks is silica (quartzite). Our country began to produce general silica bricks in the 1930s, and began to mass produce silica bricks for steelmaking open hearth furnaces and coke ovens in the early 1950s. For half a century, with the elimination of ste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B32/00C04B14/04C04B18/16
CPCC04B28/02Y02W30/91C04B14/04C04B14/28C04B18/167C04B18/243C04B20/008C04B22/06C04B22/064C04B22/126
Inventor 叶方保冯振德李志刚韩根长刘新红
Owner ZHENGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products