Bamboo fiber towel product prepared through modified adhesive

A bamboo fiber towel and adhesive technology, applied in the field of textiles, can solve the problems that the fineness and softness of bamboo fiber products need to be improved, affect the appearance and use, and the production steps are cumbersome, etc., to achieve high bonding strength, increase mildew resistance, and large attachment Focus on the effect

Active Publication Date: 2015-01-07
安吉登冠竹木开发有限公司
View PDF10 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Yet above-mentioned method production step is loaded down with trivial details, and processing time is long, and the fineness and softness of bamboo fiber product still need to be impr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo fiber towel product prepared through modified adhesive
  • Bamboo fiber towel product prepared through modified adhesive
  • Bamboo fiber towel product prepared through modified adhesive

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0057] Example one

[0058] Preparation of nano silver:

[0059] A. Add sodium dodecyl sulfonate solution, aqueous polyacrylate and hydrazine hydrate solution to the silver nitrate aqueous solution to obtain a mixed solution. The molar ratio of sodium dodecyl sulfonate to silver nitrate is 4:1; The molar ratio of acrylate to silver nitrate is 0.4:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.2:1;

[0060] B. Add dicyclohexane-18-crown-6 and sodium metaphosphate to the mixture. The molar ratio of dicyclohexane-18-crown-6 to silver nitrate is 3:1; sodium metaphosphate and nitric acid The molar ratio of silver is 0.8:1, and the pH value is controlled to be 8-9 to obtain nano-silver.

[0061] The composition ratio of the modified adhesive used in bamboo fiber products:

[0062] 25 parts of phthalic anhydride, 7 parts of furfuryl alcohol extracted from the core residue of corn cob, 10 parts of triethylene glycol, 15 parts of glutaric acid, 8 parts of butanetriol, 5 parts o...

Example Embodiment

[0090] Example two

[0091] Preparation of nano silver:

[0092] A. Add sodium dodecyl sulfonate solution, aqueous polyacrylate and hydrazine hydrate solution to the silver nitrate aqueous solution to obtain a mixed solution. The molar ratio of sodium dodecyl sulfonate to silver nitrate is 6:1; The molar ratio of acrylate to silver nitrate is 0.6:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.3:1;

[0093] B. Add dicyclohexane-18-crown-6 and sodium metaphosphate to the mixture. The molar ratio of dicyclohexane-18-crown-6 to silver nitrate is 5:1; sodium metaphosphate and nitric acid The molar ratio of silver is 1.3:1, and the pH is controlled to be 8-9 to obtain nano-silver.

[0094] The composition ratio of the modified adhesive used in bamboo fiber products:

[0095] 35 parts of phthalic anhydride, 11 parts of furfuryl alcohol extracted from oats or wheat bran, 12 parts of triethylene glycol, 18 parts of glutaric acid, 10 parts of butanetriol, 7 parts of zinc oxide p...

Example Embodiment

[0123] Example three

[0124] Preparation of nano silver:

[0125] A. Add sodium dodecyl sulfonate solution, aqueous polyacrylate and hydrazine hydrate solution to the silver nitrate aqueous solution to obtain a mixed solution. The molar ratio of sodium dodecyl sulfonate to silver nitrate is 5:1; The molar ratio of acrylate to silver nitrate is 0.5:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.25:1;

[0126] B. Add dicyclohexane-18-crown-6 and sodium metaphosphate to the mixture. The molar ratio of dicyclohexane-18-crown-6 to silver nitrate is 4:1; sodium metaphosphate and nitric acid The molar ratio of silver is 1:1, and the pH is controlled to be 8-9 to obtain nano-silver.

[0127] The composition ratio of the modified adhesive used in bamboo fiber products:

[0128] 30 parts of phthalic anhydride, 7-11 parts of furfuryl alcohol extracted from bamboo sawdust, 11 parts of triethylene glycol, 16 parts of glutaric acid, 9 parts of butanetriol, 6 parts of zinc oxide pow...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a textile, in particular to a bamboo fiber towel product prepared through a modified adhesive. The bamboo fiber towel product is manufactured by the following steps: bamboo fiber preparation; towel product preparation which comprises the steps of cloth turning, weft yarn cutting, head sewing, single-sided singeing, desizing, scouring, bleaching, mercerizing, dyeing, weft yarn finishing, adhesive dipping and tentering, wherein the adhesive dipping step comprises the steps of dipping fabric in the modified adhesive for 18-25 minutes and draining the adhesive for 5-8 minutes; the modified adhesive consists of the following raw materials in part by weight: phthalic anhydride, furfuryl alcohol, triethylene glycol, glutaric acid, butantriol, zinc oxide powder, magnesium oxide, chloroprene rubber, 70-95 parts of elastic rubber, 2-3 parts of softening oil, dimethyl carbonate, benzoyl peroxide, ethyl acetate, an emulsifier, 20-30 parts of flour, 5*10 <-5> to 9*10 <-5> parts of nanometer silver, flame retardant, 0.8-2.5 parts of a catalyst, 3-7 parts of a bamboo vinegar water solution and 6-13 parts of bamboo carbon powder with the grain diameter of 0.01-0.06mm; the elastic rubber comprises first elastic rubber and second elastic rubber which are mixed according to a weight ratio of (1-3):1. The bamboo fiber towel product prepared by the invention has great softness and anti-bacterial activity.

Description

technical field [0001] The invention relates to a textile, in particular to a bamboo fiber towel product prepared by modifying an adhesive. Background technique [0002] Bamboo fiber currently on the market has the following two classes: one is the regenerated fiber produced from bamboo pulp, commonly referred to as bamboo pulp fiber; the other is the fiber directly extracted from bamboo through a special process, called raw bamboo fiber. Because bamboo fiber has more superior properties in terms of hygroscopicity, air permeability, and spinnability, the study of spinnable bamboo fiber has obvious economic benefits and good social benefits. [0003] In recent years my country's original bamboo fiber manufacturing method has many invention patents, CN11078520C announced a kind of raw bamboo strips, rolling strips, the manufacture method of forming bamboo fiber bundle products, CN1261290C announced a kind of raw bamboo bamboo chip adopts pure physics The method is to separate ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/263D06M15/564D06M15/21D06M15/227D06M15/19D06M15/11D06M15/693D06M11/83D06M11/44D06M13/165D06M13/192D06M13/148D06M13/232D06M13/224D06M11/74D06M11/72D06M11/82A47K10/02D06M101/04
Inventor 曹小生
Owner 安吉登冠竹木开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap