Functional reconstituted lumber

A restructured and functional technology, applied in wood treatment, wood impregnation, impregnation of wood, etc., can solve the problems of interfering with dyeing agent, color development and dyeing veneer interface gluing, poor compatibility of water-based adhesives, environmental pollution in the bleaching and dyeing process, etc. Low formaldehyde and VOC emission, good compatibility and good penetration

Active Publication Date: 2016-06-29
DEHUA TB NEW DECORATION MATERIAL CO LTD
View PDF11 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN103171014B (2015-4-15) discloses a preparation method of scientific and technological wood, but the formaldehyde emission of the technological wood is high, the dyeing agent is difficult to penetrate, easy to lose, not weather-resistant, poor compatibility with water-based adhesives, and environmental pollution in the bleaching and dyeing process More serious; because the flame retardant seriously interferes with the color development of the dye and the interface gluing of the dyed veneer, this technical wood has not been treated with flame retardant, and its functionality needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Functional reconstituted lumber
  • Functional reconstituted lumber
  • Functional reconstituted lumber

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0075] The preparation method of β-cyclodextrin peppermint oil micropowder is as follows: at 20°C, mix β-cyclodextrin and peppermint oil at a mass ratio of 8:65, and peppermint oil is embedded in the cavity of β-cyclodextrin in the form of molecules , forming β-cyclodextrin peppermint oil micropowder in clathrate form;

[0076] The extraction method of bamboo leaf flavonoids is as follows: select the dry leaves of the lower part of the bamboo that is more than six years old in Moganshan, Deqing, and grind them into 0.5mm bamboo leaf fine powder; Add 75wt% methanol solution to dissolve and filter, and take the filtrate as the liquid to be separated by column chromatography.

[0077] Three-component compound solution formula two

[0078] It is composed of biomass nanofiber solubilizer, flame retardant and acidic disazo dye compound solution according to the mass ratio of 1:40:100;

[0079] The configuration of biomass nanofiber solubilizer: by weight, 1 part of bamboo leaf f...

Embodiment 1

[0088] The preparation method of modified MUF adhesive is:

[0089] A. 100 parts of formaldehyde aqueous solution, 0.1 part and 0.3 part of amino-terminated hyperbranched polymer PAMAM whose mass concentration is 36.5wt% are 100 parts by weight, and 0.3 part of amino-terminated hyperbranched polymer PAMAM is put into the reactor, and the stirring is started; The active substance is sodium hydroxide, potassium hydroxide, calcium hydroxide, barium hydroxide or ammonia water;

[0090] B. Add 1 part of hexachlorocyclotriphosphazene, heat up to 50°C, and when the temperature rises to 75°C by itself, add 35 parts of melamine, continue to heat up to 90°C, and react to obtain a preliminary polycondensate;

[0091] C. Add 40 parts of melamine to the above-mentioned preliminary polycondensate, and add 0.6 part of p-toluenesulfonamide to obtain the second polycondensate;

[0092] D. Add 20 parts of urea when the temperature of the second polycondensation product is lowered to 70°C, cont...

Embodiment 2

[0094] The preparation method of modified MUF adhesive is:

[0095] A. 100 parts of formaldehyde aqueous solution, 0.5 part and 0.6 part of amino-terminated hyperbranched polymer PAMAM whose mass concentration is 50wt% are 100 parts in formaldehyde aqueous solution and 0.6 part of amino-terminated hyperbranched polymer PAMAM by weight, and the mass concentration is put into the reactor, and the stirring is started; The active substance is sodium hydroxide, potassium hydroxide, calcium hydroxide, barium hydroxide or ammonia water;

[0096] B. Add 1 part of hexachlorocyclotriphosphazene, heat up to 55°C, and when the temperature rises to 85°C, add 55 parts of melamine, continue to heat up to 95°C, and react to obtain a preliminary polycondensate;

[0097] C. Add 45 parts of melamine in the above-mentioned preliminary polycondensate, and add 0.9 part of p-toluenesulfonamide to obtain the second polycondensate;

[0098] D. Add 30 parts of urea when the temperature of the second p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a furniture panel, particularly to functional reconstituted lumber. A manufacturing technology of the functional reconstituted lumber comprises the steps of preparing blank veneers through rotary cutting or slicing, and shearing the blank veneers into a required size, so as to obtain A veneers; soaking the A veneers in a ternary compound solution composed of a biomass nanocellulose solubilizer, a fire retardant and an acid dye for toughening, inflaming retarding and dyeing treatment, so as to obtain B veneers; adding a formaldehyde decomposition powder into a modified MUF adhesive, uniformly stirring, and dispensing on the B veneers, so as to obtain C veneers; assembling the C veneers, and carrying out cold pressing treatment, so as to obtain D square lumber; and carrying out compound hot pressing on the D square lumber with a transparent abrasion-resistant surface film adhesive paper layer, wherein the transparent abrasion-resistant surface film adhesive paper layer is a film adhesive paper layer formed through soaking transparent abrasion-resistant surface paper in an amino-formaldehyde resin adhesive solution containing tourmaline powder and Al2O3; the particle size of tourmaline negative ion powder is 500 meshes or above; and the count capacity of negative ions in the Giger. Miller zone is 3000 ions / cc or above. According to the functional reconstituted lumber, the effect that the lumber has multiple functions in a reconstituted decorative lumber manufacturing technology is achieved.

Description

technical field [0001] The invention relates to a furniture board, in particular to a functional recombined board. Background technique [0002] As the problem of global warming becomes increasingly prominent and extreme weather occurs frequently, the low-carbon economy with the theme of "low emissions, low pollution, and low energy consumption" is increasingly recognized and respected by people. Under such background conditions, the wood industry is playing an increasingly important role in developing a low-carbon economy and coping with climate change by taking advantage of its inherent "green", "environmental protection" and "clean" characteristics. Wood and wood products have a good carbon sequestration effect. As long as it does not rot or burn, the carbon sequestration function of wood and wood products will continue for a long time and stably. Some carbon fixation time can reach decades, hundreds of years. Therefore, increasing the use of wood and prolonging the se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27D1/08B27K3/02B27K5/02B27K3/52B27M1/06B32B37/06B32B37/10B32B37/12C07D311/30C07D311/40C08G12/40
CPCB27D1/08B27K3/02B27K3/52B27K5/02B27K2240/30B27M1/06B32B37/06B32B37/10B32B37/12C07D311/30C07D311/40C08G12/40
Inventor 杨勇李延军韩景泉黄超伯詹先旭沈金祥卓艳彭国青
Owner DEHUA TB NEW DECORATION MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com