Sintered light environmentally-friendly brick produced from ceramic waste residues and silt and manufacturing method thereof
A technology of ceramic waste slag and environmentally friendly bricks, which is applied in the field of sintered lightweight environmentally friendly bricks. The sintered lightweight environmentally friendly bricks can solve problems such as environmental hazards, secondary pollution, polluted soil and groundwater resources, and achieve energy saving and elimination. The effect of secondary pollution
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0038] The mixture of damaged blanks, unfired and glazed damaged waste products, calcined and glazed semi-finished products, damaged and cracked waste products, waste building ceramics, and waste sanitary ceramics residues generated during the production of ceramics is crushed, sorted, and magnetically separated. After removing the scrap metal, it is then sorted by wheel grinding to make powder with a particle size of less than 2mm;
[0039] A kind of volcanic ash-like mixed material formed by burning coal at high temperature to generate electricity is a kind of solid waste discharged from coal-fired power plants, with a fineness of 45 microns of fly ash,
[0040] A kind of solid waste that is discharged after domestic waste is incinerated for power generation, after sorting, crushing, and magnetic separation to remove scrap metal, it is made into a powder with a particle size of less than 2mm;
[0041] A kind of solid waste produced when cleaning rivers, canals, and lakes pollu...
Embodiment 2
[0045] Get the ceramic waste slag powder 40kg of embodiment 1, fly ash 25kg, garbage ash powder 15kg, sludge powder 25kg, marble waste slag powder 20, particle diameter is calcium sulfate 6kg, boric acid 2kg, sodium borate 1kg of 0.2mm , Ferrous Sulfate 2kg, Magnesium Sulfate 3kg, Li macromolecule heavy metal collector 0.2kg and water 18kg, above-mentioned raw material is mixed and adopts twin-shaft stirrer to stir and be wet shape, utilize vacuum extruder to extrude and cut through billet cutting machine, Under the pressure of 23Mpa, the ceramic waste slag silt light-weight environmental protection brick adobe is made, and after natural drying for 7 days, the formed and naturally dried ceramic waste slag silt light-weight environmental protection brick adobe is sent to the wheel kiln for roasting by a battery car. After roasting, it is made Ceramic waste slag sintered lightweight environmental protection brick products. After testing, the average compressive strength is: 11Mp...
Embodiment 3
[0047] Get embodiment 1 ceramic waste slag powder 45kg, fly ash 35kg, garbage ash powder 20kg, silt powder 30kg, marble waste slag powder 25kg, particle diameter is the calcium sulfate 8kg of-0.2mm, boric acid 3kg, sodium borate 2kg , Ferrous Sulfate 3kg, Magnesium Sulfate 6kg, Li macromolecule heavy metal collector 0.4kg and water 25kg, the above-mentioned raw materials are mixed and stirred to be wet shape and extruded with mechanical vibration, and made ceramic waste slag silt light under the pressure of 30Mpa After 7 days of natural drying, the light hollow blocks of ceramic waste slag and silt that have been formed and dried naturally are sent to the wheel kiln for roasting by a battery car, and then made into ceramic waste slag silt sintered light hollow blocks product. After testing, the average compressive strength is: 7.5Mpa, the minimum value of a single block is: 6.9Mpa, the dry apparent density is: 1002kg / m3, and the drying shrinkage rate is: 0.023%, all of which a...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com