Water-based aluminum powder pigment, and preparation method and application thereof

An aluminum powder and pigment technology, applied in the field of surface treatment of metallic pigments, can solve the problems of aluminum powder pigments losing metallic luster, difficult to disperse aluminum powder pigments, agglomeration of aluminum powder pigments, etc., and achieve excellent storage stability and good compatibility. good dispersion effect

Active Publication Date: 2015-08-05
CHANGDE JINPENG PRINTING
View PDF12 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order for aluminum powder pigments to be used in water-based media (weak acid or weak alkali), the first problem that needs to be solved is: aluminum powder is easily corroded and reacts with the medium, which not only makes the aluminum powder pigment lose its metallic luster, but also produces Hydrogen, there is a danger of explosion; the second problem that needs to be solved is: aluminum powder pigments are difficult to disperse in water-based resins, and the compatibility between the two is poor, resulting in agglomeration of aluminum powder pigments and a decrease in gloss, which is not conducive to subsequent use
This method belongs to the in-situ polymerization method, the research and development of aluminum pigment surface modification and anticorrosion technology, the Chinese Journal of Corrosion and Protection, Volume 34, Issue 5 mentioned that in this method, the adsorption driving force of the initiator ammonium persulfate on the aluminum surface It is not chemical bonding, but electrostatic attraction, which is easier to fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based aluminum powder pigment, and preparation method and application thereof
  • Water-based aluminum powder pigment, and preparation method and application thereof
  • Water-based aluminum powder pigment, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] Step 1: Add 1 part of aluminum powder coated with silica and 30 parts of toluene to the reactor in terms of parts by mass (the same as the following), add 0.01 part of 4 , 4'-Azo (4-cyanovaleric acid (3'-dimethylchlorosilane) propyl ester) and 0.1 part of triethylamine, stirred at room temperature for 12 hours, then washed with ethanol, filtered to obtain coating modification Aluminum powder paint.

[0059] The second step: Add 1 part of coated modified aluminum powder pigment, 30 parts of methanol and 0.5 part of acrylic acid into the reactor, deoxygenate the reactor under liquid nitrogen conditions, then react in a water bath at 60 ° C for 3 hours, filter, After washing and drying, the water-based aluminum powder pigment is obtained.

[0060] The corrosion resistance of the water-based aluminum powder pigment of the present embodiment 1: there is no hydrogen gas precipitation in the aqueous solution in the pH8-12 range for 6 months.

[0061] Glossiness of the wa...

Embodiment 2

[0065] The first step: in parts by mass, add 1 part of aluminum powder coated with silica and 30 parts of toluene into the reactor, stir with nitrogen at room temperature; add 0.02 parts of 4,4'-azo ( 4-cyanovaleric acid (3'-dimethylchlorosilane) propyl ester) and 0.2 parts of triethylamine, stirred at room temperature for 12 hours; then washed with isopropanol, filtered to obtain coated modified aluminum powder pigment.

[0066] The second step: Add 1 part of coated modified aluminum powder pigment, 30 parts of methanol and 1 part of methyl acrylate into the reactor; deoxygenate the reactor under liquid nitrogen conditions, and then react in a water bath at 70 ° C for 3 hours; After filtering, washing and drying, the water-based aluminum powder pigment is obtained.

[0067] The corrosion resistance of the water-based aluminum powder pigment of the present embodiment 2: no hydrogen gas is separated out in 6 months in the aqueous solution in the range of pH8-12.

[0068] G...

Embodiment 3

[0071] The first step: in parts by mass, add 2 parts of aluminum powder coated with silica and 40 parts of toluene into the reactor, and stir with nitrogen at room temperature; add 0.05 parts of 4,4'-azo ( 4-cyanovaleric acid (3'-dimethylchlorosilane) propyl ester) and 0.2 parts of triethylamine, stirred and reacted at room temperature for 20 hours; then washed with methanol, filtered to obtain coated modified aluminum powder pigment.

[0072] The second step: add 2 parts of coated modified aluminum powder pigments, 40 parts of methanol and 1 part of methyl methacrylate into the reactor; deoxygenate the reactor under liquid nitrogen conditions, and then react in a water bath at 60 °C for 3 hours; filtered, washed, and dried to obtain water-based aluminum powder pigments.

[0073] The corrosion resistance of the water-based aluminum powder pigment of the present embodiment 3: there is no hydrogen gas precipitation in the aqueous solution in the pH8-12 range for 6 months. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a water-based aluminum powder pigment, and a preparation method and application thereof. The surface coating of the water-based aluminum powder pigment is silicon dioxide, the inside is aluminum powder, the outside of the surface coating is provided with connection points connected through chemical bonds, and each connection point is connected with a polymer. The connection point is 4,4'-azo(propyl 4-cyano(3'-dimethylchlorosilane)valerate), 4-azoisobutylcyano4-cyano(propyl (3'-dimethylchlorosilane)valerate) or azoisobutyldicyanophenyl(3-ethyldimethylchlorosilane), and the polymer is prepared by carrying out polymerization reaction on a polymerizable monomer. The initiator and polymer are firmly fixed to the silicon dioxide surface, and thus, have favorable protective effects on the inside aluminum powder. The water-based aluminum powder pigment has favorable dispersity in water-based paints and inks.

Description

technical field [0001] The invention relates to the technical field of surface treatment of metal pigments, in particular to a water-based aluminum powder pigment, a preparation method and an application. Background technique [0002] Aluminum powder pigment is one of the most common metallic pigments, and is favored by designers for its unique sparkle, covering and decorative effects. Its consumption has grown rapidly since the last century, and in recent decades it has developed towards high added value and water-phase adaptability. The main application areas are industrial coatings, automotive coatings, decoration, printing inks, plastic processing, etc. [0003] Traditional aluminum powder pigments are all solvent-based aluminum powders, and the solvent-based products formulated with them contain relatively high organic volatiles, are difficult to clean, and are harmful to the environment and human body. With the continuous development of science and technology, peopl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/64C09C3/06C09C3/10C09C3/12C09C3/08C09D17/00
Inventor 孔繁辉黎厚斌徐军何宇航刘兴海欧立国王超
Owner CHANGDE JINPENG PRINTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com