Aging-resistant insulating sheath material for transformer and preparation method thereof

An insulating sheath and anti-aging technology, which is applied in the field of aging-resistant insulating sheathing materials and its preparation, can solve the problems of easy-aging cracks, economic losses, and leakage of insulating sheaths, and achieve good insulation performance, physical and mechanical properties, and durability. Excellent aging performance, excellent acid and alkali resistance

Inactive Publication Date: 2014-01-15
ANHUI KELIN ELECTRONICS
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing insulating sheath is prone to aging and cracking due to long-term sunlight exposure, salt spray, and acid rai

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aging-resistant insulating sheath material for transformer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] An aging-resistant insulating sheath material for transformers, made of the following raw materials (kg): methyl vinyl silicone rubber (110-2) 60, butadiene rubber (BR9000) 25, low-density polyethylene 15, sediment White carbon black 25, zinc oxide 4, stearic acid 1.5, dicumyl peroxide 2, sulfur 1, antioxidant OD 1.5, accelerator TMTD 1.5, diphenylsilanediol 6, epoxy soybean oil 8 , Acetyl triethyl citrate 10, hydroxy silicone oil 4, zinc borate 8, antimony trioxide 6, nano potassium feldspar 12, nano alumina 8, composite filler 4;

[0013] The preparation method of the composite filler is as follows: a. Weigh bauxite, sepiolite, illite, and kaolin in a weight ratio of 6:4:3:1 and mix them evenly, calcining at 520°C for 3h, cooling to normal temperature, and adding Stir in 15% sulfuric acid solution at 1500rpm for 2 hours, filter, wash until neutral, dry, crush, and pass through a 400-mesh sieve; b. Add water to the sieved powder and stir to make a suspension with a con...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aging-resistant insulating sheath material for a transformer and a preparation method thereof. The aging-resistant insulating sheath material is prepared from 50-70 weight parts of methyl vinyl silicone rubber, 20-30 weight parts of butadiene rubber, 15-20 weight parts of low density polyethylene, 20-30 weight parts of precipitated silica, 3-5 weight parts of zinc oxide, 1-2 weight parts of stearic acid, 2-3 weight parts of dicumyl peroxide, 1-2 weight parts of sulfur, 1-2 weight parts of an antiager OD, 1-2 weight parts of a promoter TMTD, 4-8 weight parts of diphenylsilanediol, 5-10 weight parts of epoxidized soybean oil, 8-12 weight parts of triethyl O-acetylcitrate, 3-6 weight parts of hydroxyl silicone oil, 5-10 weight parts of zinc borate, 4-8 weight parts of antimonous oxide, 10-15 weight parts of nanometer potassium feldspar, 5-10 weight parts of nanometer aluminum oxide, and 3-6 weight parts of a composite filling material. The aging-resistant insulating sheath material has excellent aging resistance, excellent acid and alkali resistance, excellent smoke resistance, excellent ozone resistance, excellent weather resistance, good insulating properties, and good physical and mechanical properties, can be used out of doors for a long time, can resist strong acid, strong alkali and salt spray, can be exposed to the sun and rain, does not deform and crack, and is durable.

Description

technical field [0001] The invention relates to an aging-resistant insulating sheath material for a transformer and a preparation method thereof, belonging to the technical field of sealing materials. Background technique [0002] The transformer insulating sheath is used for the shielding insulation protection of the surface of the transformer bus bridge tube parent, which can effectively prevent the exposed transformer bus bridge from being accidentally touched by humans, small animals such as birds and animals or foreign objects. Electrical accidents caused by condensation flashover, pollution flashover, and icicle sticky snow, and prevent power outage accidents caused by salt spray, acid rain, and chemical gas corrosion that damage the inlet and outlet lines of transformers. However, the existing insulating sheath is prone to aging and cracking due to long-term exposure to sunlight, salt spray, and acid rain corrosion, resulting in accidents such as short circuits, elect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/07C08L9/00C08L23/06C08L23/08C08K13/06C08K9/02C08K3/30C08K3/34C08K3/36C08K5/14C08K5/1515
Inventor 周俊徐淑平
Owner ANHUI KELIN ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap