Castable for branch iron trough of 1,250 m<3> blast furnace

A technology of castables and supporting iron channels, which is applied in the field of metallurgical refractory materials, can solve the problems of stable and safe production of blast furnaces, high viscosity of binders, thermal spalling structures, etc., and achieve enhanced high temperature strength and various properties, thermal shock stability Good performance, increase the effect of wetting angle

Inactive Publication Date: 2015-12-30
万燕杰
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of castable with brown corundum as the main component has poor thermal shock resistance, and it is easy to cause thermal spalling and structural spalling, which greatly increases the frequency of repairing the support iron ditch and brings great hidden dangers to the stable and safe production of the blast furnace. In addition, As a binder, sol has high viscosity, is not easy to construct, and has high cost, so it still needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Castable for branch iron trough of 1,250 m&lt;3&gt; blast furnace

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Use formula 1 to prepare blast furnace support iron channel: mix ingredients according to formula 1 and stir in a mixer, then add 3-8% of the above-mentioned total amount of clean water, stir evenly, and pour it into the mold installed in the support iron channel through which molten iron flows. Add castables, and natural curing for 1 hour to demould the blast furnace support iron ditch.

Embodiment 2

[0022] Use formula 2 to prepare the blast furnace support iron channel: mix the ingredients according to formula 2 and stir in the mixer, then add the above-mentioned total amount of 3-8% of clean water, stir evenly, and pour it into the mold installed in the support iron channel where the molten iron flows. Add castables, and natural curing for 1 hour to demould the blast furnace support iron ditch.

Embodiment 3

[0024] Use formula 3 to prepare blast furnace support iron channel: mix ingredients according to formula 3 and stir in a mixer, then add 3-8% of the above-mentioned total amount of clean water, stir evenly, and pour it into the mold installed in the support iron channel through which molten iron flows. Add castables, and natural curing for 1 hour to demould the blast furnace support iron ditch.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a castable for a branch iron trough of a 1,250 m<3> blast furnace. The castable comprises a main material and an admixture, wherein the main material comprises components in parts by weight as follows: 5-8 parts of 8-5-mm aluminum silicate, 15-20 parts of 5-3-mm chromium nitride, 10-15 parts of 3-1-mm sillimanite, 8-15 parts of 1-0-mm calcium chromite, 2-5 parts of meta-clay powder, 3-7 parts of cobalt oxide aluminum powder, 5-10 parts of cutting powder, 3-8 parts of amorphous graphite powder, 1-2 parts of composite carbon powder, 0-3 parts of molybdenum trioxide powder, 3-5 parts of alumina micro-powder, 1-5 parts of magnesium oxide iron powder, 1-3 parts of rho alumina and 0-5 parts of fused pure calcium aluminate cement; in terms of the total parts by weight of the main material being 100%, the admixture comprises 0.1-0.2 parts by weight of calcium lignosulphonate, 0.01-0.05 parts by weight of nano dried potato powder, 0.01 parts by weight of malic acid and 0.1 parts by weight of C12H14N4O5S2. The blast furnace iron trough prepared from the castable has the characteristics of good thermal shock resistance, good erosion resistance, high iron flux and long service life.

Description

technical field [0001] The invention relates to a castable for a 1250m3 blast furnace support channel, which belongs to the field of refractory materials for metallurgy. Background technique [0002] Most of the existing iron channel castables are Al2O3-SiC-C castables, but ordinary Al2O3-SiC-C iron channel castables are used in blast furnaces, and the amount of iron passing through them at one time is about 120,000 tons. With the strengthening of smelting, the demand for increasing the output of molten iron is becoming more and more prominent, and the need for a large amount of iron to be passed through the iron channel at one time is also becoming more and more urgent. However, due to the poor corrosion resistance and thermal shock resistance of the iron channel at present, thermal spalling has occurred. And structural spalling is an important reason for the short life of the support iron ditch. [0003] CN102101782A discloses a casting material for iron trench, which is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 万燕杰
Owner 万燕杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com