Rapid determination of total iron content in vanadium titanomagnetite

A vanadium-titanium magnetite, rapid determination technology, applied in chemical analysis by titration method, material analysis by observing the influence of chemical indicators, and analysis by making materials undergo chemical reactions, etc., can solve the problem of total iron analysis Accuracy is greatly affected, does not meet the requirements of rapid analysis, and increases the cost of analysis, etc., to achieve the effect of rapid on-site analysis, reduction of uncertain conditions and system errors, and rapid determination of methods

Inactive Publication Date: 2016-08-24
武汉钢铁有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the determination method of total iron in vanadium-titanium magnetite is to use the sample to separate vanadium after alkali fusion. This method has a long process and increases the analysis cost, which does not meet the requirements of the production site for rapid analysis.
In addition, Zhang Yubin, Du Chunping, etc. published the article "Rapid Analysis of Total Iron in Vanadium-Titanite" in "Jiangxi Metallurgy", 2007, 27(6): 39-40, 43, introducing the addition of fluoride Ammonium, use ammonium fluoride to eliminate the interference of vanadium and titanium. In this process, vanadium is not all reduced to trivalent vanadium and fluorine complex, and some of it may be reduced to tetravalent vanadium, which will also consume potassium dichromate standard titration solution, so that The analysis result is too high, it is often accumulated with the negative error in the analysis method, and a false accurate result is formed for the sample with low vanadium content, and some iron ions will also be complexed by fluorine ions, and will not be reduced, forming a negative error , so for vanadium-titanium magnetite samples with high vanadium content, it has a great influence on the accuracy of total iron analysis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rapid determination of total iron content in vanadium titanomagnetite
  • Rapid determination of total iron content in vanadium titanomagnetite
  • Rapid determination of total iron content in vanadium titanomagnetite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Get the vanadium-titanium magnetite of a certain mine, wherein the total iron content is quickly measured, and the measuring method comprises the following steps in turn:

[0033] 1) take by weighing the vanadium-titanium magnetite sample to be measured that is 0.1018g, place in the 250mL Erlenmeyer flask;

[0034] 2) Add a sufficient amount of ore dissolving solution to the Erlenmeyer flask. The composition of the ore dissolving solution is 5 mL of sodium fluoride solution with a volume mass fraction concentration of 50 g / L, and 12.0 mL of sulfur-phosphorus mixed acid solution with a volume ratio of 1:1. and 2mL concentrated nitric acid, shake the bottle gently to disperse the sample, heat it on a high-temperature electric furnace until sulfuric acid fumes come out of the bottle to the mouth of the bottle, remove it, and cool slightly;

[0035] 3) Add 10 mL of hydrochloric acid solution with a volume ratio of 1:3;

[0036] 4) Add dropwise a stannous chloride solution ...

Embodiment 2

[0059] Get the vanadium-titanium magnetite of a certain mine, wherein the total iron content is quickly measured, and the measuring method comprises the following steps in turn:

[0060] 1) Weigh 0.2005g of the vanadium-titanium magnetite standard sample GBW07226 to be measured, and place it in a 250mL conical flask;

[0061] 2) Add a sufficient amount of ore dissolving solution to the Erlenmeyer flask, the composition of the ore dissolving solution is: 8mL potassium fluoride solution with a volume mass fraction of 50g / L, 20mL sulfur-phosphorus mixed acid solution with a volume ratio of 1:1, 3mL Concentrated nitric acid, gently shake the bottle to disperse the sample, heat it on a high-temperature electric furnace until sulfuric acid fumes come out of the bottle to the mouth of the bottle, remove it, and cool slightly;

[0062] 3) Add 15mL of hydrochloric acid solution with a volume ratio of 1:2;

[0063] 4) Add dropwise a stannous chloride solution with a volume mass fractio...

Embodiment 3

[0081] Get the vanadium-titanium magnetite of a certain mine, wherein the total iron content is quickly measured, and the measuring method comprises the following steps in turn:

[0082] 1) Weigh 0.4997g vanadium-titanium magnetite standard sample GBW07224, and place it in a 1000mL conical flask;

[0083] 2) Add a sufficient amount of ore dissolving solution to the Erlenmeyer flask, the composition of the ore dissolving solution is: 30mL volume mass fraction 50g / L sodium fluoride solution, add 90mL sulfur phosphorus mixed acid solution with a volume ratio of 1:1, add 10mL of concentrated nitric acid, gently shake the bottle to disperse the sample, heat it on a high-temperature electric furnace until sulfuric acid fumes come from the bottle to the mouth of the bottle, remove it, and cool slightly;

[0084] 3) Add 30mL of hydrochloric acid solution with a volume ratio of 1:2;

[0085] 4) Add dropwise a stannous chloride solution with a volume mass fraction of 60g / L (dissolve 6g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The rapid determination method of total iron content in a kind of vanadium-titanium magnetite provided by the invention comprises: 1) taking by weighing the vanadium-titanium magnetite sample whose weight is M; 2) adding a sufficient amount of ore dissolving solution to be measured Vanadium-titanium-magnetite sample is heated and dissolved; 3) Add dilute hydrochloric acid in the reaction vessel; 4) Then dropwise add tin protochloride solution to light yellow, heat to slightly boiling again, then cool to room temperature; 5) Add to the reaction vessel Add sodium tungstate solution to the container, drop titanium trichloride solution to blue, and add dropwise titanium trichloride solution to a slight excess; 6) then drop potassium dichromate solution to colorless, and add diphenylamine sulfonate dropwise sodium acid indicator; 7) titrate to purple with potassium dichromate standard titration solution; 8) measure the weight percentage of vanadium in the solution after titration to purple; 9) calculate the steps. The method is simple in operation, fast in determination speed, and the test results are comparable to the national standard method, which can better meet the needs of on-site rapid analysis.

Description

technical field [0001] The invention belongs to the technical field of iron ore component analysis, and in particular relates to a rapid determination method for total iron content in vanadium-titanium magnetite. Background technique [0002] Vanadium-titanium magnetite is not only an important source of iron, but also associated with various components such as vanadium, titanium, chromium, cobalt, nickel, platinum group and scandium, which have important comprehensive utilization value. Total iron is an important indicator of the grade and quality of vanadium-titanium magnetite, so the content of total iron is one of the items that must be inspected in the trade and process application research of vanadium-titanium magnetite. [0003] At present, the determination method of total iron in vanadium-titanium magnetite is to separate the vanadium after alkali melting of the sample. This method has a long process and increases the analysis cost, which does not meet the requireme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N31/16G01N21/79
Inventor 闻向东邵梅周郑赖碧波陈士华张穗忠吴立新杨艳朱缨
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com