Wear-resistant and weather-resistant epoxy resin coating adhesive and its preparation method

A technology of epoxy resin coating and epoxy resin, applied in epoxy resin glue, novolac epoxy resin adhesive, adhesive and other directions, can solve the problems of poor aging resistance and poor construction, and achieve weather resistance. Good properties, taking into account the effects of anti-settling and good reactivity

Active Publication Date: 2012-10-17
YANTAI TIGHTSEN FINE CHEM
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve technical problems such as poor wear resistance, weather resistance, aging resistance and poor workability of epoxy resin protective coatings in the prior art, and to provide a wear-resistant and weather-resistant epoxy resin coating glue a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant and weather-resistant epoxy resin coating adhesive and its preparation method
  • Wear-resistant and weather-resistant epoxy resin coating adhesive and its preparation method
  • Wear-resistant and weather-resistant epoxy resin coating adhesive and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Preparation of yellow color paste: Weigh 800 g of alicyclic glycidyl ether epoxy resin CER-170 and 200 g of chrome yellow pigment in the coating, mix and wet with a shovel; adjust the gap between the sticks of the three-roll mill and pass the mixture through the rollers three times , get a yellow paste.

[0053] Preparation of Component A:

[0054] Weigh phenolic epoxy resin PNE-172250g, cycloaliphatic glycidyl ether epoxy resin CER-17060g, epoxy resin toughener CYH-27750g, add them to a 2L planetary disperser, and heat to the glue temperature while stirring 70°C, stir at medium speed for 15 minutes, add epoxy diluent 1,2-hexanediol diglycidyl ether CD-118050g, add organic bentonite 4g, stir and disperse for 30 minutes; add 3000 mesh activated kaolin 50g; add 1000 mesh white 400g of corundum powder, stir and disperse at high speed for 30 minutes; add 50g of chopped glass fiber, stir and disperse at medium speed for 10 minutes, cool down to 40°C and control the temperat...

Embodiment 2

[0060] Preparation of yellow color paste: (same as Example 1)

[0061] Preparation of Component A:

[0062] Weigh 200g of phenolic epoxy resin PNE-172, 120g of cycloaliphatic glycidyl ether epoxy resin CER-170, and 40g of epoxy resin toughener CYH-277, add them to a 2L planetary disperser, and heat them to the glue while stirring. The liquid temperature was 70°C, stirring at a medium speed for 15 minutes, adding 40 g of epoxy diluent 1,2-hexanediol diglycidyl ether CD-1180, adding 6 g of organic bentonite, stirring and dispersing for 30 minutes; adding 30 g of 3000-mesh activated kaolin; Add 439g of 1000-mesh white corundum powder, stir and disperse at high speed for 30 minutes; add 40g of chopped glass fiber, stir and disperse at medium speed for 10 minutes, cool down to 40°C and control the temperature, add coupling agent KH560 12g, antioxidant 4g, UV absorber 4g, stir at medium speed for 15 minutes; add 50g of yellow color paste and 15g of white carbon black, stir and disp...

Embodiment 3

[0068] Preparation of yellow color paste: (same as Example 1)

[0069] Preparation of component A:

[0070] Weigh 150g of phenolic epoxy resin PNE-172, 160g of cycloaliphatic glycidyl ether epoxy resin CER-170, and 40g of epoxy resin toughener QS-BN, add them to a 2L planetary disperser, and heat them to a glue solution while stirring. The temperature was 70°C, stirring at medium speed for 15 minutes, adding epoxy diluent 1,2-hexanediol diglycidyl ether CD-1180 40g, adding organic bentonite 8g, stirring and dispersing for 30 minutes; adding 3000 mesh active kaolin 50g; adding 418g of 1000-mesh white corundum powder, stir and disperse at high speed for 30 minutes; add 60g of chopped glass fiber, stir and disperse at medium speed for 10 minutes, cool down to 40°C and control the temperature, add coupling agent KH560 5g, antioxidant 3g, UV absorber 6g , stir at medium speed for 15 minutes; add 50g of yellow color paste and 10g of white carbon black, stir and disperse at high spe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention which relates to a wear-resistant and weather-resistant epoxy resin coating adhesive and its preparation method belongs to the technical field of adhesives. The adhesive comprises a component A and a component B, wherein the component A comprises 6-16 parts of an alicyclic glycidyl ether epoxy resin, 15-25 parts of a novolac epoxy resin, 4-6 parts of an epoxy active diluent, 4-6 parts of a responsive flexibilizer, 0.5-1.2 parts of a coupling agent, 0.4-0.8 parts of organic bentonite, 0.3-0.5 parts of an antioxidant, 0.4-0.8 parts of an ultraviolet ray absorbent, 40-45 parts of white corundum powder, 3-5 parts of filler powder, 4-6 parts of a short glass fiber, 5 parts of a yellow color paste, and 1-2 parts of white carbon black; and the component B comprises 15-25 parts of an alicyclic amine, 10-15 parts of isophorone diamine, 6-9 parts of aminoethylpiperazine, 2-3 parts of a curing accelerator, 40-45 parts of the white corundum powder, 4-6 parts of the short glass fiber, 4-6 parts of the filler powder and 3-5 parts of the white carbon black. The preparation method comprises the steps of yellow color paste preparation, component A preparation and component B preparation. Compared with adhesives obtained through the prior art, the mechanical strength and the wear resistance of the adhesive of the invention are obviously improved.

Description

Technical field: [0001] The invention relates to a wear-resistant and weather-resistant epoxy resin coating adhesive and a preparation method thereof, belonging to the technical field of adhesives. technical background: [0002] Epoxy resin has good adhesion to most materials, and the cured epoxy resin has the characteristics of high bonding strength, heat resistance, chemical resistance, good dielectric property, and low shrinkage; it is used in bonding and protective coatings. On the one hand, liquid bisphenol A glycidyl ether type epoxy resin is widely used, but because it contains benzene ring, its ultraviolet radiation resistance and aging resistance are poor, and it will gradually change color and pulverize in outdoor environments, making the bonding and protection failure. In addition, when the liquid bisphenol A epoxy resin is cured, the cohesive stress is large, the cured product is hard and brittle, and the acid and alkali resistance and humidity resistance are po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J163/04C09J163/00C09J11/04C09J11/06
Inventor 林志秀林绍盛
Owner YANTAI TIGHTSEN FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap