Method for producing wood plastic composite material using plant straw and waste plastic and material thereof

A technology of wood-plastic composite material and plant straw, which is applied in the field of making wood-plastic composite material and its materials by using plant straw and waste plastics, which can solve the problems of difficulty in utilization and separation of sundries, and achieve less fungal infection and simple processing technology Effect

Inactive Publication Date: 2012-12-26
石河子市森力新材料科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At the same time, a large amount of residual film is produced in the process of mulch film planting. At present, after recycling, plastic processing enterprises reuse it as recycled materials, but it is difficult to use it due to the difficulty of separating a large number of sundries mixed in it.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (1) The cotton stalks recovered and dried until the moisture content is lower than 15% are pulverized to pass through a 250 μm sieve, and dried until the moisture content is ≤3%, so as to obtain plant fiber powder with a particle size below 250 μm for use;

[0035] (2) The waste film is crushed to pieces of ≤3cm, washed until the sediment content is ≤1%, dehydrated and dried until the water content is ≤5%, first aggregated at a temperature of 80°C and then sent to a granulator for granulation. Use a sieve to take resin particles with a particle size of ≤3 mm for use;

[0036] (3), get DBP, benzyl maleic anhydride, polyester wax by weight and mix for subsequent use in a ratio of 25:25:25;

[0037] (4) Take 60% of the above-mentioned plant fiber powder, 35% of resin granules, and 5% of compound additives by weight, fully mix them evenly, and extrude them with a twin-screw extruder. The temperature of the barrel is controlled at 175 ° C, and the temperature of the confluen...

Embodiment 2

[0040] (1) Cotton stalks recovered and dried to a moisture content of less than 20% are pulverized and passed through a 500 μm sieve to obtain plant fiber powder with a particle size of less than 500 μm, which is dried until the moisture content is ≤2% for later use;

[0041] (2) Crush the waste film to ≤5cm fragments, wash until the sediment content is ≤1%, dehydrate and dry until the water content is ≤2%, first aggregate at 88°C for standby, and crush the waste drip irrigation tape to ≤1cm The fragments are cleaned until the sediment content is ≤1%, dehydrated and dried until the water content is ≤2%, and sent to the granulator together with the waste film material after the above-mentioned agglomeration to granulate, and the resin particles with a particle size of ≤3mm are sieved for use ;

[0042] (3), take DBP, benzyl maleic anhydride, polyethylene wax by weight and mix in a ratio of 15:25:35, and add each 5 parts of triphenyl phosphate and TBS while mixing for subsequent...

Embodiment 3

[0046] (1) The cotton stalks recovered and dried until the moisture content is lower than 20% are pulverized and passed through an 840 μm sieve, and dried until the moisture content is ≤3%, so as to obtain plant fiber powder with a particle size below 800 μm for use;

[0047] (2) Crush the mixed waste plastics such as mineral water bottles, waste drip irrigation belts, etc. into fragments of ≤2cm, wash until the sediment content is ≤1%, dehydrate and dry until the water content is ≤5%, and send it into granulation Machine granulation, pass through a sieve to take resin particles with a particle size of ≤2mm for use;

[0048] (3), take DBP, benzyl maleic anhydride, and paraffin by weight and mix in a ratio of 20:35:25, and add UV-531, 5 parts and 10 parts of hexabromobenzene for subsequent use;

[0049](4) Get above-mentioned plant fiber powder 55%, resin granule 45%, composite additive 5% by weight and fully mix evenly, adopt twin-screw extruder extrusion molding, the barrel t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for manufacturing wood plastic composite material by using plant straw and waste plastics and materials thereof. Polyester and plant wood fiber materials such as sawdust, bamboo powder, rice hull, straw, and the like, are mixed according to certain ratios, a tailor-made additive is added, and after the processes of high temperature, extrusion, molding, and the like, the composite building profile is manufactured. The wood plastic material can replace wood, plastics, and the like, and is mainly used in the industries of packaging, building materials, furniture, logistics, and the like. The invention has simple processing technology, and the product has good processing properties and strength property, good water proof and corrosion resistant property and adjustability, the materials have wide sources and applications, especially the plant straw and waste plastics which contain waste mulch film and are recovered under the northern planting pattern of mulch film can be used for production, thus using the waste and restraining the current pollution of the mulch film planting to the lands effectively.

Description

Technical field: [0001] The invention relates to a method of using plant straws to manufacture wood-plastic composite materials and the materials obtained by the method, in particular to a method mainly using plant straws containing old plastic films and waste plastic films recovered from the northern plastic film planting mode. A method for a wood-plastic composite material and a material obtained by the method. Background technique: [0002] At present, a large amount of straw produced by agricultural production is first crushed and returned to the field as fertilizer, but the long-term use of this treatment method will increase the possibility of crop diseases, and its utilization value is also low; second, it is used as fuel. The value is greatly reduced, and some are treated as waste, such as incineration, which not only causes waste of resources, but also pollutes the environment. [0003] Some people use it to make compressed fiberboard, and due to technological reas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B27N3/28B27N5/00B27N1/00B27N1/02B29C47/92C08L97/02C08K5/09C08L101/00C08L91/06B29K105/06B29C48/92
CPCB29C48/04
Inventor 成玉彪李建新黄立新朱玉
Owner 石河子市森力新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap