Multifunctional composite sheet material and process for making same

A manufacturing process and multi-functional technology, applied in the direction of flat products, other household appliances, synthetic resin layered products, etc., can solve problems such as production and living troubles, freezing of water flow in pipes, bursting pipes, etc., and prolong the service life , Prevent water flow from freezing and freezing, good thermal radiation performance

Inactive Publication Date: 2013-01-02
成都科航建材科技发展集团有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Furthermore, in the cold and long winter, the water supply and drainage pipes widely used in industrial or civil buildings are attacked by the severe cold, and the water flow in the pipes often freezes, freezes, bursts, etc., which brings troubles to people's production and life; at the same time , people living in modern high-rise buildings, the noise of the downpipe water flow generated when they use the kitchen and bathroom to drain water in the morning, middle and evening makes people living in the middle and low floors complain and suffer a lot, and it cannot make people live in a relatively In the quiet and overflowing home living environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional composite sheet material and process for making same
  • Multifunctional composite sheet material and process for making same
  • Multifunctional composite sheet material and process for making same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] The manufacturing process of the composite multifunctional sheet, the steps are as follows,

[0064] ①. Raw material preparation: prepare raw materials according to the following raw materials and parts by weight, wherein,

[0065]

[0066] Stearic acid 5

[0067] Zinc stearate 5

[0068] Calcium stearate 5

[0069] Azodicarbonamide 3

[0070] Antioxidant 264 3;

[0071] ②. Thermal mixing: Put the polyvinyl chloride resin, powdered nitrile rubber, barium sulfate, carbon black, and diatomaceous earth among the above raw materials into a high-speed heating mixer with a volume of 300L for high-speed mixing, so that the temperature reaches 60±5 ℃, then add stearic acid, zinc stearate, calcium stearate, antioxidant 264 and continue mixing at high speed, and when the temperature reaches 70℃, slowly add dioctyl phthalate and continue mixing at high speed to make the temperature Reach 105°C to obtain a thermally mixed primary material;

[0072] ③. Cold mixing: Put the ...

Embodiment 2

[0078] The manufacturing process of the composite multifunctional sheet, the steps are as follows,

[0079] ①. Raw material preparation: prepare raw materials according to the following raw materials and parts by weight, wherein,

[0080] PVC resin 80

[0081] Powdered Nitrile Rubber 20

[0082] Barium sulfate 40

[0083] carbon black 3

[0084] Diatomaceous earth 40

[0085] Dioctyl phthalate 30

[0086] stearic acid 2

[0087] Zinc stearate 2

[0088] Calcium Stearate 2

[0089] Azodicarbonamide 1

[0090] Antioxidant 264 0.5;

[0091] ②. Thermal mixing: Put the polyvinyl chloride resin, powdered nitrile rubber, barium sulfate, carbon black, and diatomaceous earth among the above raw materials into a high-speed heating mixer with a volume of 300L for high-speed mixing, so that the temperature reaches 60±5 ℃, then add stearic acid, zinc stearate, calcium stearate, antioxidant 264 and continue mixing at high speed, and when the temperature reaches 70℃, slowly add dio...

Embodiment 3

[0098] The manufacturing process of the composite multifunctional sheet, the steps are as follows,

[0099] ①. Raw material preparation: prepare raw materials according to the following raw materials and parts by weight, wherein,

[0100] PVC resin 85

[0101] Powdered Nitrile Rubber 15

[0102] Barium sulfate 50

[0103] carbon black 4

[0104] Diatomaceous earth 50

[0105] Dioctyl phthalate 35

[0106] stearic acid 3

[0107] Zinc stearate 3

[0108] Calcium Stearate 3

[0109] Azodicarbonamide 2

[0110] Antioxidant 264 1.5;

[0111] ②. Thermal mixing: Put the polyvinyl chloride resin, powdered nitrile rubber, barium sulfate, carbon black, and diatomaceous earth among the above raw materials into a high-speed heating mixer with a volume of 300L for high-speed mixing, so that the temperature reaches 60±5 ℃, then add stearic acid, zinc stearate, calcium stearate, antioxidant 264 and continue mixing at high speed, and when the temperature reaches 70℃, slowly add dio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a multifunctional composite sheet material and the production process thereof. The production process comprises the following steps: material preparation, hot mixing, cold mixing, extrusion granulation, extrusion output, lamination, aluminum foil attachment and finishing. The sheet material consists of four layers: aluminum foil, a substrate, fiber glass and polyurethane foam. The production process has the advantages of simple process, low cost and easy construction and maintenance. The product has sound-insulating and heat-insulating effects and good resistance to light radiation and thermal radiation. The multifunctional composite sheet material allows the building to meet the requirements for sound insulation, heat insulation, light radiation resistance and thermal radiation resistance. The multifunctional composite sheet material reflects ultraviolet ray in sunlight, ensures normal temperature difference and normal flow and running of oil and gas in a tube, slows down the light ageing and thermal ageing processes of a pipe network, and prolongs the service life of the equipment. Additionally, the multifunctional composite sheet material can efficiently prevent water-freezing and explosion of a pipe and substantially eliminate the noise during water drainage. The product provides good sound-insulating and heat-insulating effects and good resistanceto light radiation and thermal radiation in refrigerated warehouse in logistical refrigerators and special vehicles and ships.

Description

technical field [0001] The present invention relates to a composite sheet and its production process. More specifically, it relates to a composite sheet suitable for the surface of building facilities, industrial / civil pipeline wrapping and the inner surface of logistics freezer, etc., which can play the role of sound insulation, heat preservation, heat insulation, Composite multifunctional sheet material resistant to light radiation and heat radiation and its manufacturing process. Background technique [0002] At present, with the development of social economy, science and technology and the gradual scarcity of available resources, all countries are taking the development of high-tech products that are environmentally friendly and energy-saving as the leading direction. [0003] First of all, building facilities such as various types of auditoriums, theaters, concert halls, conference halls, national defense and military facilities, and scientific research institutions all...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B37/02B32B37/12B32B15/08B32B27/12B32B27/18B32B17/04B32B3/30B32B5/18B32B7/12B29B7/00B29B9/00B29B11/10B29C47/92B29C47/82B29L7/00B29K309/00B29K27/06B29C48/04B29C48/07B29C48/12B29C48/92
CPCB29C48/92B29C2948/92704B29C48/04B29C48/07B29C48/12B29C48/9185B29C2948/9259B29C2948/92885B29C2948/92895
Inventor 何霖
Owner 成都科航建材科技发展集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com