Method for producing health-care polyprophylene bulked continuous filament

A technology of bulked filament and manufacturing method, applied in the direction of single-component polyolefin rayon, etc., can solve the problems of large static electricity, poor thermal performance, elongation, etc., to improve moisture absorption, improve strength and elongation, promote Physical and mental health effects

Active Publication Date: 2014-08-13
ZHEJIANG SCI-TECH UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polypropylene fiber, also known as PP fiber or polypropylene fiber, is a fiber spun from isotactic polypropylene. Its biggest advantage is light weight and a density of 0.91 / cm 3 , 20-30% lighter than ordinary chemical fibers, is the smallest proportion of all textile fibers; it has high strength, large elongation, high initial modulus, and excellent elasticity; polypropylene fiber is second only to polyamide in abrasion resistance Fiber; good corrosion resistance, especially good stability to inorganic acids and alkalis; no mold, no rot, no fear of insects, etc., but there are disadvantages such as hygroscopicity, poor thermal performance, and large static electricity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The manufacture method of health-care polypropylene expanded filament of the present invention, it adopts following steps:

[0027] In step A), take 15 parts by mass of magnesium borate whiskers whose characteristic parameters are 0.2-1um in diameter and 6-15um in length; 15 parts whose length×width are 10um×5um sepiolite; 10 parts whose characteristic parameters are Palygorskite fibers with a diameter of 0.1-0.8um and a length of 6-15um; after mixing these three materials evenly, roast them in a vacuum furnace at 350°C for 4h-6h to obtain high strength, high void, high water absorption, and high water retention Inorganic nanomaterials; after cooling, stir and disperse with sodium hexametaphosphate in absolute ethanol, and treat with normal pressure plasma for 10-20min to obtain inorganic nanomaterials with clean surface, etching and high adhesion; Ultrasonic dispersion and cleaning in 60-70°C deionized water of the dispersion liquid for 30 minutes, take the suspended w...

Embodiment 2

[0031] The manufacture method of health-care polypropylene expanded filament of the present invention, it adopts following steps:

[0032] A) According to the number of parts by mass, take 12 copies of magnesium borate whiskers with a characteristic parameter diameter of 0.2-1um and a length of 6-15um, 12 parts with a characteristic parameter length×width of 10um×5um sepiolite; 8 copies with a characteristic parameter diameter of 0.1 -0.8um, palygorskite fiber with a length of 6-15um; after mixing these three materials evenly, roast them in a vacuum furnace at 300°C for 4-6h to obtain inorganic nanomaterials with high strength, high voids, high water absorption and high water retention Stir and disperse in dehydrated alcohol with sodium hexametaphosphate after cooling, and treat with normal pressure plasma for 10-20min to obtain inorganic nanomaterials with clean surface, etching and high adhesion; Ultrasonic dispersion and cleaning in deionized water at 60-70°C for 25 minutes...

Embodiment 3

[0036] The manufacture method of health-care polypropylene expanded filament of the present invention, it adopts following steps:

[0037] A) According to the number of parts by mass, take 18 copies of magnesium borate whiskers whose characteristic parameters are 0.2-1um in diameter and 15um in length, 18 copies whose characteristic parameters are 10um×5um sepiolite; um, palygorskite fibers with a length of 6-15um; after mixing these three materials evenly, roast them in a vacuum furnace at 400°C for 4-6h to obtain inorganic nanomaterials with high strength, high voids, high water absorption, and high water retention; cooling Finally, stir and disperse with sodium hexametaphosphate in absolute ethanol, and treat with normal pressure plasma for 10-20min to obtain inorganic nanomaterials with clean surface, etching and high adhesion; then in the 60- Ultrasonic dispersion and cleaning in deionized water at 70°C for 35 minutes, take the suspended whiskers in the upper layer of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

A method for producing a health-care polyprophylene bulked continuous filament (BCF) adopts the following steps: A, magnesium borate whisker, sepiolite and palygorskite fiber are mixed uniformly to be sintered in a vacuum furnace, are cooled and stirred in absolute ethyl alcohol through sodium hexametaphosphate to be dispersed, are subjected to plasma treatment at normal pressure and then are ultrasonically dispersed, cleaned, filtered and dried in deionized water which contains calcium stearate dispersion liquid; B, talcum powder and aluminic acid ester coupling agent are mixed and stirred; then, nanoscale tourmaline composite powder, calcium stearate propene polymer (PP)-g-maleic anhydride (MAH) bulking agent and the modified whisker mixture which is obtained in step A are added to be mixed and stirred, and polypropylene is added to be stirred at a high speed so as to obtain a modified polypropylene mixture; and C, the modified polypropylene mixture is dried and is subjected to melt extrusion in an extruding machine to spin the comfortable health-care polyprophylene bulked continuous filament which has the functions of well absorbing moisture, releasing moisture, resisting static electricity and naturally releasing negative oxygen ions.

Description

technical field [0001] The invention relates to a health-care polypropylene bulked filament (BCF), which includes tourmaline composite powder, inorganic materials, polypropylene polymer modification, etc., and belongs to the textile material manufacturing technology. Background technique [0002] Polypropylene fiber, also known as PP fiber or polypropylene fiber, is a fiber spun from isotactic polypropylene. Its biggest advantage is light weight and a density of 0.91 / cm 3 , 20-30% lighter than ordinary chemical fibers, is the smallest proportion of all textile fibers; it has high strength, large elongation, high initial modulus, and excellent elasticity; polypropylene fiber is second only to polyamide in abrasion resistance Fiber; good corrosion resistance, especially good stability to inorganic acids and alkalis; no mold, no rot, no fear of insects, etc., but there are disadvantages such as hygroscopicity, poor thermal performance, and high static electricity. [0003] The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/46D01F1/10
Inventor 凌荣根韩晨杨美娟凌晓龙方千瑞
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com