An ozone-resistant cable sheath material

A cable sheathing material and ozone-resistant technology, used in insulated cables, cables, circuits, etc., can solve problems such as poor storage stability, and achieve the effects of low shrinkage, good dispersion, and delaying aging speed.

Active Publication Date: 2015-09-30
ANHUI KANGLIYA CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has high tensile strength, elongation and reversible crystallinity, good adhesion, aging resistance, heat resistance, oil resistance and chemical corrosion resistance. It can be used for a long time at 80-100 °C and has a certain flame retardancy. However, the disadvantage is that the storage stability is poor. Therefore, using neoprene as a cable sheath material can ensure that it has strong heat resistance, aging resistance, oil resistance, corrosion resistance, etc., and by adding some modified fillers. Improving its storage stability further improves the performance of the cable sheathing material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] An ozone-resistant cable sheathing material is characterized in that it is composed of the following raw materials in parts by weight (kg):

[0014] Neoprene M-40 100, SG-4 PVC resin 19, mica powder 30, modified filler 25, glass powder 4, epoxy butyl oleate 6, dibutyl maleate 6, oxidized polyethylene Wax 5, hydroquinone 2, antioxidant 1010 2, borax 4, isopropyl tris(dioctyl pyrophosphate acyloxy) titanate 2, antioxidant MB 2, benzoyl peroxide 2, sulfur 0.8, thiram 0.6;

[0015] The modified filler is composed of the following raw materials in parts by weight:

[0016] Concentration of 0.5% sulfuric acid solution 1000, barium sulfide 90, ethanol 40, aluminum hydroxide powder 15, sorbitan monooleate 12, distearoyloxy isopropoxy aluminate 3, titanium dioxide 4, formazan Triethoxysilane 2, Sodium Polyacrylate 6, Dicumyl Peroxide 2, Sodium Phosphate 6, Stearic Acid 3, Appropriate amount of water;

[0017] Continue to introduce the above sulfuric acid solution into the abo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
retention rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ozone-resistant cable sheath material. The ozone-resistant cable sheath material comprises the following raw materials by weight: 93 to 100 parts of chloroprene rubber M-40, 14 to 19 parts of an SG-4 type PVC resin, 20 to 30 parts of mica powder, 15 to 25 parts of a modification filling material, 4 to 7 parts of glass powder, 4 to 6 parts of dibutyl maleate, 3 to 5 parts of oxidized polyethlene wax, 1 to 2 parts of hydroquinones, 1 to 2 parts of the antioxidant 1010, 2 to 4 parts of borax, 1 to 2 parts of isopropyl tri(dioctylpyrophosphate) titanate, 1 to 2 parts of the anti-aging agent MB, 1 to 2 parts of benzoyl peroxide, 0.8 to 1 part of sulphur and 0.6 to 1 part of ziram. The cable sheath material produced in the invention has excellent physical properties, a stable dimension, low shrinking percentage, high tensile strength, great tearing strength, strong resilience and good resistance to oil, heat, burning, sunlight, ozone, acid and alkali and chemical reagents; and the modification filling material provided by the invention has good dispersibility and low surface tension, enables tensile strength and stress at definite elongation of the cable sheath material to be further improved, reduces heat generation and compression set, delays the ageing speed of the cable sheath material, is capable of resisting acid and alkali and allows production cost to be reduced.

Description

technical field [0001] The invention mainly relates to a cable sheathing material, in particular to an ozone-resistant cable sheathing material. Background technique [0002] Neoprene has good physical and mechanical properties, oil resistance, heat resistance, flame resistance, sunlight resistance, ozone resistance, acid and alkali resistance, and chemical reagent resistance. It has high tensile strength, elongation and reversible crystallinity, good adhesion, aging resistance, heat resistance, oil resistance and chemical corrosion resistance. It can be used for a long time at 80-100 °C and has a certain flame retardancy. However, the disadvantage is that the storage stability is poor. Therefore, using neoprene as a cable sheath material can ensure that it has strong heat resistance, aging resistance, oil resistance, corrosion resistance, etc., and by adding some modified fillers. Improving its storage stability further improves the performance of the cable sheathin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L11/00C08L27/06H01B3/28H01B7/28C08K13/06C08K9/06C08K9/04C08K3/34C08K3/40C08K5/1515C08K5/11C08K5/13C08K3/38C08K5/14C08K3/06C08K3/30C08K3/22
Inventor 李训祥王新祥周志梅李贻凤胡云昌
Owner ANHUI KANGLIYA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com