Modified polyurethane asphalt corrosion-resistant coating
An anti-corrosion coating and polyurethane technology, applied in polyurea/polyurethane coatings, anti-corrosion coatings, asphalt coatings, etc., can solve the problems of time-consuming, labor-intensive, short-lived moisture-permeable coatings, and high labor intensity. UV resistance, long life effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0015] Example 1
[0016] 1) Preparation of component A: In parts by weight, take 29 parts of PM-200 polymethyl polyphenyl isocyanate, 9.5 parts of IPDI, 7 parts of acrylic resin BS962, 8 parts of polyether 3031K; 2.5 parts of polyether 450, 6.5 parts of dioctyl ester, 5.5 parts of epoxy resin 6101, 0.0015 parts of phosphoric acid, 33.5 parts of solvent S1000 # , In the reactor, react at 40-42°C for half an hour, then heat up to 80-82°C, keep it warm for two hours, and cool down
[0017] 2) Preparation of component B: In parts by weight, take 26 parts petroleum pitch, 33 parts coal tar pitch, 10.5 parts cyclohexanone, 10 parts toluene, 8 parts solvent S1000 # , 5.5 parts of epoxy resin 618, kept in the reactor at 135~140℃ for two hours, and cooled to room temperature; then add 13 parts of aluminum tripolyphosphate, 6.5 parts of strontium chromate, 13 parts of mica under 1250 mesh Powder, 11 parts of glass phosphor flakes under a 325 mesh sieve, ground and dispersed.
[0018] 3) Blen...
Example Embodiment
[0019] Example 2
[0020] 1) Preparation of component A: In parts by weight, take 28 parts of PM-200 polymethyl polyphenyl isocyanate, 9 parts of IPDI, 6 parts of acrylic resin BS962, 7 parts of polyether 3031K; 2 parts of polyether 450, 6 parts of dioctyl ester, 5 parts of epoxy resin 6101, 0.001 parts of phosphoric acid, 31 parts of industrial xylene, in the reactor, react at 40~42℃ for half an hour, then heat up to 80~82℃, keep warm for two hours, and cool down ;
[0021] 2) Preparation of component B: In parts by weight, take 25 parts of petroleum pitch, 32 parts of coal tar pitch, 10 parts of cyclohexanone, 9 parts of toluene, 7 parts of industrial xylene, 5 parts of epoxy resin 618, in the reaction In the kettle, keep the temperature at 135~140℃ for two hours, then cool to room temperature; then add 10 parts of aluminum tripolyphosphate, 5 parts of strontium chromate, 10 parts of mica powder under 1250 mesh sieve, 10 parts of glass under 325 mesh sieve Phosphorus flakes, gr...
Example Embodiment
[0023] Example 3
[0024] 1) Preparation of component A: In parts by weight, take 30 parts PM-200 polymethyl polyphenyl isocyanate, 10 parts IPDI, 8 parts acrylic resin BS962, 9 parts polyether 3031K, 3 parts polyether 450, 7 parts dioctyl ester, 6 parts epoxy resin 6101, 0.002 parts phosphoric acid, 36 parts solvent S1000 # , In the reactor, react at 40-42°C for half an hour, then heat up to 80-82°C, keep it warm for two hours, and cool down;
[0025] 2) Preparation of component B: In parts by weight, take 27 parts of petroleum pitch, 34 parts of coal tar pitch, 11 parts of cyclohexanone, 10.5 parts of toluene, 9 parts of solvent S1000#, 6 parts of epoxy resin 618, in the reaction In the kettle, keep the temperature at 135~140℃ for two hours, then cool down to room temperature; then add 15 parts of aluminum tripolyphosphate, 8 parts of strontium chromate, 15 parts of mica powder under 1250 mesh sieve, 12 parts of glass under 325 mesh sieve Phosphorus flakes, grinding and dispersi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap