Light-weight heat-insulating material taking granite waste as raw material and preparation method thereof

A technology for granite waste and thermal insulation materials, applied in the field of lightweight thermal insulation materials, can solve the problems of high density of foamed materials, affecting application effects, low compressive strength, etc., and achieves high compressive strength, low production cost, and firing temperature. low effect

Inactive Publication Date: 2015-01-14
WUHAN UNIV OF SCI & TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But = high firing temperature and high energy consumption, resulting in high density of the foamed material, which seriously affects the application effect of the product in the fields of heat insulation, sound insulation and fire prevention
[0004] Therefore, there are some deficiencies in the comprehensive utilization of granite waste as raw materials, such as high bulk density, high thermal conductivity and low compressive strength, which cannot meet the requirements for lightweight material products in the fields of heat insulation, sound insulation, and fire prevention.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A light heat insulating material using granite waste as a raw material and a preparation method thereof. First use 50-55wt% granite waste fine powder, 15-20wt% broken glass powder, 3-5wt% limestone powder, 8-13wt% potassium chloride and 10-15wt% sodium chloride as raw materials, mix , the mixture is heat-treated at 800-950°C for 0.5-1 hour, and ground to a particle size of less than 0.045mm to obtain a grinding material; then adding limestone powder accounting for 0.5-1.5wt% of the raw material, 5-8wt% Industrial soda ash, 3-5wt% white carbon black and 8-10wt% sodium sulfate are ball milled in a ball mill for 2-5 hours to obtain a ball mill; then add 3-10wt% of raw material water to the ball mill, Stir for 10-30 minutes, press into a green body, dry, heat-treat the dried green body at 1000-1100°C for 2-5 hours, cool naturally, soak in water for 12-24 hours, and finally heat it at 80-110°C Dry for 12 to 24 hours to prepare a lightweight thermal insulation material using...

Embodiment 2

[0033] A light heat insulating material using granite waste as a raw material and a preparation method thereof. First use 60-65wt% granite waste fine powder, 13-18wt% broken glass powder, 1-3wt% limestone powder, 5-9wt% potassium chloride and 5-10wt% sodium chloride as raw materials, mix , the mixture is heat-treated at 900-1000°C for 0.8-1.3 hours, and ground to a particle size of less than 0.045mm to obtain a grinding material; then adding limestone powder accounting for 2-3 wt% of raw materials, 7-10 wt% Industrial soda ash, 1-3wt% white carbon black and 1-3wt% sodium sulfate were ball milled in a ball mill for 2-5 hours to obtain a ball mill; then add 3-10wt% of raw material water to the ball mill, Stir for 10-30 minutes, press into a green body, dry, heat-treat the dried green body at 800-900°C for 2-5 hours, cool naturally, soak in water for 12-24 hours, and finally heat it at 80-110°C Dry for 12 to 24 hours to prepare a lightweight thermal insulation material using gra...

Embodiment 3

[0036]A light heat insulating material using granite waste as a raw material and a preparation method thereof. First use 55-60wt% granite waste fine powder, 10-15wt% broken glass powder, 3-5wt% limestone powder, 8-13wt% potassium chloride and 10-15wt% sodium chloride as raw materials, mix , the mixture is heat-treated at 950-1050°C for 1-1.5 hours, and ground to a particle size of less than 0.045mm to obtain a grinding material; then adding limestone powder accounting for 1-2wt% of the raw material, 5-7wt% Industrial soda ash, 2-4wt% white carbon black and 2-4wt% sodium sulfate were ball milled in a ball mill for 2-5 hours to obtain a ball mill; then add 3-10wt% of raw material water to the ball mill, Stir for 10-30 minutes, press into a green body, dry, heat-treat the dried green body at 900-1000°C for 2-5 hours, cool naturally, soak in water for 12-24 hours, and finally heat it at 80-110°C Dry for 12 to 24 hours to prepare a lightweight thermal insulation material using gra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a light-weight heat-insulating material taking granite waste as a raw material and preparation method thereof. The technical scheme comprises the following steps: mixing 50-65wt% of granite waste fine powder, 10-20wt% of chunk glass powder, 1-5wt% of limestone powder, 5-13wt% of potassium chloride, 5-15wt% of sodium chloride used as raw materials; performing heat treatment at 800-1200 DEG C for 0.5-2 hours, and grounding until the particle size is less than 0.045mm; adding limestone powder, industrial sodium carbonate, white carbon black and sodium sulfate which respectively account for 0.5-3wt%, 5-10wt%, 1-5wt% and 1-10wt% of the raw materials into the ground material, and performing ball milling for 2-5 hours; and adding water which accounts for 3-10wt% of the raw materials into the ball milled material, stirring, pressing into a blank, drying, performing heat treatment at 800-1200 DEG C for 2-5 hours, naturally cooling, soaking with water, and drying at 80-110 DEG C, thus preparing the light-weight heat-insulating material taking granite waste as a raw material. The invention is simple in process, low in production cost, beneficial to comprehensive utilization of resources and friendly to environment; and the product is low in volume density, low in heat conductivity coefficient and high in compression strength.

Description

technical field [0001] The invention belongs to the technical field of lightweight thermal insulation materials. In particular, it relates to a light heat insulating material using granite waste as a raw material and a preparation method thereof. Background technique [0002] Granite is a plutonic acidic igneous rock with a high silica content, mainly composed of dark minerals such as quartz, feldspar and a small amount of mica. Due to the characteristics of not easy weathering, high hardness and wear resistance, granite is widely used in the fields of architectural decoration engineering, ground stone materials and carving materials. my country is a large stone processing country. With the increase in the demand for granite in recent years, a large amount of waste stones and waste stone powder have been produced in the stone processing process. If they are not used rationally, a large amount of waste will be discharged and accumulated. Serious pollution The environment and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/00B09B3/00
Inventor 刘浩王玺堂王周福张保国
Owner WUHAN UNIV OF SCI & TECH