Method for modifying natural zeolite powder
A natural zeolite and zeolite powder technology, applied in chemical instruments and methods, silicates, inorganic chemistry, etc., can solve the problems of unsatisfactory removal of ammonia nitrogen, unsuitable drinking water treatment, and reduced efficiency of ammonia removal, etc., to save preparation Time and energy consumption, improved adsorption performance, good modification effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0028] Example 1 Modified zeolite powder
[0029] The specific preparation steps of the modified zeolite powder of this embodiment are as follows:
[0030] (1) Pretreatment: Take natural zeolite powder, wash it with water several times to remove soluble impurities, and dry it at 104°C for 4.0 hours;
[0031] (2) Modification treatment: According to the mass ratio of zeolite powder: sodium chloride = 1:1, the natural zeolite powder and sodium chloride after the pretreatment are mixed and put into the alkali-resistant reactor, and then added to the reactor Add 1.0mol / L sodium hydroxide solution, so that the sodium hydroxide solution is immersed in natural zeolite powder and sodium chloride, then after 30 hours, rinse with water to neutrality, and then dry at 104℃ for another 5.0 hours to make modified Zeolite powder.
Example Embodiment
[0032] Example 2 Modified zeolite powder
[0033] The specific preparation steps of the modified zeolite powder of this embodiment are as follows:
[0034] (1) Pretreatment: Take natural zeolite powder, wash it several times with water to remove soluble impurities, and dry it at 50°C for 2.0 hours;
[0035] (2) Modification treatment: According to the mass ratio of zeolite powder: sodium chloride=50:1, the natural zeolite powder and sodium chloride after the pretreatment are mixed and put into the alkali-resistant reactor, and then into the reactor Add 5mol / L sodium hydroxide solution so that the sodium hydroxide solution is immersed in natural zeolite powder and sodium chloride, then after 5 hours, rinse with water to neutrality, and then dry at 50℃ for another 1.0 hour to make modified zeolite powder.
Example Embodiment
[0036] Example 3 Adsorption performance of modified zeolite powder
[0037] In this example, the modified zeolite powder prepared in Example 1 was selected to compare the adsorption performance with other zeolite powder prepared by hydrogen type modification treatment, alkaline modification treatment, sodium type modification treatment and double modification treatment.
[0038] This embodiment is divided into the following six experimental groups:
[0039] 1. Natural zeolite: commercially available natural zeolite powder produced in Xinyang, Henan, with a particle size range of 50-800 mesh;
[0040] 2. Modified zeolite: prepared in Example 1;
[0041]3. Hydrogen zeolite: add the above natural zeolite to 1.0mol / L hydrochloric acid solution and shake for 12 hours, rinse with water until the pH value is neutral, and dry at 104°C for 5.0 hours to prepare hydrogen zeolite;
[0042] 4. Alkaline zeolite: add the above natural zeolite powder to 1.0mol / L sodium hydroxide solution and shak...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction