Wet-mixed masonry coating plaster

A plaster and wet mixing technology, applied in the field of wet plastering plaster, can solve the problems of inability to completely complete the self-insulation effect, thick mortar coating, long construction period, etc., and achieves low production cost, high work efficiency, and economical savings. effect of material

Active Publication Date: 2017-11-07
宋乐财
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the continuous advancement of building a conservation-oriented society, it is very important to promote the development, demonstration and promotion of resource-saving technologies. In terms of construction, most of the masonry mortars we use in aerated concrete blocks and foam concrete blocks still use traditional Cement mortar and dry-mixed dry-mixed mortar, but they have not been widely used due to high cost. The thermal conductivity of traditional cement mortar and dry-mixed dry-mixed mortar is much higher than that of aerated concrete blocks and foam concrete blocks. The thermal bridge and cold bridge increase energy consumption, and the self-insulation effect cannot be completely completed, and the traditional cement mortar and dry-mixed dry powder mortar are used for plastering the wall surface and need to be hung with nets and not breathable. The mortar coating is thick during construction, and the construction period is long. Long, inconsistent with my country's basic national policy of building a conservation-minded society and sustainable development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] (1) A kind of wet-mix plastering paste, the raw materials are taken according to the percentage: calcium carbide slag 30%, fly ash slag 35%, compound liquid 34.98%, deodorant (hydrogen peroxide) 0.009%, polycarboxylic acid water-reducing Agent 0.005%, short fiber (grass fiber) 0.006%;

[0016] (2) Deodorization: After uniformly mixing the deodorant and carbide slag, let stand for 2 hours to deodorize;

[0017] (3) Prepare the mixed solution: take methyl cellulose ether and polyacrylamide, and mix them with water in a blender evenly, 0.006% of the water for methyl cellulose ether, and 0.012% of the water for polyacrylamide;

[0018] (4) Preparation of ash paste: Put the calcium carbide slag, fly ash, and short fibers deodorized in step (1) into the pulverizer and pass through a 10-mesh sieve for crushing, and mix the crushed mixture and the mixed solution prepared in step (2) Add the polycarboxylate superplasticizer into the mixer and stir for 3 minutes until the mixtur...

Embodiment 2

[0020] (1) A kind of wet-mix plastering paste, the raw materials are taken according to the percentage: calcium carbide slag 25%, fly ash slag 39.98%, compound liquid 35%, deodorant (hydrogen peroxide) 0.005%, polycarboxylic acid water-reducing Agent 0.006%, short fiber (grass fiber and glass fiber 1:1) 0.009%;

[0021] (2) Deodorization: After uniformly mixing the deodorant and carbide slag, let stand for 2 hours to deodorize;

[0022] (3) Prepare the mixed solution: take methyl cellulose ether and polyacrylamide, and mix them with water in a blender, 0.01% of the water for methyl cellulose ether and 0.01% of the water for polyacrylamide;

[0023] (4) Preparation of ash paste: Put the calcium carbide slag, fly ash, and short fibers deodorized in step (1) into the pulverizer and pass through a 15-mesh sieve to pulverize, and mix the pulverized mixture and the mixed solution prepared in step (2) Add the polycarboxylate superplasticizer into the mixer and stir for 4 minutes unt...

Embodiment 3

[0025] (1) A kind of wet-mix plastering paste, the raw materials are taken according to the percentage: calcium carbide slag 34.98%, fly ash slag 35%, compound liquid 30%, deodorant (hydrogen peroxide) 0.003%, polycarboxylic acid water-reducing Agent 0.01%, short fiber (glass fiber and lignin fiber 1:1) 0.007%;

[0026] (2) Deodorization: After uniformly mixing the deodorant and carbide slag, let stand for 2 hours to deodorize;

[0027] (3) Prepare the mixed solution: take methyl cellulose ether and polyacrylamide, mix them evenly with water in a blender, take 0.012% of the water for methyl cellulose ether, and 0.06% of the water for polyacrylamide;

[0028] (4) Preparation of ash paste: Put the calcium carbide slag, fly ash, and short fibers deodorized in step (1) into the pulverizer and pass through a 20-mesh sieve to pulverize, and mix the pulverized mixture and the mixed solution prepared in step (2) Add the polycarboxylate superplasticizer into the mixer, and stir for 5 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses thin mortar joint masonry thin layer plastering special for buildings and in particular relates to wet-mixed masonry coating plaster prepared by taking acetylene sludge and pulverized coal ash as main raw materials. The wet-mixed masonry coating plaster is composed of the following raw materials in percentage: acetylene sludge, pulverized coal ash, complex liquid, a deodorant, polycarboxylate superplasticizer and staple fibers. The wet-mixed masonry coating plaster disclosed by the invention refers to thin mortar joint masonry plaster for aerated concrete blocks and foamed concrete blocks and thin foam ash plaster for buildings. According to the wet-mixed masonry coating plaster, industrial wastes acetylene sludge and pulverized coal ash are changed into valuable materials, the wet-mixed masonry coating plaster is low in manufacturing cost and can be popularized in a large area, the mechanical property is matched with that of the aerated concrete blocks, the thermal insulation properties are excellent, the wall surface does not need to be watered during construction, only capping mass on the old wall surface needs to be removed, and the masonry coating thickness is 3-5mm. Compared with the traditional mortar with the masonry coating thickness of 2cm, the wet-mixed masonry coating plaster disclosed by the invention is high in working efficiency, rapid in construction and capable of saving materials, can achieve excellent gas permeability and is a revolutionary transformed environment-friendly material.

Description

technical field [0001] The invention relates to building materials, and is a thin plaster for thin mortar seam masonry special for buildings, in particular to a wet-mixed plastering paste prepared from calcium carbide slag and fly ash slag as main raw materials. Background technique [0002] With the continuous advancement of building a conservation-oriented society, it is very important to promote the development, demonstration and promotion of resource-saving technologies. In terms of construction, most of the masonry mortars we use in aerated concrete blocks and foam concrete blocks still use traditional Cement mortar and dry-mixed dry-mixed mortar, but they have not been widely used due to high cost. The thermal conductivity of traditional cement mortar and dry-mixed dry-mixed mortar is much higher than that of aerated concrete blocks and foam concrete blocks. The thermal bridge and cold bridge increase energy consumption, and the self-insulation effect cannot be completel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/28C04B18/04C04B18/08
CPCC04B18/0481C04B18/08C04B26/285C04B2111/00482C04B24/2652C04B22/068C04B24/24C04B16/02C04B14/42C04B16/06Y02W30/91
Inventor 宋乐财
Owner 宋乐财
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products