Polyurethane sponge and processing method thereof

A polyurethane sponge and polymer technology, applied in the field of polymer materials, can solve problems such as inability to wash with water, unfavorable human health, etc., and achieve the effects of high production success rate, improved competitiveness, and low halogen viscosity

Inactive Publication Date: 2017-07-18
东莞恒生高分子科技有限公司
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Polyurethane sponge is used in the above household products, because it cannot be washed with water, it will inevitably breed bacteria and mildew after a long time, which is not conducive to human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] 1) Accurately measure and prepare the raw materials of components A and B. In parts by weight, component A includes: 40 parts of flame-retardant polyether polyol, 60 parts of polymer polyol, stannous octoate and triethylamine according to 1: 1 Proportion of 0.51 parts of catalyst, 1 part of silicone oil, 2 parts of deionized water; component B includes 60 parts of commercially available TDI80 / 20, titanium dioxide silver-loaded inorganic antibacterial agent and quaternary ammonium salt antibacterial agent according to the ratio of 1:1 0.5 part of agent;

[0025] The above-mentioned flame-retardant polyether polyols are customized by our company's designated manufacturers, and the composite polyether polyols are produced by ring-opening polymerization using halogen-containing epoxy compound monomers, phosphorus-containing, antimony and other compounds and starter mixtures; The molar mass of polyether polyol is 3000-5000g / mol; in the production of sponge, water is indispen...

Embodiment 2

[0032] 1) Accurately measure and prepare the raw materials of components A and B. In parts by weight, component A includes: 60 parts of flame-retardant polyether polyol, 40 parts of polymer polyol, triethanolamine and triethylenediamine according to 1: 1 proportioning catalyst 1 part, silicone oil 3 parts, deionized water 3 parts; B component includes commercially available TDI80 / 20 40 parts, titanium dioxide photocatalyst antibacterial agent 1 part, antifungal agent 8-hydroxyquinoline copper 0.5 part, 1 part of tourmaline powder with a diameter of 100-1000nm;

[0033] 2) Add component A into the mixer and stir for 25 minutes at 5000r / min, check all indicators are qualified and ready to use;

[0034] 3) Add the raw materials of group B into the mixer and mix with the raw materials of group A, stir at 5000r / min for 30s, pour into the foaming container for foaming;

[0035] 4) Natural aging for 2-4 hours;

[0036] 5) demoulding to obtain the finished product;

[0037] 6) Afte...

Embodiment 3

[0039] 1) Accurately measure and prepare the raw materials of components A and B. In parts by weight, component A includes: 50 parts of flame-retardant polyether polyol, 50 parts of polymer polyol, stannous octoate and triethylamine according to 1: 1. 0.8 parts of catalyst, 2 parts of silicone oil, 3 parts of deionized water; B component includes 50 parts of commercially available TDI80 / 20, 1.5 parts of quaternary phosphonium salt antibacterial agent, 0.5 parts of flame retardant diethyl phosphate, 0.8 parts of tourmaline powder with a diameter between 100 and 1000 nm;

[0040] 2) Add component A into the mixer and stir for 20 minutes at 3000r / min, check all indicators are qualified and ready to use;

[0041] 3) Put the raw materials of group B into the mixer and mix with the raw materials of group A, stir at 4000r / min for 45s, pour into the foaming container for foaming;

[0042] 4) Natural aging for 2-4 hours;

[0043] 5) demoulding to obtain the finished product;

[0044...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses polyurethane sponge and a processing method thereof. Polyether polyol with a flame retardant function is directly added to a material A, and a diethyl ethylphosphonate fire retardant is selectively added to a material B, so that the polyurethane sponge does not contain halogen, is low in viscosity and very stable in a two-component system of the material A and the material B, and a product is endowed with good fireproof and flame-retardant properties while the process is simple. The product is endowed with good mildew-proof and antibacterial effects through an antibacterial agent and a mildew preventive added to the material B; and through addition of nanoscale inorganic material tourmaline powder, the product has the function of lastingly emitting anions. The production technology and the formula are relatively simple on the premise that all performance indexes reach the expected requirements; the production process and the formula are relatively simple; the processes such as heating or refrigerating do not need to be specifically carried out in the production process and foaming and curing in a natural state can be carried out; the production success rate of sample post-detection is very high; the produced polyurethane sponge has obvious fireproof and flame-retardant functions, antibacterial and anti-mildew functions and continuous anion release function, and is beneficial to improvement of the competitiveness of the product.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a polyurethane sponge and a processing method thereof. Background technique [0002] The full name of polyurethane in Chinese is polyurethane, referred to as polyurethane. According to the physical properties of the product, it can be divided into polyurethane rigid foam, polyurethane soft foam, PU self-skinned sponge, etc., and the formula can be modified during production to obtain different density, elasticity and rigidity. and other physical properties. Among them, polyurethane soft foam is what we often call polyurethane sponge. According to the degree of softness and hardness, that is, the load resistance performance, polyurethane sponge foam can be divided into ordinary soft foam, super soft foam, high load-bearing soft foam, and high resilience soft foam. Wait. Compared with the expensive price of natural latex products, polyurethane sponge is wide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/76C08G18/66C08G18/50C08G18/63C08K3/38C08K5/521C08K5/3437C08K9/10C08K3/08C08K5/19C08K3/22C08K5/49C08J9/08C08J9/14
CPCC08G18/4072C08G18/50C08G18/5075C08G18/632C08G18/7614C08G2101/00C08J9/08C08J9/145C08J2203/02C08J2203/142C08J2203/184C08J2375/08C08K3/08C08K3/22C08K3/38C08K5/19C08K5/3437C08K5/49C08K5/521C08K9/10C08K2003/0806C08K2003/2241C08K2201/003C08K2201/011C08G2110/0083
Inventor 卓惠良
Owner 东莞恒生高分子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com