Environment-friendly plastic

A technology of environmentally friendly plastics and raw materials, applied in the field of environmentally friendly plastics, can solve the problems of strong water absorption, fast decomposition rate, oxidation resistance, and weak impact resistance, and achieve low water absorption, slow decomposition speed, and good impact resistance.

Inactive Publication Date: 2017-01-04
GUANGXI NANNING ZHICUI SCI TECH CONSULTATION CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved by the present invention is to provide an environmentally friendly plastic to solve the problems of fast decomposition rate, weak oxidation resistance, impact resistance, and strong water absorption in the environmental protection plastic material with agricultural product starch as the main component in the prior art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The preparation method of described environment-friendly plastics, comprises the following steps:

[0035] S1: Polylactic acid resin, modified poly-β-hydroxybutyrate PHB, diisononyl phthalate DINP, epoxy tall oleate butyl, linear low density polyethylene grafted with maleic anhydride, γ- Glycidyl etheroxypropyl trimethoxysilane was mixed and stirred at a temperature of 105-120°C and a rotation speed of 200-400r / min for 10-15min to obtain mixture I;

[0036] S2: Under nitrogen protection, add alkaline clay, calcium carbonate, jute fiber, methyl methacrylate-butadiene-styrene copolymer, aluminum potassium sulfate, citrate, Ethylene-vinyl acetate copolymer, ethylene bisoleic acid amide, diphenylmethane diisocyanate, degradation agent, stirring at ultrasonic power of 120-180W, temperature of 90-96°C, rotation speed of 200-300r / min for 2- 2.5h, the mixture II was obtained;

[0037] S3: Add peanut protein powder, oxidized cornstarch, anti-mold and antibacterial agent, antio...

Embodiment 1

[0041] A kind of environment-friendly plastic, by weight, comprises following raw material: 120 parts of polylactic acid resin, 80 parts of modified poly-beta-hydroxybutyric acid PHB, 8 parts of diisononyl phthalate DINP, epoxy tall oil 20 parts of butyl ester, 13 parts of peanut protein powder, 10 parts of oxidized corn starch, 6 parts of alkaline clay, 5 parts of calcium carbonate, 12 parts of jute fiber, 1.5 parts of linear low density polyethylene grafted maleic anhydride, γ-shrink 1.5 parts of glyceryl ether oxypropyltrimethoxysilane, 2.5 parts of methyl methacrylate-butadiene-styrene copolymer, 1.5 parts of potassium aluminum sulfate, 3.5 parts of citrate, 2.5 parts of ethylene-vinyl acetate copolymer, 2 parts of ethylene bisoleic acid amide, 1.5 parts of diphenylmethane diisocyanate, 2.1 parts of anti-mold and antibacterial agent, 1.5 parts of degradation agent, 0.9 part of antioxidant, 0.8 part of stabilizer;

[0042] The alkaline clay is nanoscale alkaline clay;

[0...

Embodiment 2

[0054] A kind of environment-friendly plastic, by weight, comprises following raw material: polylactic acid resin 100 parts, modified poly-beta-hydroxybutyric acid PHB75 parts, diisononyl phthalate DINP 6 parts, epoxy tall oil 15 parts of butyl ester, 10 parts of peanut protein powder, 7 parts of oxidized corn starch, 3 parts of alkaline clay, 3 parts of calcium carbonate, 8 parts of jute fiber, 1 part of linear low density polyethylene grafted maleic anhydride, γ-shrink 1 part of glyceryl ether oxypropyltrimethoxysilane, 2 parts of methyl methacrylate-butadiene-styrene copolymer, 1 part of aluminum potassium sulfate, 3 parts of citrate, 2 parts of ethylene-vinyl acetate copolymer, 1 part of ethylene bisoleic acid amide, 1 part of diphenylmethane diisocyanate, 0.8 part of anti-mold and antibacterial agent, 1 part of degradation agent, 0.6 part of antioxidant, 0.5 part of stabilizer;

[0055] The alkaline clay is nanoscale alkaline clay;

[0056] Described calcium carbonate is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses environment-friendly plastic. The plastic is prepared from the following raw materials: polylactic resin, modified poly-beta-hydroxybutyric acid PHB, diisononyl phthalate DINP, epoxy tall oil butyl acetate, peanut protein flour, oxidized corn starch, alkaline clay, calcium carbonate, jute fibers, linear low-density polyethylene grafted maleic anhydride, gamma- glycidoxy propyl trimethoxy silane, methyl methacrylate-butadiene-styrene copolymer, aluminum potassium sulfate, citrate, ethylene-vinyl acetate copolymer, ethylene bis-oleamide, diphenyl-methane-diisocyanate, an antimycotic antibacterial agent, a degradation agent, antioxidant and a stabilizing agent. The environment-friendly plastic has good tensile strength and elongation at break, has good impact resistance, relatively low moisture absorption and good light transmittance, and can be completely degraded into carbon dioxide and water in 132-135 days, and has no pollution to the environment.

Description

[0001] 【Technical field】 [0002] The invention belongs to the fields of plastic preparation technology and environmental protection, and in particular relates to an environmentally friendly plastic. [0003] 【Background technique】 [0004] Plastics are widely used, such as plastic toys, plastic bottles, plastic packaging, plastic bags, etc. We cannot live without plastics. Studies have found that plastic products produced from polylactic acid resin can be completely degraded into carbon dioxide and water in a composting environment. Moreover, polylactic acid resin has good compatibility, transparency, solvent resistance and biaxial stretching properties, etc., and can be processed in a variety of ways. At present, the more common plastic products at home and abroad are disposable cups, knives and forks, plates, Plastic bags, non-woven fabrics, etc., theoretically as long as they are plastic products, can be made of this bioplastic material. [0005] However, as we all know, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/04C08L89/00C08L3/10C08L51/06C08L23/08C08L1/02C08K13/02C08K5/12C08K3/26C08K3/32C08K5/134
CPCC08K2201/011C08L67/04C08L2201/06C08L2201/10C08L2205/025C08L2205/035C08L2205/16C08L89/00C08L3/10C08L51/06C08L23/0853C08L1/02C08K13/02C08K5/12C08K2003/265C08K2003/322C08K5/1345
Inventor 朱俊宇
Owner GUANGXI NANNING ZHICUI SCI TECH CONSULTATION CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com