PET (Polyethyleneglycol Terephthalate) fiber/glass fiber composite sound absorbing cotton and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of glass fiber and quartz glass fiber, which is applied in the field of non-woven fabrics, can solve the problems of insufficient product adhesion, no flame retardant treatment, poor tensile strength, etc., and achieve improved sound absorption, good product adhesion, and production efficiency high effect
Inactive Publication Date: 2013-03-13
芜湖跃飞新型吸音材料股份有限公司
View PDF6 Cites 21 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, there are many deficiencies in the existing sound-absorbing cotton products and their manufacturing methods. The main performances are: the original manual operation, the use of knife stacks, low productivity; no flame-retardant treatment; insufficient adhesion of the product, easy to loose, tension Poor strength, etc.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0015] A PET fiber / glass fiber composite sound-absorbing cotton, made of the following raw materials in parts by weight: PET fiber 75, quartz glass fiber 48, fatty alcohol polyoxyethylene ether sodium sulfate 16, Pingpingjia O-10 25, PP 95, LDPE 32. Calcium carbonate whisker 16, modified diatomaceous earth 12, stearic acid 2.5, trioctyl trimellitate 6, ammonium polyphosphate 5, oxidized polyethylene wax 3, bis(dioctyloxypyrophosphate) ) Ethylene titanate 1.5, zinc stearate 2, isooctyl tin dimethyldithioglycolate 2, antioxidant RD 0.8, antioxidant 1010 1.5.
[0016] Wherein, the modified diatomite is prepared by the following method: put the dried diatomite into a ball mill, add 25% graphite, 2% vermiculite powder, 2% sepiolite powder, 5% light Calcium carbonate, 2.5% water glass and 4% polyvinyl alcohol, ball milled for 10 hours, calcined at 1100°C for 2 hours, crushed and ground into 200 mesh powder.
[0017] The preparation method of PET fiber / glass fiber comp...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
diameter
aaaaa
aaaaa
oxygen index
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses PET (Polyethyleneglycol Terephthalate) fiber / glass fiber composite sound absorbing cotton, which is prepared from the following raw materials in parts by weight: 70-80 parts of PET fiber, 40-50 parts of quartz glass, 15-20 parts of fatty alcohol polyoxyethylene ether sodium sulfate, 20-30 parts of peregal O-10, 80-100 parts of PP (Polypropylene), 30-40 parts of LDPE (Low-Density Polyethylene), 15-20 parts of calcium carbonate whiskers, 10-15 parts of modified diatomite, 2-3 parts of stearic acid, 5-8 parts of trioctyl trimellitate, 4-6 parts of ammonium polyphosphate, 2-3 parts of oxidized polyethlene wax, 1-2 parts of di(dioctyloxy pyrophosphate)ethylene titanium ester, 2-3 parts of zinc stearate, 1-2 parts of dimethyldimercaptoisooctylacetate tin, 0.5-1.5 parts of anti-aging agent RD, and 1-2 parts of antioxidant 1010. The sound absorbing cotton prepared in the invention has the advantages of high appearance flatness, uniform thickness, soft handfeel, high product viscosity, high tensile property, high sound absorbing performance, good flame retarding effect and the like.
Description
technical field [0001] The invention relates to nonwoven fabric technology, in particular to a PET fiber / glass fiber composite sound-absorbing cotton and a preparation method thereof. Background technique [0002] Noise is one of the three major public hazards that pollute the environment in modern society. Noise directly affects people's health. With the progress of society, people put forward higher and higher requirements for the prevention and control of noise that pollutes the environment. Sound-absorbing cotton can convert the vibration energy of medium and high-frequency noise generated in life into the kinetic energy of the fine denier fibers inside the sound-absorbing cotton, and convert it into heat energy and disappear, achieving the function of sound absorption and noise reduction. Therefore, sound-absorbing cotton has good sound-absorbing, heat-insulating and warm-keeping properties, and has been widely used in the fields of building materials, automobiles and o...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.