Polypropylene composition for transparent high temperature boiling film and preparation method thereof

A polypropylene composition and high-temperature cooking technology, which is applied in the field of polypropylene composition for transparent high-temperature cooking film and its preparation, can solve the problems of food contamination, low transparency, poor hygienic processing performance, etc., and achieve good impact resistance , high surface gloss, high heat resistance

Active Publication Date: 2018-01-12
CHINA PETROLEUM & CHEM CORP
View PDF13 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the aluminum-plastic composite film has the characteristics of shading and preventing aroma from escaping, but at the same time, the aluminum-plastic composite film has shortcomings such as opacity, poor folding resistance, invisible food inside, and cannot be processed by microwaves. It is gradually being eliminated. The national standard GB/ Composite film with aluminum foil structure has also been deleted in T10004-2008
The existing transparent retort-resistant composite film is usually a composite film composed of non-polyolefin materials and polypropylene or polyethylene. These commonly used non-polyolefin materials include polyester, nylon (PA), polyvinylidene chloride (PVDC), polyethylene Alcohol (PVA), ethylene-vinyl alcohol copolymer (EVOH), etc. Although some of these materials have good barrier properties, their cooking resistance is poor, such as PVA and EVOH; PVDC has good barrier properties and cooking resistance. However, its hygienic processing performance is poor, and it is easy to cause food pollution when used in food packaging materials.
PA has good mechanical properties, transparency, oxygen barrier properties, high-temperature cooking performance and hygiene safety, etc., but PA is very easy to absorb water, and the performance of the composite film will decrea

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene composition for transparent high temperature boiling film and preparation method thereof
  • Polypropylene composition for transparent high temperature boiling film and preparation method thereof
  • Polypropylene composition for transparent high temperature boiling film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3

[0045] The preparation method of impact copolymer polypropylene resin in embodiment 1-3:

[0046] Using propylene and ethylene monomers as raw materials, using Ziegler-Natta type titanium series catalyst as the main catalyst, the co-catalyst includes triethylaluminum (TEAL) and electron donor (C-DONOR), in double-loop reactor and gas phase The process equipment combined with fluidized bed reactor is prepared from above, in which the polymerization reaction of homopolypropylene is carried out in the loop reactor stage, the polymerization temperature is 69-71 ℃, the pressure of the loop reactor is 3.3-4.0MPa, and the reaction is in the gas phase The propylene and ethylene monomers are fed into the reactor stage simultaneously for gas-phase copolymerization, and the polymerization temperature is 75-78°C. During the reaction process of the polymerization process, by controlling the C ＝ 2 / (C ＝ 2 +C ＝ 3 )(V / V) at 0.08-0.18 and H 2 / C ＝ 2 (V / V) in the range of 0.25-0.45, re...

Embodiment 1

[0048] Preparation steps of polypropylene composition for transparent high-temperature cooking film:

[0049] The calcium stearate of 0.1 part, the calcium stearate of 0.04 part, the glycerol monostearate that will add 0.1 part of antioxidant 1010, 0.1 part of antioxidant 168, 0.04 part, 0.03 part of glycerol monostearate in the impact copolymerized polypropylene resin powder, its composition The addition amount of nucleating agent and antisticking agent is shown in Table 1, and all kinds of raw materials are commercially available products.

[0050] Put the polypropylene powder and various additives in a high-speed mixer, stir for 3 minutes at a speed of 1500r / min, and mix the obtained premix evenly; then add the obtained premix to the co-rotating twin-screw extruder Medium-melt mixing, the temperature of the highest section of the extruder is 210°C, the main engine speed of the extruder is 200r / min, the feeding speed is 40r / min, extruded and granulated to obtain a transparen...

Embodiment 2-3

[0055] The addition amount of antioxidant, acid absorbing agent and antistatic agent in embodiment 2-3 is the same as that of embodiment 1, and its raw material consumption is shown in table 1. Its performance test sample and film preparation steps are all the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melting temperatureaaaaaaaaaa
Crystallization temperatureaaaaaaaaaa
Login to view more

Abstract

The invention relates to a polypropylene composition for a transparent high temperature boiling film and a preparation method thereof. The polypropylene composition is prepared from following raw materials: impact resistant co-polypropylene resin, an antioxidant, an acid absorbent, an antistatic agent, a nucleating agent, an anti-adhesion agent, and a slipping agent. The obtained polypropylene composition has the advantages of low haze, excellent transparency, good impact resistant performance, high heatproof property, and high surface glossiness, and can be made into a highly transparent filmresistant to high temperature boiling. The haze of a cast film with a thickness of 36 [mu]m is only 0.52%. At the same time, compared with those of a film prepared from common random co-polypropylene, the tensile strength, fracture/tensile strain, and tear resistant performance of prepared film are better. The prepared transparent high temperature boiling film is mainly used in the food package field.

Description

technical field [0001] The invention relates to a polypropylene composition for film, more specifically to a polypropylene composition for transparent high-temperature cooking film and a preparation method thereof. Background technique [0002] Cast polypropylene film (CPP) has the advantages of good transparency, high gloss, strong moisture resistance, high heat resistance, easy heat sealing, etc., and has good packaging machinery applicability, so it is widely used, especially in food Packaging is the main thing. According to the application, it can be divided into three categories: composite film, aluminized film, and cooking film. In recent years, with the acceleration of the pace of modern life and the rapid development of the tourism industry, the demand for retort films used in the packaging of cooked foods such as meat and soy products is increasing. [0003] Retort film is divided into ordinary retort film (also known as semi-high temperature retort grade) and hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/16C08K13/02C08K5/00C08K5/134C08K5/526C08K5/098C08K3/36C08F110/06C08F210/06C08F210/16C08F4/646B29C47/92B29C48/92
Inventor 李延亮李丽蒋善君唐岩陈智能苑东兴卢昶裴小静王秀丽明月陈华赉黄峰
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap