Fluorine-containing paper oil-proof agent and its preparation method

A technology of oil repellant and paper, which is applied in papermaking, textile and papermaking, non-fiber pulp addition, etc., to achieve the effect of improving oil repellency, reducing surface performance and strong adhesion

Inactive Publication Date: 2012-09-19
QUANZHOU SICONG NEW MATERIAL DEV
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Fluorine-containing paper oil-repellent has good waterproof and oil-proof performance, so it has been paid attention to by some large foreign companies and scientific research institutions and is competing to carry out related research work. There are few studies on this

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorine-containing paper oil-proof agent and its preparation method
  • Fluorine-containing paper oil-proof agent and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Example 1: Take 91.0g monomer perfluoroalkyl ethyl acrylate, 22.5g monomer methyl methacrylate, 22.5g monomer stearyl acrylate, 2.5g monomer methylol acrylamide, 3.0g monomer Bulk N,N-diethylaminoethyl methacrylate, 8.5g monomer diacetone acrylamide, 0.9g initiator azobisisobutyronitrile, 0.3g chain transfer agent dodecylmercaptan, 100.0g acetone Add 100.0g of isopropanol mixed solvent into a reaction vessel equipped with a stirrer, a thermometer and a condenser. After passing through nitrogen gas for deoxygenation, stir and heat, and raise the temperature to 50-80°C. After reacting for 6-8 hours, add 2.5g concentration It is 30% by weight hydrogen peroxide aqueous solution and 450g deionized water, stop the reaction after 1 hour, cool down to room temperature, distill off the acetone and isopropanol solvents, adjust the pH value to 6.0-7.0 with acetic acid, and obtain a solid content of 27.5%. Fluorine-containing paper oil repellent, the specific gravity of the polymer...

Embodiment 2

[0047] Example 2: Take 101.0g of monomeric perfluoroalkylethyl acrylate, 10.0g of monomeric lauryl acrylate, 21.5g of monomeric acrylonitrile, and 13.5g of monomeric N,N-dimethylaminoethyl methacrylate , 4.0g monomer ureidomethacrylate QM-1558, 2.2g initiator azobisisobutyronitrile, 0.3g chain transfer agent dodecyl mercaptan, 100.0g acetone and 100.0g isopropanol mixed solvent was added In the reaction vessel equipped with a stirrer, a thermometer and a condenser, after passing nitrogen gas to deoxygenate, stir and heat, raise the temperature to 50-80°C, and after reacting for 6-8 hours, add 7.4g of 30% hydrogen peroxide aqueous solution with a concentration of 30% by weight And 450g deionized water, stop reaction after 1 hour, drop to room temperature, steam acetone and isopropanol solvent, adjust pH value with acetic acid to be 6.0-7.0, obtain the fluorine-containing paper oil repellent of 22.5% solid content, polymer The specific gravity is 1.01-1.10, and the molecular wei...

Embodiment 3

[0048] Example 3: Take 112.5g monomer perfluoroalkyl ethyl acrylate, 15.5g monomer methyl acrylate, 11.5g monomer stearyl methacrylate, 4.0g monomer methylol acrylamide, 2.0g monomer Bulk N,N-diethylaminoethyl methacrylate, 4.5g monomer allyl ureidoethyl ether WAMⅡ, 1.5g initiator azobisisobutyronitrile, 0.5g chain transfer agent dodecyl sulfide Alcohol, 100.0g of acetone and 100.0g of isopropanol mixed solvent is added to a reaction vessel equipped with a stirrer, a thermometer and a condenser. After passing through nitrogen to deoxygenate, stir and heat, raise the temperature to 50-80°C, and react for 6-8 hours , adding 4.1g concentration of 30% hydrogen peroxide aqueous solution and 450g deionized water, stop reaction after 1 hour, drop to room temperature, distill off acetone and isopropanol solvent, adjust pH value to 6.0-7.0 with acetic acid, obtain Fluorine-containing paper oil repellent with a solid content of 26.5%, the specific gravity of the polymer is 1.01-1.10, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A fluorine-containing paper oil-proof agent is an acrylate polymer solution containing a perfluoroalkyl side chain, wherein the polymer is prepared from 55.0-85.0% of a fluorine-containing monomer, 5.0-35.0% of a fluorine-free monomer, 3.0-10.0% of a functional monomer, 2.0-10.0% of an adhesion reinforcing monomer, 0.5-2.0% of an initiator, 0.1-0.4% of a chain transfer agent, and acetone and isopropanol mixed solution by copolymerization. The polymer solution has the characteristics of strong adhesion, low consumption, good oil resistance and good water resistance. By adding the adhesion reinforcing monomer, a fluorine-containing activator can be adhered to paper fiber, and the surface property of the paper fiber is reduced, therefore, the oil proofness of the paper is improved, and the strength and stiffness of the paper are increased at the same time.

Description

technical field [0001] The invention relates to an industrially used paper waterproof and oil-repellent agent and its preparation technology, in particular to a preparation technology of a fluorine-containing paper oil-repellent agent. Packaging bags, folding paper lunch boxes, cream pastry packaging boxes and paper bags are being treated to resist the penetration of animal and vegetable oils. Background technique [0002] With the improvement of people's living standards and the continuous strengthening of environmental protection awareness, many plastic products that are difficult to degrade are gradually replaced by paper products, especially in the field of packaging. Paper products have been widely used in catering, food and other packaging and daily life. The paper products used in this field are required to have a certain waterproof and oil-proof function. As an excellent waterproof and oil-proof material, fluorine-containing paper oil-proof agent uses the special s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H21/14C08F220/24C08F220/22C08F220/38C08F220/14C08F220/18C08F220/44C08F212/08C08F2/38
Inventor 程思聪
Owner QUANZHOU SICONG NEW MATERIAL DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap