Germicidal negative-radical waterproof coating and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A waterproof coating, root blocking technology, applied in antifouling/underwater coatings, polyester coatings, coatings, etc., can solve the problems of high cost, high cost, difficult to puncture, etc., and achieve enhanced hardness, wear resistance, resistance to High aging performance, good antibacterial and bactericidal effect
Inactive Publication Date: 2015-01-14
ANHUI LENCAQI BUILDING MATERIAL
View PDF7 Cites 10 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, general building waterproof materials are difficult to resist the puncture of plant roots.
At present, there are mainly root-blocking waterproofing membranes and root-blocking waterproof coatings on the market. Root-blocking waterproofing membranes mainly include composite copper-based modified asphalt waterproofing membranes. The root-blocking effect of this membrane is reliable, but the cost is also very expensive; The other is the metal base waterproof membrane. The defect of this type of material is that the base is located in the middle of the material, so that the metal base cannot be closed at the overlap of the coils, leaving a channel for the root system of the plant that can change the growth direction, so that the roots are blocked. The waterproof effect is invalid; another category is metal coiled materials, which are welded and seamed, and the effect is reliable, but the disadvantages are high cost and metal ions are poisonous to plant roots, which will cause deformed plant growth, and the production process of waterproof coiled materials is very difficult. Complex, high cost, high requirements for construction personnel, difficult to maintain and maintain later, so the scope of use is limited
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0012] specific implementation plan
[0013] The present invention will be described in detail below through specific examples.
[0014] A bactericidal root-blocking waterproof coating, made of the following raw materials in parts by weight (kg): dispersant EFKA40100.4, defoamer BYK-3900.1, defoamer BYK-0570.2, dodecylbenzenesulfonic acid 0.3, Silicone modified polyester resin 46, acrylic resin 13, hexamethoxymethyl melamine resin 7, rutile titanium dioxide 6, silica sol 4, methyl cellulose 0.4, palm wax 0.4, barium sulfate 4, mica powder 4, matting agent 1. Anti-scratch agent BYK-9800.4, S-1508, diacetone alcohol 4, butyl acetate 7, quizalofop-p-ethyl 0.6, root-blocking additive 6;
[0015] The nano root-blocking additive is made of the following raw materials in parts by weight (kg): root-blocking agent B24, petroleum pitch AH-8033, petroleum resin 14, gum rosin 5, nano-titanium dioxide 3, turpentine 12, ethyl acetate 7 , epoxy soybean oil 3, nano copper powder 7, calcin...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a germicidal negative-radical waterproof coating, which is characterized by being prepared from the following raw materials in parts by weight: 0.2-0.4 part of a dispersant EFKA4010, 0.1-0.2 part of a defoaming agent BYK-390, 0.2-0.3 part of a defoaming agent BYK-057, 0.1-0.3 part of a dodecylbenzene sulfonic acid, 40-50 parts of an organosilicone modified polyester resin, 10-15 parts of an acrylic resin, 6-8 parts of a hexamethoxymethyl melamine resin, 4-6 parts of rutile titania, 2-4 parts of silicon sol, 0.3-0.5 part of methyl cellulose, 0.3-0.5 part of palm wax, 3-6 parts of barium sulfate, 4-5 parts of mica powder, 1-2 parts of a matting agent, 0.2-0.4 part of an anti-scratch agent BYK-980, 7-9 parts of S-150, 3-5 parts of diacetone alcohol, 5-7 parts of butyl acetate, 0.5-1.0 part of quizalofop-p-ethyl, and 5-7 parts of a negative-radical additive. According to the coating disclosed by the invention, the added silicon sol is used for enhancing the hardness and wear resistance of a coated film, the added anti-scratch agent is used for improving the scratch resistance of the coated film, the added rutile titania achieves good bacteriostatic and germicidal effects and the like on the soil, and the added negative-radical additive has a good negative-radical effect and has no adverse effect on plants.
Description
technical field [0001] The invention relates to a coating and a preparation method thereof, in particular to a bactericidal and root-blocking waterproof coating and a preparation method thereof. Background technique [0002] Waterproof materials are widely used in the field of building material protection. After coating the building with waterproof coating, the building can be isolated from the external environment, thereby preventing the intrusion of rainwater, groundwater and other corrosive liquids and moisture in the air into the building. corrosion caused by building materials and prolong the service life of building materials. However, general building waterproof materials are difficult to resist the puncture of plant roots. At present, there are mainly root-blocking waterproofing membranes and root-blocking waterproof coatings on the market. Root-blocking waterproofing membranes mainly include composite copper-based modified asphalt waterproofing membranes. The root-...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.