Steel-slag inflaming-retarding heat-preservation foam concrete and preparing method thereof

A foamed concrete, flame retardant and thermal insulation technology, applied in ceramic products, other household appliances, sustainable waste treatment, etc., can solve the problems of steel slag water washing ball mill tail mud, difficult to transport and stack, pollute the production site and other problems, to reduce floating Chance of merging, water consumption reduction, effect of reducing water absorption

Inactive Publication Date: 2016-12-14
广西玉林市绿盛科贸有限责任公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Steel slag is a by-product of the steelmaking process, and steel slag water-washing ball mill mud is the sediment of metal iron extracted by wet water-washing ball milling process, and then the residue after magnetic separation; The rate is about 30%; because steel slag has a certain gelling property, it is difficult to dehydrate the steel slag washing ball mill tailings, and it is easy to harden after drying, which makes it difficult to transport and stack, and seriously pollutes the production site; as we all know, steel slag washing ball mill mud contains P 2 o 5 and sulfide, it is generally difficult to simply use it in cement and concrete; if the steel slag water-washed ball mill mud can be stabilized and used to make flame-retardant and thermal insulation foam concrete, the problem of storage and difficult utilization of water-washed ball mill tailings can be solved. To achieve a win-win situation of economic and environmental benefits

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel-slag inflaming-retarding heat-preservation foam concrete and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Example 1: The flame-retardant and heat-retaining foam concrete is prepared according to the mass ratio of various raw materials: 40 parts of cement, 42 parts of fly ash, 18 parts of mineral powder, 0.2 part of melamine water reducer, 0.03 parts of 10,000-viscosity cellulose ether part, 0.2 part of silane water-repellent agent, 4.8 parts of gypsum, 0.08 part of polypropylene fiber, 0.20 part of plant protein foaming agent, and 0.33 part of water; the preparation method is: first cement, fly ash, mineral powder, Modified component water reducer, cellulose ether, water repellent, gypsum, and polypropylene fiber are mixed evenly to obtain dry powder; the foaming agent is diluted with water, and the foaming agent aqueous solution is made into foam by an air compression foaming machine Add appropriate amount of water to the dry powder and mix it. It is required that the slurry is uniform without agglomeration and large particles. Take the prepared foam and add it to the cemen...

Embodiment 2

[0043] Example 2: The flame-retardant and heat-retaining foam concrete is prepared according to the mass ratio of various raw materials: 50 parts of cement, 25 parts of fly ash, 25 parts of mineral powder, 0.4 part of naphthalene-based water reducer, 20,000-viscosity cellulose ether 0.03 part, 0.4 part of siloxane water-repellent agent, 2 parts of gypsum, 0.16 part of polypropylene fiber, 0.21 part of animal protein foaming agent, 0.31 part of water; Its preparation method is with embodiment 1.

Embodiment 3

[0044] Example 3: The flame-retardant and heat-retaining foam concrete is prepared according to the mass ratio of various raw materials: 60 parts of cement, 12 parts of fly ash, 28 parts of mineral powder, 0.3 part of naphthalene-based water reducer, 20,000-viscosity cellulose ether 0.05 part, 0.2 part of siloxane water-repellent agent, 1.2 part of gypsum, 0.24 part of polypropylene fiber, 0.20 part of animal protein foaming agent, 0.32 part of water; Its preparation method is with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a steel-slag inflaming-retarding heat-preservation foam concrete. The steel-slag inflaming-retarding heat-preservation foam concrete is prepared from, by mass, 30-60 parts of cement, 30-70 parts of steel-slag water washing dust sludge, 10-40 parts of steel slag composite powder, 0.05-1.0 part of water reducing agent, 0.02-0.2 part of thickening agent, 0.05-1.0 part of water repellent, 1-10 parts of sintered desulfurized ash, 0.06-0.2 part of anti-cracking agent, 0.1-0.4 part of foaming agent and 0.30-0.60 part of water. The steel-slag inflaming-retarding heat-preservation foam concrete has the advantages that the preparing technology is simple, the foam concrete is high in strength, low in shrinkage, good in hydrophobicity, excellent in heat insulation performance and capable of meeting different heat preserving requirements of buildings, industrial waste such as the steel-slag water washing dust sludge, the steel slag composite powder and the sintered desulfurized ash is sufficiently used, and the excellent waste-utilizing and energy-saving environment-protection effect and good economic benefits are achieved.

Description

technical field [0001] The invention belongs to new building materials, and in particular relates to a steel slag flame-retardant and heat-preserving foam concrete and a preparation method thereof. Background technique [0002] In recent years, with the improvement of flame retardant requirements and the enhancement of environmental protection awareness, the non-halogenation, smoke suppression and detoxification of flame retardants have become the frontier topics in the field of current and future flame retardant research; traditional flame retardants are due to their There are serious shortcomings such as large amount of addition, large amount of smoke, and generation of toxic and corrosive gases, which are being replaced by a new generation of environmentally friendly flame retardants. [0003] At the same time, my country's building energy conservation has gradually been promoted to the national strategic level. Multifunctional new building materials that are both flame r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00C04B28/04C04B28/06C04B38/10C04B18/14C04B18/06C04B111/28
CPCC04B18/062C04B18/142C04B28/00C04B28/04C04B28/06C04B2111/28C04B2201/20C04B2201/32C04B2201/50C04B2103/302C04B2103/44C04B2103/65C04B16/0633C04B24/14C04B38/106C04B18/08C04B14/02C04B24/383C04B24/42C04B22/143Y02W30/91
Inventor 李灿华陈昆先
Owner 广西玉林市绿盛科贸有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products