High-strength antibacterial plastic and preparation method thereof

An antibacterial plastic, high-strength technology, used in the field of plastics

Inactive Publication Date: 2016-08-17
ANHUI YUEERWEI PLASTIC MACHINE CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, plastics are often made into containers to hold objects, and after the objects are placed in plastic containers for a long time, mildew or a large number of bacteria will often occur at the contact between the objects and the container, thereby accelerating the corruption of the stored objects, especially is when the object is food

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0013] The invention provides a kind of preparation method of high-strength antibacterial plastic, and this preparation method comprises:

[0014] 1) Mixing silicon dioxide, asbestos, kaolin, zinc borate, Chinese herbal medicine and water, decocting, and then filtering to take the filter cake to obtain antibacterial activators;

[0015] 2) Polyvinyl chloride, ethylene-ethyl acrylate copolymer, polyimide, tris (2,4-di-tert-butylphenyl) phosphite, sodium lauramide ethyl sulfate, carbon nanotubes, zirconium phosphate , bamboo leaf ketone, wollastonite fiber, vinyltrimethoxysilane and antibacterial activator are mixed, and then processed to make high-strength antibacterial plastic;

[0016] Among them, the Chinese herbal medicine contains seabuckthorn, shangzhi, haoben, nanxing, bupleurum, chuanbai, guanzhong, Tianzhugen, Wujiapi, schisandra, jiuliming, licorice festival, and saxoid.

[0017] In step 1) of the present invention, the consumption of each material can be selected in...

Embodiment 1

[0027] 1) Silica, asbestos, kaolin, zinc borate, seabuckthorn, Shangzhi, haoben, southern star, Bupleurum, Chuanbai, Guanzhong, Tianzhu root, Wujiapi, Schisandra, Jiuliming, Licorice Festival, Maqian Seedlings and water are mixed according to the ratio of 100:68:19:14:19:15:19:27:34:26:13:39:20:24:16:34:12:600 and decocted at 150°C for 30 hours. Then filter to get the filter cake to make the antibacterial active substance;

[0028] 2) Polyvinyl chloride (weight average molecular weight is 6000), ethylene-ethyl acrylate copolymer (weight average molecular weight is 10000), polyimide (weight average molecular weight is 5000), three (2,4-di-tert-butyl phenyl) phosphite, sodium lauramide ethyl sulfate, carbon nanotubes, zirconium phosphate, bamboo leaf ketone, wollastonite fiber, vinyltrimethoxysilane and antibacterial active substances according to the ratio of 100:90:56:10 : 24: 8: 17: 19: 17: 80: 49 Mixed at 200° C. for 5 hours, and then extruded (die temperature: 193° C.) to ...

Embodiment 2

[0030] 1) Silica, asbestos, kaolin, zinc borate, seabuckthorn, Shangzhi, haoben, southern star, Bupleurum, Chuanbai, Guanzhong, Tianzhu root, Wujiapi, Schisandra, Jiuliming, Licorice Festival, Maqian Mix seeds and water according to 100:50:17:9:14:10:17:25:23:21:14:35:19:21:14:32:10:500 and decoct at 140°C for 20 hours. Then filter to get the filter cake to make the antibacterial active substance;

[0031] 2) Polyvinyl chloride (weight average molecular weight is 5000), ethylene-ethyl acrylate copolymer (weight average molecular weight is 9000), polyimide (weight average molecular weight is 3000), three (2,4-di-tert-butyl phenyl) phosphite, sodium lauramide ethyl sulfate, carbon nanotubes, zirconium phosphate, bamboo ketone, wollastonite fiber, vinyltrimethoxysilane and antibacterial active substances according to the ratio of 100:80:45:8 : 20: 7: 15: 17: 13: 50: 45, mixed at 195°C for 4 hours, and then extruded (die temperature at 190°C) to obtain high-strength antibacterial...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength antibacterial plastic and a preparation method thereof. The preparation method comprises the following steps: (1) mixing silicon dioxide, asbestos, kaolin, zinc borate, Chinese herbal medicines and water for decocting, and then, filtering a filter cake to prepare an anti-bacterial activator; and 2) mixing polyvinyl chloride, ethylene-ethyl acrylate copolymer, polyimide, tri(2,4-ditert-butyl phenyl) phosphite ester, laurel amide ethyl sodium sulfate, a carbon nano tube, zirconium phosphate, bamboo leaf phenolic ketone, wollastonite fibers, vinyl trimethoxy silane and the anti-bacterial activator to obtain a mixture, and processing and forming the mixture to prepare the high-strength antibacterial plastic. The Chinese herbal medicines contain sea-buckthorn, mulberry twigs, ligusticum sinense oliver, arisaema consanguineum schott, radix bupleuri, phellodendri, cyrtomium fortune, nandina roots, cortex acanthopanacis, schisandra chinensis, jiuliming, licorice section and semen strychni. The plastic prepared by the method has excellent antibacterial characteristics and mechanical strength; and meanwhile, the raw materials are easily available, and the process is simple.

Description

technical field [0001] The invention relates to plastics, in particular to a high-strength antibacterial plastic and a preparation method thereof. Background technique [0002] Plastic is a high molecular compound polymerized by addition polymerization or polycondensation reaction with monomer as raw material. It is commonly known as plastic or resin. It can freely change its composition and shape. , Colorants and other additives. The main component of plastic is resin. The term resin was originally named after the lipids secreted by animals and plants, such as rosin, shellac, etc. Resin refers to a polymer compound that has not been mixed with various additives. Resin accounts for about 40%-100% of the total weight of plastic. The basic properties of plastics are mainly determined by the nature of the resin, but additives also play an important role. Some plastics are basically composed of synthetic resins, with no or few additives, such as plexiglass, polystyrene, etc....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/08C08L79/08C08K13/04C08K7/24C08K3/32C08K7/10C08K5/00C08K3/36C08K3/34
CPCC08L27/06C08L23/0869C08L2205/03C08L79/08C08K13/04C08K7/24C08K2003/328C08K7/10C08K5/00C08K3/36C08K3/346
Inventor 水晓萍钱万水汤涛
Owner ANHUI YUEERWEI PLASTIC MACHINE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com