Oil resistant, high and low temperature resistant ethylene propylene diene monomer rubber/polyurethane rubber cable material

A technology of EPDM rubber and polyurethane rubber, which is applied in the direction of rubber insulators and organic insulators, can solve the problems of high and low temperature resistance and oil resistance that cannot meet the requirements, and achieve improved hardness, long service life and high mechanical strength. Effect

Inactive Publication Date: 2015-12-02
繁昌县菲德通讯材料设计有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The high and low temperature resistance and oil resistance of the existing EPDM cable materials cannot meet the requirements, which limits its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The oil-resistant, high and low-temperature resistant EPDM rubber / polyurethane rubber cable material of the present invention, its raw materials include the following components by weight: 45 parts of EPDM rubber, 40 parts of polyurethane rubber, 15 parts of ethylene acrylate, ternary acrylate 3 parts of ethylene propylene rubber grafted maleic anhydride, 15 parts of carbon black, 5 parts of clay, 7 parts of coumarone resin, 1 part of zinc oxide, 1.5 parts of stearic acid, 1 part of magnesium oxide, 6 parts of zinc methacrylate, 1 part of benzoyl peroxide, 0.3 part of thiocyanic acid, 0.6 part of trimethylolpropane trimethacrylate, 0.1 part of accelerator M, 0.8 part of accelerator DZ, 0.8 part of anti-aging agent, hexamethylene glycol 1.2 parts of acid dibasic higher carbon alcohol ester, 0.3 part of diethylene glycol dibenzoate, 1.5 parts of epoxidized soybean oil, and 0.1 part of N-(morpholinethio)phthalimide.

Embodiment 2

[0017] The oil-resistant, high and low-temperature resistant EPDM rubber / polyurethane rubber cable material of the present invention, its raw materials include the following components by weight: 60 parts of EPDM rubber, 30 parts of polyurethane rubber, 10 parts of ethylene acrylate, ternary acrylate 10 parts of ethylene propylene rubber grafted maleic anhydride, 5 parts of carbon black, 20 parts of clay, 2 parts of coumarone resin, 2.5 parts of zinc oxide, 0.5 parts of stearic acid, 5 parts of magnesium oxide, 2 parts of zinc methacrylate, 0.2 parts of benzoyl peroxide, 1.0 parts of thiocyanic acid, 0.2 parts of trimethylolpropane trimethacrylate, 0.5 parts of accelerator M, 0.3 parts of accelerator DZ, 2 parts of anti-aging agent AW, adipic di 0.5 parts of acid dibasic higher carbon alcohol ester, 1.2 parts of diethylene glycol dibenzoate, 0.3 parts of epoxy soybean oil, and 0.3 parts of N-(morpholinethio) phthalimide.

Embodiment 3

[0019]The oil-resistant, high and low-temperature resistant EPDM rubber / polyurethane rubber cable material of the present invention, its raw materials include the following components by weight: 50 parts of EPDM rubber, 37 parts of polyurethane rubber, 14 parts of ethylene acrylate, ternary acrylate Ethylene-propylene rubber grafted maleic anhydride 7 parts, carbon black 10 parts, clay 16 parts, coumarone resin 3.5 parts, zinc oxide 2.1 parts, stearic acid 0.8 parts, magnesium oxide 3.5 parts, zinc methacrylate 4.3 parts, 0.6 parts of benzoyl peroxide, 0.4 parts of thiocyanuric acid, 0.45 parts of trimethylolpropane trimethacrylate, 0.28 parts of accelerator M, 0.57 parts of accelerator DZ, 40300.6 parts of anti-aging agent, anti-aging agent 0.5 parts of MB, 1.1 parts of dihydric higher alcohol adipate, 0.7 parts of diethylene glycol dibenzoate, 1.2 parts of epoxidized soybean oil, and 0.2 parts of N-(morpholinethio)phthalimide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an oil resistant, high and low temperature resistant ethylene propylene diene monomer / polyurethane rubber bable material. The raw material comprises the following components: ethylene propylene diene monomer rubber, polyurethane rubber, ethylene acrylate, EPDM rubber grafted with maleic anhydride, carbon black, pottery clay, coumarone resin, zinc oxide, stearate, magnesia, zinc methacrylate, benzoyl peroxide, trimerization thiocyanate, trimethylol propane trimethacrylate, accelerator M, accelerant DZ, antioxidant, dihydroxy higher alcohol, diethylene glycol dibenzoate, epoxidized soybean oil and N-(morpholine thiosulfate) phthalimide. The oil resistant, high and low temperature resistant ethylene propylene diene monomer / polyurethane rubber bable material disclosed by the invention is high in mechanical strength, excellent in oil resistance, high in temperature resistance and cold tolerance; and the cable made from the material is long in service life, so that the cost can be reduced.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to an oil-resistant, high-low temperature resistant EPDM / polyurethane rubber cable material. Background technique [0002] EPDM rubber has excellent weather resistance, ozone resistance, heat resistance, acid and alkali resistance, water vapor resistance, color stability, electrical properties, oil filling and excellent processing properties, and is widely used in the cable industry. With the development of society, people have put forward higher requirements on the performance of cables. In addition, the use environment of cable materials is often complex and changeable, especially in winter in northern regions, where the temperature difference between day and night is large, and cable materials are required to have high and low temperature resistance. The high and low temperature resistance and oil resistance of the existing EPDM cable materials cannot meet the requirement...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L75/04C08L23/08C08L51/04C08L91/00C08L45/02C08K13/02C08K3/22C08K5/098C08K5/14C08K5/3492C08K5/103C08K5/11C08K5/12H01B3/28
CPCC08L23/16C08L2201/08C08L2203/202C08L2205/035C08L2205/08H01B3/28C08L75/04C08L23/0869C08L51/04C08L91/00C08L45/02C08K13/02C08K2003/222C08K5/098C08K5/14C08K5/3492C08K5/103C08K5/11C08K5/12C08L51/003
Inventor 刘菲
Owner 繁昌县菲德通讯材料设计有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com