Method for filling and synthetizing full waterborne polyurethane base leather through nano attapulgite
A polyurethane leather bass and nano attapulgite technology, applied in textiles and papermaking, etc., can solve the problems of insufficient nano reinforcement performance, low production efficiency, dispersion and dissociation, etc., and achieve easy mass production and stable performance. , Good thickening effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0018] Example 1: Using non-woven fabric as the base fabric, impregnating it in 15wt% NaCl aqueous solution, the liquid rate of the base fabric after impregnation is 35wt%, and the coating amount is 800g / m 3 ; Dry and iron the impregnated base cloth, and then calender the surface; 15 grams of attapulgite content of 45wt%, montmorillonite content of 40wt% montmorillonite attapulgite crushed to more than 200 mesh, add 100wt% water infiltration for 24h , Squeeze on the roller 5 times, after aging for 12 hours, add 100 grams of anionic waterborne polyurethane 8000rpm high-speed pre-dispersion for 30min, then add 7 grams of sodium stearate, 4 grams of amine stearate, 4 grams of water-based pigment paste at 6000rpm high speed Stir for 20 minutes to prepare a water-based polyurethane synthetic leather slurry; immerse the pretreated base fabric in the water-based polyurethane synthetic leather slurry, scrape the surface, and dry to prepare a water-based polyurethane synthetic leather bas...
Example Embodiment
[0019] Example 2: Using non-woven fabric as the base fabric, impregnating it in 5wt% NaCl aqueous solution, the liquid rate of the base fabric after impregnation is 15wt%, and the coating amount is 400g / m 3 ; Dry and iron the impregnated base cloth, and then calender the surface; 12 grams of dolomite attapulgite with 25wt% attapulgite content and 60wt% dolomite content is crushed to more than 250 meshes, and 50wt% water is added to infiltrate for 12h. Roll squeeze 3 times, after aging for 4h, add 100g of anionic waterborne polyurethane at 10000rpm high speed pre-dispersing for 30min, then add 3g of sodium dodecylbenzene sulfonate, 2g of amine stearate, 1g of water-based pigment paste Stir at a high speed at 8000 rpm for 20 minutes to prepare a water-based polyurethane synthetic leather slurry; immerse the pre-treated base fabric in the water-based polyurethane synthetic leather slurry, scrape the surface, and dry to prepare a water-based polyurethane synthetic leather bass.
Example Embodiment
[0020] Example 3: Use non-woven fabric as the base fabric and impregnate it in a 10wt% NaCl aqueous solution. The liquid rate of the base fabric after impregnation is 25wt%, and the coating amount is 600g / m 3 ; Dry and iron the impregnated base cloth, and then calender the surface; 8 grams of high-viscosity attapulgite with 70wt% attapulgite content is crushed to more than 300 mesh, add 75wt% water to soak for 18h, and squeeze the roller 4 times After aging for 8 hours, add 100 grams of anionic water-based polyurethane pre-dispersed at 8000 rpm for 30 minutes, and then add 5 grams of sodium stearate, 3 grams of sodium succinate, and 2.5 grams of water-based pigment paste. Stir at 6000 rpm for 20 minutes to make water-based polyurethane synthetic leather. Slurry: The pretreated base cloth is immersed in the water-based polyurethane synthetic leather slurry, the surface is leveled, and dried to prepare the water-based polyurethane synthetic leather bass.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap