Biomass resin and preparation method of fibre oriented shaving composite board

A biomass and plant cellulose technology, applied in the direction of manufacturing tools, flat products, and other household appliances, can solve the problems of low solid content, high viscosity, hindering the application of biomass adhesives, etc., to improve the solid content, physical High mechanical properties and the effect of improving the secondary bonding performance

Active Publication Date: 2016-03-02
郑州佰沃科技发展有限公司
View PDF4 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to its low solid content and high viscosity, the application of biom

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biomass resin and preparation method of fibre oriented shaving composite board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] The biomass resin of the present invention is expressed in parts by weight, and the raw materials are composed of: 100 parts of water, 0.26 parts of disodium hydrogen citrate, 1.48 parts of trisodium citrate, 0.1 part of seaweed gum, 0.2 part of guar gum, and 35 parts of defatted soybean powder. parts, 0.02 parts of Aspergillus niger protease preparation, 8 parts of potato starch, 5 parts of corn fiber powder, 0.03 parts of α-amylase, 0.01 part of cellulase, 0.2 parts of acetic anhydride, 0.5 parts of vinyltriethoxysilane, p-phenylene 0.05 part of diphenol, 0.02 part of nano silicon dioxide, 0.02 part of emulsified silicone oil, 0.1 part of isothiazolinone and 5 parts of magnesium oxide.

Embodiment 2

[0049] The preparation method of the biomass resin of embodiment 1 of the present invention, detailed steps are as follows:

[0050] (1) First, weigh various raw materials according to the ratio of the biomass resin described in Example 1;

[0051] (2) Add the weighed composite stabilizer into water to prepare an aqueous solution;

[0052] (3) Add the weighed vegetable protein powder to the solution obtained in step (2), and adjust the pH value to 7;

[0053] (4) Add the weighed protease preparation to the solution obtained in step (3), and react at 40°C for 200 minutes; when the viscosity of the system reaches 800-1200mPa.s, raise the temperature to 75°C and keep it warm for 18 minutes;

[0054] (5) Add the weighed plant starch and modified plant cellulose powder to the reaction solution obtained in step (4), cool down to 50°C, then add the weighed compound enzyme preparation, react for 70min; heat up to 75°C, and keep warm for 20min ;

[0055] (6) Cool down the reaction s...

Embodiment 3

[0058] The biomass resin of the present invention is expressed in parts by weight, and the raw materials are composed of: 100 parts of water, 0.4 part of ferrous sulfate, 0.1 part of sodium silicate, 0.5 part of polyvinyl alcohol, 0.01 part of sodium polyacrylate, 50 parts of defatted peanut powder, and 0.05 parts of protease preparation, 6 parts of corn starch, 3 parts of cotton fiber powder, 0.01 part of α-amylase, 0.01 part of β-amylase, 0.01 part of hemicellulase, 0.4 part of succinic anhydride, 0.2 part of diethylenetriamine, cyclo 0.2 parts of oxychloropropane, 3 parts of glycerin, 0.01 parts of dimethyl polyoxyalkylene, 0.05 parts of potassium sorbate, 0.05 parts of sodium propionate and 6 parts of clay.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses biomass resin and a method for preparing a fibre oriented shaving composite board by using the biomass resin as an adhesive. The biomass resin is prepared from, by weight, 100 parts of water, 1-3.5 parts of a compound stabilizer, 5-50 parts of vegetable protein powder, 0.01-0.05 part of a protease additive, 2-10 parts of plant starch, 1-7 parts of modified plant cellulose powder, 0.01-0.05 part of a complex enzyme preparation, 0.1-5 parts of a molecular structure acylation modifier, 0.1-0.5 part of a cross-linking agent, 0.01-10 parts of a resin additive, 0.01-0.05 part of an antifoaming agent, 0.1-0.5 part of a preservative and 5-10 parts of a filler. In addition, the biomass resin is used as an adhesive to be applied in a preparation technology of a fibre oriented shaving composite board. Viscosity is reduced, solid content is raised, and secondary gluing performance after drying of the adhesive is enhanced.

Description

technical field [0001] The invention belongs to the technical field of wood-based panel processing, and in particular relates to a biomass resin and a method for preparing a fiber-oriented strand composite board by using the biomass resin as an adhesive. Background technique [0002] At present, the world's forest resources are increasingly scarce, resulting in a shortage of timber market. The raw materials of my country's timber market have changed from natural forest resources to artificial forest timber, bamboo timber, crop straw and timber processing residues. It not only reduces the logging of forest resources, but also reduces environmental pollution. These woody material resources have the characteristics of scattered sources, difficult collection, small diameter class, and low stacking density. These characteristics determine that in the future, the wood industry will adopt a supply mode in which raw materials are processed into semi-finished products and then tran...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L89/00C08L3/02C08L97/02C08L83/04C08K13/02C08K5/098C08K5/5425C08K5/13C08K3/36B27N3/00B27N3/02B27N3/08B27N1/02
CPCB27N1/0263B27N3/002B27N3/02B27N3/08C08K2201/003C08K2201/011C08K2201/014C08L89/00C08L2205/025C08L2205/035C08L2205/16C08L3/02C08L97/02C08L83/04C08K13/02C08K5/098C08K5/5425C08K5/13C08K3/36
Inventor 陈锡建杨立新成宇陶杰曹新华张晓亚吴军强赵巧义
Owner 郑州佰沃科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap