Water-proof two-component polyurethane coating and preparation method thereof

A polyurethane coating, a two-component technology, applied in the direction of fireproof coatings, coatings, etc., can solve the problems of people's life and property threats, difficulty in fighting fires, etc.

Inactive Publication Date: 2015-06-03
JIANGSU XIN AN NEW MATERIALS TECH
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the early 1990s, the real estate industry and the furniture industry developed rapidly after the reform and opening up, and more and more wooden materials entered people's lives. However, due to bad living habits, such as children playing with fire, frequent fires in the home At the same time, due to the large number of people living in high-rise buildings and their heights, once a fire breaks out, it is difficult to extinguish it, especially when the disaster is serious, resulting in a serious threat to the lives and property of the broad masses of people.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] This embodiment provides a two-component water-resistant polyurethane coating, which comprises two components A and B mixed in equal proportions, and component A includes the following components in parts by mass:

[0041] 2,4-toluene diisocyanate: 30 parts, polypropylene carbonate diol with a molecular weight of 2660: 55 parts, 1,4-butanediol: 12 parts, ammonium polyphosphate: 9 parts, formaldehyde: 5 parts, acetone : 12 parts, cresyl diphenyl phosphate: 20 parts, melamine: 2 parts;

[0042] Component B includes the following components in parts by mass:

[0043] Modified polyamide curing agent: 30 parts, modified silane coupling agent: 70 parts;

[0044] Polypropylene carbonate glycol is the polypropylene carbonate glycol of 2660 molecular weight after purification, and the purification method concrete operation of polypropylene carbonate glycol is as follows:

[0045] Dehydrate the organic solvent with a 5A molecular sieve for 6 days for later use;

[0046] Ad...

Embodiment 2

[0054] This embodiment provides a two-component water-resistant polyurethane coating, which comprises two components A and B mixed in equal proportions, and component A includes the following components in parts by mass:

[0055] Hexamethylene diisocyanate: 40 parts, polypropylene carbonate diol with a molecular weight of 2660: 50 parts, 1,4 butanediol: 15 parts, dibutyltin dilaurate: 10 parts, formaldehyde: 8 parts, Ethanol: 15 parts, triphenyl phosphate: 25 parts, chlorinated paraffin: 3 parts;

[0056] Component B includes the following components in parts by mass:

[0057] Modified polyamide curing agent: 50 parts, modified silane coupling agent: 50 parts;

[0058] Polypropylene carbonate diol is polypropylene carbonate diol after purification, and the purification method concrete operation of polypropylene carbonate diol is as follows:

[0059] Dehydrate the organic solvent with 5A molecular sieves for 7 days for later use;

[0060] Add polypropylene carbonate diol...

Embodiment 3

[0068] This embodiment provides a two-component water-resistant polyurethane coating, which comprises two components A and B mixed in equal proportions, and component A includes the following components in parts by mass:

[0069] Isophorone diisocyanate: 35 parts, polypropylene carbonate diol with a molecular weight of 2660: 40 parts, 1,4 butanediol: 10 parts, melamine phosphate: 8 parts, formaldehyde: 6 parts, N-formaldehyde Base pyrrolidone: 10 parts, triphenyl phosphate: 22 parts, chlorinated paraffin: 2 parts;

[0070] Component B includes the following components in parts by mass:

[0071] Modified polyamide curing agent: 30 parts, modified silane coupling agent: 40 parts;

[0072] Polypropylene carbonate diol is polypropylene carbonate diol after purification, and the purification method concrete operation of polypropylene carbonate diol is as follows:

[0073] Dehydrate the organic solvent with 5A molecular sieves for 5 days for later use;

[0074] Add polypropyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-proof two-component polyurethane coating. The polyurethane coating comprises a component A and a component B mixed in the equal ratio, wherein the component A comprises components as follows: diisocyanate, poly propylene carbonate diol, a micromolecule chain extender, a catalyst, a catalyst capturing agent, an organic solvent, a flame retardant and a foaming agent; the component B comprises components as follows: a curing agent and a coupling agent. The invention further designs a preparation method of the water-proof two-component polyurethane coating. The preparation method of the coating is simple and easy to operate, the cost is low, and the prepared coating is good in corrosion resistance, excellent in electrical performance, good in decoration and protection performance and good in temperature resistance.

Description

technical field [0001] The invention relates to a fireproof coating and a preparation method thereof, in particular to a two-component water-resistant polyurethane coating and a preparation method thereof, belonging to the field of fireproof materials. Background technique [0002] In the early 1990s, the real estate industry and the furniture industry developed rapidly after the reform and opening up, and more and more wooden materials entered people's lives. However, due to bad living habits, such as children playing with fire, frequent fires in the home Occurs, simultaneously because the quantity of high-rise building occupant is more and reasons such as its height, once break out of fire, especially when disaster situation is serious, be difficult to fight, cause the lives and properties of broad masses of people to be seriously threatened. Therefore, we need to take a lot of safety measures to improve the fire performance of buildings, household combustibles, etc., to e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/06C09D5/18C09D7/12C08G18/66C08G18/44C08G18/32
Inventor 张望杨松林
Owner JIANGSU XIN AN NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com