Nano zinc oxide honeycomb type purification activated carbon and preparation method thereof

A nano-zinc oxide, activated carbon technology, applied in chemical instruments and methods, metal/metal oxide/metal hydroxide catalysts, physical/chemical process catalysts, etc., can solve problems such as lack, reduced adsorption effect, and inability to intimate contact , to achieve the effect of small adsorption resistance, increased adsorption and desorption speed, and low-carbon energy-saving treatment effect.

Inactive Publication Date: 2016-02-17
LISHUI HE ZI PURIFICAT EQUIP CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Activated carbon is used in the industrial field for decolorization, refining, and purification of liquid phase adsorption. In terms of gas phase adsorption, powdered and granular activated carbon cannot be in close contact with toxic and harmful substances in the air, thus greatly reducing the adsorption effect.
[0004] On the other hand, the current activated carbon application technology lacks the ability to ensure that activated carbon has a good adsorption of dirt, and also enables it to decompose toxic gases such as formaldehyde, ammonia, and benzene adsorbed in activated carbon under the action of ordinary light. Self-purification function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: The weight ratio of the raw materials used is: 23 parts of chemical activated carbon, 23 parts of coal-based granular activated carbon, 54 parts of coconut shell activated carbon, the activated carbon of three kinds of different proportions that will be selected is put into the ball mill in the ball mill, and ground into The mesh number is 500 mesh activated carbon powder. Then get 100 parts of activated carbon powder, 5 parts of nano-zinc oxide with a purity of 99%, 1.5 parts of methylcellulose, and 1.5 parts of talcum powder. The above-mentioned raw materials are sequentially added to stirring and mixing, stirring evenly to make a mixture. Then put the mixed material in a kneader (a mixer can also be used), add moderate distilled water, knead for 30 minutes, and knead it into a paste in the kneader. Then the mud paste is placed in a vacuum mud mill, and mud is honed into a uniform plasticized mud paste in the vacuum mud mill. Then put the plasticized m...

Embodiment 2

[0028] Embodiment 2: The weight ratio of the raw materials used is: 18 parts of chemical activated carbon, 25 parts of coal-based granular activated carbon, 57 parts of coconut shell activated carbon, three kinds of activated carbons with different proportions are put into a ball mill for ball milling, and ground into The mesh number is 500 mesh activated carbon powder. Then get 100 parts of activated carbon powder, 6 parts of nano-zinc oxide with a purity of 99%, 2 parts of methylcellulose, and 2 parts of talcum powder. The above-mentioned raw materials are sequentially added to stirring and mixing, stirring evenly to make a mixture. The remaining steps are the same as in Example 1, wherein the profile with a moisture content of less than 10% is put into a furnace for sintering at a sintering temperature of 900° C. for 6 hours.

[0029] The performance of the nano zinc oxide honeycomb type purification activated carbon product: iodine adsorption value 1100~1200mg / g, benzene ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
iodine adsorption valueaaaaaaaaaa
iodine adsorption valueaaaaaaaaaa
Login to View More

Abstract

The invention belongs to honeycomb type nano zinc oxide purifying activated carbon and a preparation method thereof. The honeycomb type nano zinc oxide purifying activated carbon is prepared from raw materials of, by weight, 17-28 parts of chemical activated carbon, 15-25 parts of coaly granular activated carbon, 50-60 parts of coconut shell activated carbon, 4-6 parts of nano zinc oxide 99% in purity, 1-2 parts of methylcellulose and 1-2 parts of talc powder. The method includes the steps of performing ball milling, raw material mixing and uniform stirring to prepare product materials, and then preparing the honeycomb type nano zinc oxide purifying activated carbon via vacuum pugging, extrusion forming, airing and sintering. By the method, the activated carbon can have an excellent contaminant absorption function, can decompose poisonous gases such as formaldehyde, ammonia and benzene absorbed therein under the action of ordinary light, in other words, has a self-purifying function, and further has the advantages of being formable, firm, durable in use, simple and feasible in method, low in pollution treatment cost, low-carbon, energy saving and good in treatment effect.

Description

technical field [0001] The invention belongs to a nanometer zinc oxide honeycomb type purification activated carbon and a preparation method thereof. Background technique [0002] Activated carbon is widely used in various aspects of industrial and agricultural production, such as alkali-free deodorization (refined mercaptan removal), ethylene desalted water (refined packing), catalyst carrier (palladium, platinum, rhodium, etc.), water purification and sewage treatment in the petrochemical industry; Water quality treatment and protection of power plants in the industry; decolorization and refining of chemical catalysts and carriers, gas purification, solvent recovery, and oils in the chemical industry; refining and decolorization of beverages, alcohol, monosodium glutamate mother liquor and food in the food industry; gold in the gold industry Extraction, recovery of tail liquid; sewage treatment, waste gas and harmful gas treatment, gas purification in environmental protect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/20B01J20/30B01J23/06
Inventor 刘大敏季小恩颜海军
Owner LISHUI HE ZI PURIFICAT EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com