Disposable degradable plant fibre molding dishware and making method thereof

A plant fiber and production method technology, applied in the directions of table utensils, home utensils, manufacturing tools, etc., can solve the problems of high production cost, products are not easily degraded, environmental pollution, etc., and achieve low production cost, good strength and stiffness, Good thermal insulation performance

Inactive Publication Date: 2008-11-12
刘志军 +2
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, because the glue contains formaldehyde, the production process and products pollute the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1, the present embodiment is by 100 parts of rice husks, 40 parts of adhesives, 3 parts of zinc stearate mold release agents and 1 part of waterproofing agent paraffin by 100 parts of moisture content no more than 5%. 100 parts of water, 4.0 parts of thiourea, 30.0 parts of soybean powder, 5.0 parts of polyvinyl acetate emulsion, 12.0 parts of PVA, 3.5 parts of 50% zinc oxide, 4.0 parts of starch phosphate, 0.4 parts of n-butanol, 4.0 parts of flour, 0.1 40.0 parts of sodium benzoate and 40.0 parts of urea were put into the glue-making reactor and mixed to make an adhesive. Pulverize the above-mentioned plant fiber into 100 meshes with a pulverizer, and then mix it with the adhesive, mold release agent and water repellent in a high-mixer according to the stated formula quantity with a quantitative feeder. Group, no glue block. The mixed materials are weighed and quantified according to the amount of materials required for the tableware, and then put into the...

Embodiment 2

[0013] Embodiment 2, this embodiment is made of 100 parts of rice husks, wheat husks, bran and nut shells with a moisture content of no more than 5%, one of two kinds of mixtures or multiple mixtures, 30 parts of adhesives, 5 parts of Zinc stearate release agent and 1.5 parts water repellant paraffin. 100 parts of water, 5.0 parts of thiourea, 40.0 parts of soybean powder, 8.0 parts of polyvinyl acetate emulsion, 15.0 parts of PVA, 5.0 parts of 50% zinc oxide, 6.0 parts of starch phosphate, 0.5 parts of n-butanol, 6.0 parts of flour, 0.2 42.0 parts of sodium benzoate and 42.0 parts of urea were put into a glue-making reactor and mixed to make an adhesive. Pulverize the above-mentioned plant fibers into 80 meshes with a pulverizer, and then mix them with the adhesive, mold release agent and water repellent in a high-mixer according to the stated formula quantity with a quantitative feeder. Group, no glue block. The mixed materials are weighed and quantified according to the a...

Embodiment 3

[0014] Embodiment 3, the present embodiment is made of 100 parts of wood flour with a moisture content of no more than 5%, 35 parts of adhesive, 4 parts of zinc stearate release agent and 0.5 part of waterproofing agent paraffin. The plant fiber is wheat husk. 100 parts of water, 4.5 parts of thiourea, 35.0 parts of soybean flour, 6.0 parts of polyvinyl acetate emulsion, 13.0 parts of PVA, 3.0 parts of zinc oxide, 5.0 parts of starch phosphate, 0.45 parts of n-butanol, 5.0 parts of flour, 0.15 parts of benzene Sodium formate and 35.0 urea are put into the glue making reaction kettle and mixed to make an adhesive. Grind the above-mentioned plant fibers into 120 meshes with a pulverizer, and then mix them with the adhesive, release agent and water repellent in a high-mixer according to the stated formula quantity with a quantitative feeder. Group, no glue block. The mixed materials are weighed and quantified, put into a molding machine and hot-pressed to form disposable degrad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses disposable dissoluble plant fiber pressed tableware and the preparation method thereof, the tableware are made from the following materials : 100 portions of plant fiber with a water content of less than five percent, 30 to 40 portions of adhesive, 3 to 5 portions of mould release agent and 0.5 to 1.5 portions of waterproof agent, wherein the plant fiver comprises one or a plurality kinds of crop stalks, rice hulls, wheat hulls, bran coat and nut shell; the adhesive is natural soybean glue with a solidity of between forty and fifty percent. The plant fiber molded tableware is non-toxic to health, can be used as animal food or combustion-supporting material after being recycled and ground, and can be decomposed naturally, if not being recycled, to be organic fertilizer in nature to reach the purpose of no rubbish, no pollution, from nature and back to nature; the whole preparation process has no poison gas and waste fluid pollution, the products are resistant in cooling and water, good in thermal insulation property, strength and stiffness, has low production cost, simple technology and stable product quality.

Description

1. Technical field [0001] The invention belongs to a plant fiber molded tableware and a manufacturing method thereof. 2. Background technology [0002] Disposable plant fiber molded tableware is made of crushed plant fiber raw materials, mixed with adhesive, and then molded at high temperature. The raw materials of plant fiber are mainly crop straw, rice bran, wood flour, etc.; the adhesive mainly uses formaldehyde series urea-formaldehyde resin, phenolic resin or melamine resin adhesive. The raw material of the plant fiber is crushed and blended with an adhesive, and an appropriate amount of filler is added to be molded into a product. In the prior art, because the glue contains formaldehyde, the production process and products pollute the environment to varying degrees, and the production cost is high, and the products are not easy to degrade. 3. Contents of the invention [0003] The present invention solves the above-mentioned problems in the prior art, and provides ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L97/02B29C33/60B27N1/00B27N1/02A47G19/00
Inventor 刘志军刘伟刘智
Owner 刘志军
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap