Cement clinker and preparation method thereof

A technology for cement clinker and raw materials, applied in the direction of cement production, etc., can solve the problems affecting the economic benefits of extracting alumina from fly ash, cannot be applied, and secondary environmental pollution, and achieves saving energy consumption and reducing energy consumption. , The effect of fine grinding and low cost

Inactive Publication Date: 2012-02-08
INNER MONGOLIA DATANG INT RENEWABLE RESOURCES DEV
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nevertheless, the soda lime sintering method will produce 2-2.5 tons of aluminum extraction residue per ton of alumina. If such a large amount of aluminum extraction residue cannot be used, it will not only occupy a large amount of land, but also cause secondary pollution to the environment and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cement clinker and preparation method thereof
  • Cement clinker and preparation method thereof
  • Cement clinker and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0033] Example 1

[0034] figure 1 The process flow chart of the method for preparing cement clinker provided in the first embodiment of the present invention.

[0035] The main component of the residue obtained after the alumina is extracted by the fly ash soda lime sintering method is the calcium silicate, and the above-mentioned residue is processed by the desalination process to obtain the fly ash aluminum extraction residue. The steps of the dealkalization process are as follows: (1) The aluminum extraction residue is stirred with water to prepare an aluminum extraction residue slurry; (2) while stirring, calcium carbide slag is slowly added to the aluminum extraction residue slurry to carry out the dealkalization reaction; (3) ) Filtering and washing the aluminum extraction residue slurry after the dealkalization reaction. The alkali content of fly ash aluminum residue is below 0.6%, and its main chemical components are CaO and SiO 2 , The main phase of fly ash aluminum res...

Example Embodiment

[0046] Example 2

[0047] The difference from the embodiment is that the raw materials (raw meal) used in this embodiment include: 80 parts by weight of fly ash aluminum residue, 18 parts by weight of limestone, 2 parts by weight of iron ore, mixed and homogenized, and the homogenized raw material Take a small amount of the material for particle size test, pass a 100-mesh sieve, the sieve residue is 7.2%, which meets the raw material particle size requirements. The homogenized raw meal is sent to a rotary kiln for high-temperature calcination at a calcination temperature of 1360°C, and after cooling, cement clinker S-2 is prepared.

[0048] Fly ash aluminum residue includes the following components in weight ratio: CaO: 56.71, SiO 2 : 25.36, Al 2 O 3 : 4.62, Fe 2 O 3 : 2.48, MgO: 2.03, Na 2 O+0.66K 2 O: 0.52, loss on ignition: 8.28.

[0049] The chemical composition and rate value of the cement clinker S-2 prepared in this embodiment are shown in Table 3, and the physical and mechan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention discloses cement clinker and a preparation method thereof. The cement clinker is prepared from the following raw materials in part by weight: 60-88 parts of aluminum extracted coal ash residue, 38-10 parts of limestone and 1-3 parts of iron ore. The preparation method of the cement clinker comprises the following steps of: firstly, grinding the raw materials; then, homogenizing the ground raw materials; and finally calcining the raw materials to obtain the cement clinker. The invention overcomes various defects in the prior art, simple raw materials and high utilization rate are realized, and the traditional cement production process does not need to be improved. The obtained portland cement has high early strength, and the amount of strength increase is stable without great fluctuations. Compared with the traditional cement clinker production process, the preparation method can enable the consumption of limestone for each ton of cement clinker is lowered by 60-90%, the emission amount of CO2 is lowered by 60-90%, energy consumption is lowered by more than 30%, and the production capacity of single kiln is improved by 30%. The preparation method is a cyclic and economic project tightly linked to aluminum extraction from coal ash.

Description

technical field [0001] The invention relates to building material technology, in particular to a cement clinker and a preparation method thereof. Background technique [0002] With the increasing shortage of bauxite resources in our country, the use of fly ash, coal gangue and other industrial solid wastes to extract alumina has attracted more and more attention. For example, the Late Paleozoic coal seams and gangue in the Ordos Basin are rich in boehmite and kaolinite and other minerals, and the alumina content in the fly ash produced after combustion is as high as about 50%, which is comparable to that in medium-grade bauxite. The content is equivalent, and it is a very valuable raw material for alumina production. According to statistics, the potential reserves of high-aluminum fly ash in the central and western regions of Inner Mongolia are as high as 15 billion tons. With the increasing shortage of bauxite resources in our country, the extraction of alumina from other...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B7/26
CPCY02P40/10
Inventor 闫绍勇陈刚孙俊民张国希张战军周立平洪景南张晓云高峰
Owner INNER MONGOLIA DATANG INT RENEWABLE RESOURCES DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap