Polypropylene fiber containing composite nitrogen phosphorus flame retardant used for periwig and its production method

A polypropylene fiber, nitrogen and phosphorus flame retardant technology, applied in the field of chemistry, can solve the problems of brominated flame retardants, such as adverse effects on human health, prohibition, etc., to achieve good gloss, smooth hand feel, and environmental friendliness.

Active Publication Date: 2011-09-28
HENAN REBECCA HAIR PRODS TNC
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Patent 200910235458.4, low-temperature flame-retardant polypropylene fiber for wigs discloses a polypropylene with brominated flame retardants, antimony-based flame retardants and nanomaterials, but many studies have proved that brominated flame retardants are harmful to human health impact, already banned in the EU and US

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Add 100 parts of fiber-grade polypropylene S2025 (Secco Petrochemical), 1.5 parts of fatty acid calcium zinc composite stabilizer (Mitsubishi Chemical Co., Ltd.) and 2 parts of cooling masterbatch (Sinopec Yanshan Petrochemical Company) into the high-speed shear mixer, start the machine Set the mixing speed at 300r / min~500r / min, stir for 5min~15min, make the temperature of the material reach 110℃~130℃, then add 15 parts of ammonium polyphosphate (Shanghai Mileper Chemical Material Technology Co., Ltd.), 15 parts of pentaerythritol (Shanghai Meilaipo Chemical Material Technology Co., Ltd.), 12 parts of melamine (Shanghai Meilaipo Chemical Material Technology Co., Ltd.), 1.5 parts of silane coupling agent (Nanjing Shuguang Chemical Group Co., Ltd.) immediately continue to stir and mix the speed to 500r / min~1200r / min, stirring for 5min~15min, so that the material temperature reaches 130℃~160℃. Then add 4 parts of carbon black masterbatch (carbon black content 30%, Clarian...

Embodiment 2

[0045]Add 100 parts of fiber-grade polypropylene S2025 (Secco Petrochemical), 1.8 parts of butyltin laurate (Mitsubishi Chemical Co., Ltd.) and 2 parts of cooling masterbatch (Sinopec Yanshan Petrochemical Company) into the high-speed shear mixer, start the machine and set the mixing speed At 300r / min~500r / min, stir for 5min~15min, make the temperature of the material reach 110℃~130℃, then add 20 parts of ammonium polyphosphate (Shanghai Meilaipo Chemical Material Technology Co., Ltd.), 15 parts of dipentaerythritol (Sinopharm Group Chemical Reagent Co., Ltd.), 12 parts of melamine (Shanghai Mileper Chemical Material Technology Co., Ltd.) and 2.0 parts of titanate coupling agent (Nanjing Shuguang Chemical Group Co., Ltd.) immediately continue to stir and mix the mixing speed to 500r / min~ 1200r / min, stirring for 5min to 15min, to make the temperature of the material reach 130°C to 160°C; add 4 parts of carbon black masterbatch (30% carbon black content, Clariant), keep the speed...

Embodiment 3

[0047] Add 60 parts of fiber-grade polypropylene S2025 (Secco Petrochemical) and 1.5 parts of butyltin laurate (Mitsubishi Chemical Co., Ltd.) into the high-speed shear mixer, set the mixing speed at 300r / min~500r / min when starting up, and stir for 5min~ 15min, make the material temperature reach 110 ℃ ~ 130 ℃, then add 18 parts of ammonium polyphosphate (Shanghai Meilaipo Chemical Material Technology Co., Ltd.), 18 parts of dipentaerythritol (Sinopharm Chemical Reagent Co., Ltd.), 15 parts of melamine (Shanghai Meilaipo Chemical Material Technology Co., Ltd.) and 2.0 parts of titanate coupling agent (Nanjing Shuguang Chemical Group Co., Ltd.), immediately increase the mixing speed to 500r / min~1200r / min, and stir for 5min~15min to make the material The temperature reaches 130°C-160°C, and after discharge, it is fed into a twin-screw extruder to extrude and pelletize at 220-240°C. The slices are dried to a water content below 100ppm to make polypropylene flame retardant masterb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention belongs to the chemical technology field, particularly relates to polypropylene fiber containing a composite nitrogen phosphorus flame retardant used for periwig and its production method. The invention is characterized in that the components comprise by mass: 100 parts of polypropylene, 5 to 20 parts of dehydrating agent, 5 to 20 parts of charring agent, 5 to 20 parts of foaming agent, 1 to 5 parts of coupling agent, 1.5 to 2.5 parts of heat stabilizer and 1.0 to 2.0 parts of polypropylene heat degradation masterbatch. Polypropylene, the heat stabilizer and polypropylene heat degradation masterbatch are added into a high-shear mixer in proportion, the dehydrating agent, the charring agent, the foaming agent and the coupling agent are orderly added for improving the continuously stirring mixing rotating speed, color masterbatch is added and the rotating speed is kept, the material is discharged after continuously stirring, the discharged material is extruded by adouble screw extruder, melt spinning is performed after drying, the extruded nascent fiber is cooled and reeled by crosswind and a filament is obtained after drawing-off. The present invention has the advantages of non-toxicity, smoke suppression, friendly environment and the like.

Description

[technical field] [0001] The invention relates to the field of chemical technology, in particular to a polypropylene fiber for wigs compounded with nitrogen and phosphorus flame retardants and a production method thereof. [Background technique] [0002] At present, people always want to change their hairstyles but are worried that their hair will be damaged. Long-term blow-drying, dyeing, and perm will damage the hair quality. In order to have a fashionable shape at any time, wigs are becoming more and more popular. [0003] Patent 200910235458.4, low-temperature flame-retardant polypropylene fiber for wigs discloses a polypropylene with brominated flame retardants, antimony-based flame retardants and nanomaterials, but many studies have proved that brominated flame retardants are harmful to human health impact, has been banned in the European Union and the United States. Brominated compounds are bioaccumulative and destructive to the human nervous system, immune system and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/46D01F1/07D01F1/10A41G3/00D01D1/04D01D5/08D01D5/088D01D5/12
Inventor 李全民王依民吴学丙郭楠郭林锋刘术佳
Owner HENAN REBECCA HAIR PRODS TNC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com